Study on bilayer composite hydrogel film for wound dressing based on chitosan/sodium alginate-polyvinyl alcohol
ZHAO Qi,ZHAO Xiangyu,LIU Yan,XIE Hebing,ZHANG Jianxiang,WANG Liuyi,ZHANG Jiwen,WU Li
DOI: https://doi.org/10.7501/j.issn.1674-6376.2023.11.005
2023-01-01
Abstract:Objective To prepare and evaluate the quality of polyvinyl alcohol(PVA)/sodium alginate(SA)-PVA/chitosan(CS)double-layer hydrogel film wound dressing.Methods Mix PVA and SA in a mass ratio of 2∶1 to prepare a PVA/SA mixed solution.Mix PVA and CS in mass ratios of1∶1,2∶1,3∶1,4∶1,and 5∶1 to prepare PVA/CS mixed solutions with different mass ratios.PAPCS double-layer hydrogel membrane wound dressing was prepared by coating method.The properties of hydrogel films were evaluated,and PVA to CS quality ratio was screened by water vapor permeability,swelling property,water retention,mechanical property,in vitro coagulation ability and blood compatibility.The structure and morphology of the hydrogel films were then characterized by fourier transform infrared spectroscopy(FTIR)and scanning electron microscopy(SEM).Moreover,the antibacterial activity of PAPCS with I2@COF@PAPCS in vitro was compared through inhibition zone assay.Results When the mass ratio of PVA to CS was 2:1,the comprehensive properties of PAPCS hydrogel membrane were better.The results suggested bilayer PAPCS hydrogel films had porous structure,good swelling performance,water retention and mechanical properties.The water vapor transmission rate of PAPCS hydrogel films was(2 643.76±91.62)g·m-2 d-1,close to the ideal range.Compared with PVA/SA,the coagulation index of PAPCS hydrogel films was significantly decreased(P＜0.01),the coagulation index was(72.93±3.58)％,and the hemolysis rate was less than 5％,which had good blood coagulation ability and blood compatibility.Compared with PVA/SA,PAPCS hydrogel film showed significant bacteriostasis against S.aureus and E.coli,and the diameters of the antibacterial zone were(11.89±0.22)and(12.28±0.25)mm.The diameters of antibacterial zone of I2@COF@PAPCS against S.aureus and E.coli were(21.95±1.47)and(18.89±0.81)mm,which were significantly better than PAPCS(P＜0.001).Conclusion PAPCS hydrogel film could be prepared successfully by coating method,which had good performance indexes,obvious clotting,and bacteriostatic effects.And the bacteriostasis of PAPCS hydrogel film could be further improved by combining with I2@COF.