Abstract:During the first discharge process of sodium‐ion batteries, the Fe1‐xS@C anode exhibits an intriguing pulverization phenomenon, with no discernible aggregation of pulverized particles occurring in subsequent cycles. Benefiting from this unique ultrafine pulverization, the Fe1‐xS@C anode demonstrates excellent sodium storage performance. Iron sulfides have attracted tremendous research interest for the anode of sodium‐ion batteries due to their high capacity and abundant resource. However, the intrinsic pulverization and aggregation of iron sulfide electrodes induced by the conversion reaction during cycling are considered destructive and undesirable, which often impedes their capacity, rate capability, and long‐term cycling stability. Herein, an interesting pulverization phenomenon of ultrathin carbon‐coated Fe1‐xS nanoplates (Fe1‐xS@C) is observed during the first discharge process of sodium‐ion batteries, which leads to the formation of Fe1‐xS nanoparticles with quantum size (≈5 nm) tightly embedded in the carbon matrix. Surprisingly, no discernible aggregation phenomenon can be detected in subsequent cycles. In/ex situ experiments and theoretical calculations demonstrate that ultrafine pulverization can confer several advantages, including sustaining reversible conversion reactions, reducing the adsorption energies, and diffusion energy barriers of sodium atoms, and preventing the aggregation of Fe1‐xS particles by strengthening the adsorption between pulverized Fe1‐xS nanoparticles and carbon. As a result, benefiting from the unique ultrafine pulverization, the Fe1‐xS@C anode simultaneously exhibits high reversible capacity (610 mAh g−1 at 0.5 A g−1), superior rate capability (427.9 mAh g−1 at 20 A g−1), and ultralong cycling stability (377.9 mAh g−1 after 2500 cycles at 20 A g−1).

Uniform Yolk-Shell Iron Sulfide–carbon Nanospheres for Superior Sodium–iron Sulfide Batteries

Yolk‐Shell Structure and Spin‐Polarized Surface Capacitance Enable FeS Stable and Fast Ion Transport in Sodium‐Ion Batteries

A promising cathode material of sodium iron–nickel hexacyanoferrate for sodium ion batteries

Carbon Coated Amorphous Bimetallic Sulfide Hollow Nanocubes Towards Advanced Sodium Ion Battery Anode

Improved Sodium-Ion Storage Performance of Ultrasmall Iron Selenide Nanoparticles.

A highly-stable layered Fe/Mn-based cathode with ultralow strain for advanced sodium-ion batteries

Promoting Highly Reversible Sodium Storage of Iron Sulfide Hollow Polyhedrons via Cobalt Incorporation and Graphene Wrapping

Facile Formation of NiCo2O4 Yolk-Shell Spheres for Highly Reversible Sodium Storage

Yolk–Shelled C@Fe3O4 Nanoboxes As Efficient Sulfur Hosts for High‐Performance Lithium–Sulfur Batteries

Sulfur encapsulation into yolk-shell Fe2N@nitrogen doped carbon for ambient-temperature sodium-sulfur battery cathode

Encapsulating Sulfides into Tridymite/Carbon Reactors Enables Stable Sodium Ion Conversion/Alloying Anode with High Initial Coulombic Efficiency Over 89%

Metal-organic Frameworks Engaged Formation of FeSe2/N-doped Carbon As Anode Enables High-Performance Sodium-Ion Batteries

Co9S8@carbon Yolk-Shell Nanocages As a High Performance Direct Conversion Anode Material for Sodium Ion Batteries

Rational design of MoNi sulfide yolk-shell heterostructure nanospheres as the efficient sulfur hosts for high-performance lithium-sulfur batteries

Long-Cycling-Life Sodium-Ion Battery Using Binary Metal Sulfide Hybrid Nanocages as Anode

Hierarchical Metal Sulfide/Carbon Spheres: A Generalized Synthesis and High Sodium-Storage Performance.

Hollow Heterostructured Cu1.96S/NiS Microspheres Coupled with Nitrogen/Sulfur Dual-Doped Carbon Realizing Superior Reaction Kinetics and Sodium Storage

Linearly Interlinked Fe-Nx-Fe Single Atoms Catalyze High-Rate Sodium-Sulfur Batteries

Unlocking the Potential of Iron Sulfides for Sodium‐Ion Batteries by Ultrafine Pulverization

A Yolk–Shell‐Structured FePO4 Cathode for High‐Rate and Long‐Cycling Sodium‐Ion Batteries

A Mott–Schottky Heterojunction with Strong Chemisorption and Fast Conversion Effects for Room‐Temperature Na–S Batteries