Ni/MnO/chitosan nanocomposites: synthesis, characterization and investigation of photocatalytic applications for degradation of malachite green

Azam Sobhani

DOI: https://doi.org/10.1007/s10854-024-12456-0

2024-04-01

Journal of Materials Science Materials in Electronics

Abstract:Recently, water pollution has become a big issue due to rapid industrialization and the increasing population. In this study, Ni mixed MnO structures (Ni/MnO) were prepared by a facile green co-precipitation technique with sucrose as a capping and reducing agent. The nanostructures were coated with chitosan by crosslink, and 1:1 and 2:1 W/W ratios of Ni/MnO:chitosan were weighted. XRD analysis revealed the formation of Ni/MnO and Ni/MnO/chitosan nanocomposites. According to the XRD results, the hydrothermal method is not an appropriate route in the present condition. But, the co-precipitation method is suitable and produces Ni/MnO with diameters ~ 50 nm. SEM analysis showed the formation of the semi-spherical structures (diameter 200–900 nm), formed from the accumulation of nanobars. The TEM image showed the formation of the nanobars with diameters lower than 40 nm. UV–Vis spectrum of Ni/MnO showed bonds ~ 250 and 290 nm and an optical bandgap ~ 3.5 eV. The prepared Ni/MnO showed a ferromagnetic-type hysterics loop with a coercivity of about 739 Oe. The Ni/MnO and Ni/MnO/chitosan were used as photocatalysts for the degradation of aqueous solutions containing malachite green (MG) and erithrosin (ES), and various operational parameters (dye type, photocatalyst dosage, dye concentration, solution pH) were investigated in this study. The optimized Ni/MnO and Ni/MnO/chitosan samples (0.05 g) showed 68% and 89% degradation for MG solution (5 ppm) within 90 min of visible irradiation. The MG degradation occurred at a higher rate at pH > 7 than at other pHs, and 92% of MG was degraded in this condition. The novelty of this work lies in the introduction of a new nanocomposite for photocatalysis in visible light, achieving high efficiency within a short time frame of 90 min.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied