Abstract:Carbon aerogels, owing to the high-temperature durability and low thermal conductivity, are promising candidates for high-temperature thermal insulation used in inert atmospheres. However, significant drying shrinkage poses challenges in fabricating large-sized carbon aerogels and optimizing their thermal insulation properties. Herein, we report the synthesis of monolithic carbon aerogels with low drying shrinkage and controllable nanostructures by adding self-crosslinked chitosan to provide reaction sites and three-dimensional network support based on the traditional resorcinol–formaldehyde method in an acetic acid environment. Owing to the increased cross-linking degree of resorcinol–formaldehyde gel from the polymerization and hydrogen bonding between chitosan and resorcinol–formaldehyde oligomers, the skeleton of gel network is strengthened and the shrinkage during supercritical drying is as low as 1.51 %, resulting in a good monolithic shape of carbon aerogel (130 × 130 × 15 mm). Besides, they exhibit typical nanoporous characteristics with uniform and small particle size (9–130 nm) and low density (0.070–0.221 g·cm−3), achieving a low thermal conductivity of 0.047 W·m−1·K−1 at 1100 °C and high compressive strength of 1.80 MPa (density of 0.138 g·cm−3). This method facilitates the production of carbon aerogels with low shrinkage, minimal defects, low density, and small pore size, rendering them suitable for applications requiring large dimensions and low defect levels, such as fiber-reinforced composites and high-performance thermal insulators.

Scalable Template Synthesis of Resorcinol–Formaldehyde/Graphene Oxide Composite Aerogels with Tunable Densities and Mechanical Properties

Flexible, Strong, Multifunctional Graphene Oxide/Silica-Based Composite Aerogels Via a Double-Cross-Linked Network Approach

A General and Programmable Synthesis of Graphene-Based Composite Aerogels by a Melamine-Sponge-Templated Hydrothermal Process

Superelastic, Anticorrosive, and Flame-Resistant Nitrogen-Containing Resorcinol Formaldehyde/Graphene Oxide Composite Aerogels

Reconstruction of Inherent Graphene Oxide Liquid Crystals for Large-Scale Fabrication of Structure-Intact Graphene Aerogel Bulk Toward Practical Applications

Nanosheet Graphene Composite Carbon Aerogels from Resorcinol-Formaldehyde via an Adsorption-Assembly Polymerization Method .

Conductive Resilient Graphene Aerogel Via Magnesiothermic Reduction of Graphene Oxide Assemblies

Arbitrary-shaped Reduced Graphene Oxide Aerogels Via an Unsaturated Water Vapor Reduction

Synthesis of Structure Controllable Carbon Aerogel with Low Drying Shrinkage and Scalable Size As High-Temperature Thermal Insulator

Structurally Stable, High-Strength Graphene Oxide/Carbon Nanotube/Epoxy Resin Aerogels as Three-Dimensional Skeletal Precursors for Wave-Absorbing Materials

High-strength and Morphology-Controlled Aerogel Based on Carboxymethyl Cellulose and Graphene Oxide.

Retarding Ostwald Ripening to Directly Cast 3D Porous Graphene Oxide Bulks at Open Ambient Conditions.

Graphene-templated Carbon Aerogels Combining with Ultra-High Electrical Conductivity and Ultra-Low Thermal Conductivity

Synthesis of sodium silicate-based silica aerogels with graphene oxide by ambient pressure drying

Naturally Dried Graphene-Based Nanocomposite Aerogels with Exceptional Elasticity and High Electrical Conductivity.

SiC Nanowires Bridged Graphene Aerogels with a Vertically Aligned Structure for Highly Thermal Conductive Epoxy Resin Composites and Their Mechanism

Silicone/graphene oxide co-cross-linked aerogels with wide-temperature mechanical flexibility, super-hydrophobicity and flame resistance for exceptional thermal insulation and oil/water separation

Synthesis and Characterization of Graphene Oxide/Chitosan Composite Aerogels with High Mechanical Performance

Ultralight Covalent Organic Framework/graphene Aerogels with Hierarchical Porosity

Edge-to-Edge Assembled Graphene Oxide Aerogels with Outstanding Mechanical Performance and Superhigh Chemical Activity

Superelastic Cobalt Silicate@Resorcinol Formaldehyde Resin Core-Shell Nanobelt Aerogel Monoliths with Outstanding Fire Retardant and Thermal Insulating Capability