Interface Engineering of Hierarchical MoS 2 /ZnS/C Heterostructures as Anode Materials for Highly Improved Lithium Storage Capability
Peng Hu,Zhiyuan Jia,Yue Wang,Qinqin Zhou,Ning Liu,Fan Li,Jinshu Wang
DOI: https://doi.org/10.1021/acsaem.0c01266
IF: 6.4
2020-07-23
ACS Applied Energy Materials
Abstract:Constructing hybrid heterostructures of transition-metal dichalcogenides is an effective strategy to enhance their electrochemical performance and stability as anode materials in lithium-ion batteries. In this work, a facile in situ strategy was developed to engineer lattice-mismatched MoS<sub>2</sub>–ZnS together with C into hierarchical nanostructures. The three-dimensional architecture was constructed using few-layer MoS<sub>2</sub> nanosheets as the building block, and ZnS and C coexisted among the MoS<sub>2</sub> nanosheets with a mesoporous structure. By the synergy effect of integrated interfaces and hierarchical configuration, as-formed heterostructures exhibit increased conductivity, enhanced e<sup>–</sup>/Li<sup>+</sup> transfer efficiency, and retarded volume expansion during the electrochemical process. All of these contribute to the greatly increased lithium storage capability and well-preserved stability. Impressively, as-obtained materials exhibit a high lithium storage capacity of 961.9 mA g<sup>–1</sup> at 100 mA g<sup>–1</sup> after 100 cycles (about 3.1 times higher than pristine MoS<sub>2</sub> after 35 cycles), good rate retention, and superior cycling stability with 9.5% decay. Therefore, the proposed strategy provides a favorable direction for developing high-activity and low-cost electrode materials with potential applications in electrochemical fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c01266?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c01266</a>.EDS analysis of the obtained MoS<sub>2</sub>/ZnS/C heterostructures; FT-IR spectra of products before and after heating treatment; XPS spectra of MoS<sub>2</sub>/ZnS-DETA precursor; nitrogen adsorption–desorption isotherms of MoS<sub>2</sub>/ZnS-DETA precursor; SEM image and XRD patterns of MoS<sub>2</sub>/ZnS-DETA hybrid nanostructures with adding different Zn/Mo molar ratios; and SEM and XRD analyses of products obtained with a Zn/Mo molar ratio of 0.7:1 (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c01266/suppl_file/ae0c01266_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels