Abstract:Besides excellent biocompatibility and biodegradability, a useful tissue engineering scaffold should provide suitable macropores and nanofibrous structure, similar to extracellular matrix (ECM), to induce desired cellular activities and to guide tissue regeneration. In the present study, a mild process to prepare porous and nanofibrous silk-based scaffolds from aqueous solution is described. Using collagen to control the self-assembly of silk, nanofibrous silk scaffolds were firstly achieved through lyophilization. Water annealing was used to generate insolubility in the silk-based scaffolds, thereby avoiding the use of organic solvents. The nano-fibrils formed in the silk-collagen scaffolds had diameters of 20–100 nm, similar with native collagen in ECM. The silk-collagen scaffolds dissolved slowly in PBS solution, with about a 28% mass lost after 4 weeks. Following the dissolution or degradation, the nanofibrous structure inside the macropore walls emerged and interacted with cells directly. During in vitro cell culture, the nanofibrous silk-collagen scaffolds containing 7.4% collagen demonstrated significantly improved cell compatibility when compared with salt-leached silk scaffolds and silk-collagen scaffolds containing 20% collagen that emerged less nano-fibrils. Therefore, this new process provides useful scaffolds for tissue engineering applications. Furthermore, the process involves all-aqueous, room temperature and pressure processing without the use of toxic chemicals or solvents, offering new green chemistry approaches, as well as options to load bioactive drugs or growth factors into process.

Nanoscale Control of Silks for Nanofibrous Scaffold Formation with an Improved Porous Structure

Preparation and characterization of nano-hydroxyapatite/silk fibroin porous scaffolds.

Silk fibroin/sodium alginate composite nano-fibrous scaffold prepared through thermally induced phase-separation (TIPS) method for biomedical applications

Fabrication and characterization of porous tubular silk fibroin scaffolds.

Lyophilized Silk Sponges: A Versatile Biomaterial Platform for Soft Tissue Engineering

From Common Biomass Materials to High-Performance Tissue Engineering Scaffold: Biomimetic Preparation, Properties Characterization, in Vitro and in Vivo Evaluations

Nanofibrous architecture of silk fibroin scaffolds prepared with a mild self-assembly process.

Preparation and properties of nano-fiber, softBombyx mori silk protein scaffolds

Green Process to Prepare Water-Insoluble Silk Scaffolds with Silk I Structure.

Facile Synthesis of 3D Silk Fibroin Scaffolds with Tunable Properties for Regenerative Medicine

Preparation of the Silk Fibroin 3D Scaffolds with Large Pore Sizes and High Interconnectivity

Design and engineering of silk fibroin scaffolds with biomimetic hierarchical structures.

Multifunctional silk fibroin – Poly(L-lactic acid) porous nanofibers: Designing adjustable nanopores to control composite properties and biological responses

Woven Silk Fabric-Reinforced Silk Nanofibrous Scaffolds for Regenerating Load-Bearing Soft Tissues.

Programing Performance of Silk Fibroin Superstrong Scaffolds by Mesoscopic Regulation among Hierarchical Structures.

Silk Scaffolds with Tunable Mechanical Capability for Cell Differentiation.

Correction to “biomimetic Silk Scaffolds with an Amorphous Structure for Soft Tissue Engineering”

Fabrication of Silk Hydrogel Scaffolds with Aligned Porous Structures and Tunable Mechanical Properties

Programing Performance of Silk Fibroin Materials by Controlled Nucleation

Advances in Preparation of Porous Silk Fibroin Scaffolds for Medical Tissue Engineering

Hierarchical Macro/micro-Porous Silk Fibroin Scaffolds for Tissue Engineering