Abstract:Wear and oxidative degradation may limit the life span of UHMWPE implants. Cross-linking and stabilisation by vitamin E are proposed to overcome wear and degradation. The present investigation takes a close look to the oxidative behaviour of cross-linked and stabilised UHMWPE. First, the consolidated vitamin E stabilised UHMWPE was qualified in terms of microstructure and homogeneity of the distribution of the additive to be suitable for oxidation profiles over the entire section. Then cross-linked samples with five different concentrations of vitamin E (nil to 1.0%) underwent two different ageing protocols. The first was under pressurized oxygen at 70 degrees C, as defined in the ASTM F 2003 standard with a prolonged period of 60 days, the second was in 5% aqueous hydrogen peroxide solution with iron (III) chloride as catalyst at 50 degrees C. The first accelerated ageing protocol showed that a vitamin E concentration as low as 0.05% is effective to protect irradiated highly cross-linked UHMWPE against oxidation when exposed direct to oxygen. Vitamin E stabilised, highly cross-linked UHMWPE exhibits therefore no oxidation potential origination from the irradiation treatment. Analysis of samples treated by the second chemical ageing yielded, that vitamin E is effective to prolong initial stability against a supplementary attack of hydrogen peroxide and reactive radicals. The time period of stability against the aggressive hydrogen peroxide solution increases with increasing vitamin E content. However, even 0.05% have a marked stabilisation effect. Therefore, such small additions of vitamin E are effective to protect the UHMWPE material against a supplementary exposure to in vivo oxidation after the irradiation treatment. In conclusion, vitamin E shields cross-linked UHMWPE for orthopaedic application against oxidation in the heat of consolidation, during irradiation treatment and finally while implanted in the human body.

A comparative microstructural study of vitamin-E blended and infused highly crosslinked UHMWPE for total knee arthroplasty.

Strain-induced Microstructural Rearrangement in Ultra-High Molecular Weight Polyethylene for Hip Joints: A Comparison Between Conventional and Vitamin E-infused Highly-Crosslinked Liners.

Vitamin-E blended and infused highly cross-linked polyethylene for total hip arthroplasty: a comparison of three-dimensional crystalline morphology and strain recovery behavior.

813 the Performances of Vitamin E (D, L-α-Tocopherol) Added Ultra High Molecular Weight Polyethylene for Artificial Knee Components

Effects of vitamin E blending on plastic deformation mechanisms of highly crosslinked ultrahigh molecular weight polyethylene (HXL-UHMWPE) in total hip arthroplasty.

ON THE PHYSICAL AND STRUCTURAL EFFECTS OF VITAMIN-E BLENDING IN HIGHLY CROSS-LINKED POLYETHYLENE FOR TOTAL HIP ARTHROPLASTY

Strain-Induced Crystallization and Orientation of Vitamin E-Blended Ultrahigh Molecular Weight Polyethylene

Microstructural Modifications Induced by Accelerated Aging and Lipid Absorption in Remelted and Annealed UHMWPEs for Total Hip Arthroplasty.

Vitamin E-enriched medium cross-linked polyethylene in total knee arthroplasty (VIKEP): clinical outcome, oxidation profile, and wear analysis in comparison to standard polyethylene—study protocol for a randomized controlled trial

High temperature melted, radiation cross-linked, vitamin E stabilized oxidation resistant UHMWPE with low wear and high impact strength

Vitamin E Can Be Used to Hinder Scissioning in Radiation Cross-Linked Uhmwpe During High-Temperature Melting

Highly Cross-Linked Polyethylene in Total Hip and Knee Replacement: Spatial Distribution of Molecular Orientation and Shape Recovery Behavior

1227 the Effect of Vitamin E (D, L-α-Tocopherol) Addition on Microscopic Mechanical Behavior of Ultra High Molecular Weight Polyethylene

Effect of e-beam sterilization on the in vivo performance of conventional UHMWPE tibial plates for total knee arthroplasty

Effect of Surface Crosslinking on the Wear and Friction Behavior of Tea Polyphenol Stabilized Ultra-High Molecular Weight Polyethylene for Total Joint Replacements

Impact resistance and fractography in ultra high molecular weight polyethylenes

Accelerated ageing experiments with crosslinked and conventional ultra-high molecular weight polyethylene (UHMW-PE) stabilised with alpha-tocopherol for total joint arthroplasty

High-Temperature Melted, Cross-Linked, and Stabilized Ultrahigh Molecular Weight Polyethylene

Raman Spectroscopic Study of Remelting and Annealing-Induced Effects on Microstructure and Compressive Deformation Behavior of Highly Crosslinked UHMWPE for Total Hip Arthroplasty.

Improved Oxidation Stability and Crosslink Density of Chemically Crosslinked Ultrahigh Molecular Weight Polyethylene Using the Antioxidant Synergy for Artificial Joints

Use of vitamin E to protect cross-linked UHMWPE from oxidation