Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Effect of Engelhard titanosilicate microporous material on photocatalytic performance of cement

Challenges and Opportunities of Using Titanium Dioxide Photocatalysis on Cement-Based Materials

Recent advances in photocatalysis on cement-based materials

Developing Novel Photocatalytic Cementitious Permeable Pavements for Depollution of Contaminants and Impurities in Urban Cities

Photocatalyst efficiencies in concrete technology: The effect of photocatalyst placement

Ecological Efficiency Photocatalytic Concrete

Recent Progress in Nanomaterials for Modern Concrete Infrastructure: Advantages and Challenges

Evaluation of self-cleaning performance of TiO2-intermixed and TiO2-coated cement mortars under natural sunlight

Effects of the use of TiO2 on the early ages of white cement-based mortars: analysis of chemical, physical, mechanical, and photocatalytic properties

The Effect of TiO2 Doped Photocatalytic Nano-Additives on the Hydration and Microstructure of Portland and High Alumina Cements

Study on the Photo-Catalytic Properties of Nano-TiO<sub>2</sub> Cementitious Materials

Nano-TiO2 particles: a photocatalytic admixture to amp up the performance efficiency of cementitious composites

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Reducing the effects of clogging and surface wear on the radiative properties of concrete blocks produced with recycled glass by incorporating titanium dioxide nanoparticles

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Study on Visible Light Catalysis of Graphite Carbon Nitride-Silica Composite Material and Its Surface Treatment of Cement

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

Development of photocatalytic carbonation coating for concrete: Enhancement of air quality and sequestration of CO2

Evaluation of Nitrogen Oxide Reduction Performance in Permeable Concrete Surfaces Treated with a TiO2 Photocatalyst

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Highly-efficient green photocatalytic cementitious materials with robust weathering resistance: From laboratory to application