Abstract:Magnetic nanoparticles (MNPs) modified simultaneously with amorphous Fe and Mn oxides (Mag-Fe-Mn) were synthesized to remove arsenite [As(III)] from water. Mag-Fe-Mn particles were fabricated through heterogeneous nucleation technique by employing the maghemite as the magnetic core and Fe Mn binary oxide (FMBO) as the coating materials. Powder X-ray diffraction, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy were utilized to characterize the hybrid material. With a saturation magnetization of 23.2 emu/g, Mag-Fe-Mn particles with size of 20 -50 nm could be easily separated from solutions with a simple magnetic process in short time (within 5 min). At pH 7.0, 200 mu g/L of As(III) could be easily decreased to below 10 mu g/L by Mag-Fe-Mn particles (0.1 g/L) within 20 min. As(III) could be effectively removed by Mag-Fe-Mn particles at initial pH range from 4 to 8 and the residual As was completely oxidized to less toxic arsenate [As(V)]. The co-occurring redox reactions between Mn oxide and As(III) was confirmed by XPS analysis. Chloride, sulfate, bicarbonate, and nitrate at common concentration range had negligible influence on As(III) removal, whereas, silicate and phosphate reduced the As(III) removal by competing with arsenic species for adsorption sites. As(M) removal was not obviously affected by natural organic matter (up to 8 mg/L as TOC). Mag-Fe-Mn could be regenerated with ternary solution of NaOH, NaCl, and NaClO. Throughout five consecutive cycles, the adsorption and desorption efficiencies maintained above 98% and 87%, respectively. Mag-Fe-Mn had a larger adsorption capacity for As(III) (47.76 mg/g) and could remove trace As(III) more thoroughly than MNPs modified solely with either Fe or Mn oxide due to the synergistic effect of the coating Fe and Mn oxides. This research extended the potential applicability of FMBO to a great extent and provided a convenient approach to efficiently remove trace As(III) from water. (C) 2013 Elsevier Ltd. All rights reserved.

Dispersion-precipitation synthesis of nanosized magnetic iron oxide for efficient removal of arsenite in water.

Superparamagnetic mesoporous ferrite nanocrystal clusters for efficient removal of arsenite from water

Removal of Arsenic Contaminants with Magnetic Γ-Fe2o3 Nanoparticles

Arsenic removal from aqueous solutions by adsorption onto iron oxide/activated carbon magnetic composite

Simultaneous removal of arsenate and arsenite in water using a novel functional halloysite nanotube composite

One-Step Preparation of Chitosan-Based Magnetic Adsorbent and Its Application to the Adsorption of Inorganic Arsenic in Water

Efficient Removal of As(III) Via Simultaneous Oxidation and Adsorption by Magnetic Sulfur-Doped Fe-Cu-Y Trimetal Oxide Nanoparticles

Removal of Trace Arsenite through Simultaneous Photocatalytic Oxidation and Adsorption by Magnetic Fe 3 O 4 @PpPDA@TiO 2 Core–Shell Nanoparticles

Electrospinning Chitosan/Fe-Mn Nanofibrous Composite for Efficient and Rapid Removal of Arsenite from Water

Removal of As(V) from aqueous solution using modified Fe3O4 nanoparticles

Arsenic removal from water by nanometer iron oxide coated single-wall carbon nanotubes

Adsorption Behavior and Mechanism of Arsenic on Mesoporous Silica Modified by Iron-Manganese Binary Oxide (Femnox/sba-15) from Aqueous Systems.

Efficient Removal of Trace Arsenite Through Oxidation and Adsorption by Magnetic Nanoparticles Modified with Fe-Mn Binary Oxide

Enhanced removal of trace arsenate by magnetic nanoparticles modified with arginine and lysine

Removal of arsenate by cetyltrimethylammonium bromide modified magnetic nanoparticles.

Adsorption behavior and mechanism of different arsenic species on mesoporous MnFe 2 O 4 magnetic nanoparticles.

General and Controllable Synthesis of Novel Mesoporous Magnetic Iron Oxide@Carbon Encapsulates for Efficient Arsenic Removal

Selective and Efficient Removal of As(V) and As(III) from Water by Resin-Based Hydrated Iron Oxide

Preparation and Evaluation of a Novel Fe–Mn Binary Oxide Adsorbent for Effective Arsenite Removal

Ferrous Magnetic Nanoparticles for Arsenic Removal from Groundwater

Fe-MOFs/graphene oxide-derived magnetic nanocomposite for enhanced adsorption of As(V) in aqueous solution