Preparation and Characterization of Photo-crosslinked Layer-by-Layer (LBL) Self-assembled Antibacterial Films
Xue-bin Wang,Yuan Xue,Yao-wu Zhou,Sheng-yi Chen,Chun-yan Bao,Lin-yong Zhu
DOI: https://doi.org/10.11777/j.issn1000-3304.2021.21182
2022-01-01
Acta Polymerica Sinica
Abstract:Bacteria are one of the oldest life forms on the earth. They have strong adaptability to various environments and can be seen almost everywhere on the earth. Bacteria will adhere to different surfaces and then reproduce to form dense aggregates or biofilms with a thickness of several microns to tens of centimeters, which will seriously affect the properties of materials, especially for medical devices. Bacterial adhesion and biofilm formation on these devices are an important reason for the failure of medical implantation and the formation of large-area medical infection. Therefore, researchers are focusing on developing antibacterial surface coatings to eliminate or prevent the initial adhesion of bacteria and biofilm formation on the surface of materials. Alternating layered self-assembly (LBL) film, as the most popular coating technology, is applicable to the surface of various materials. Due to its advantages of simple operation, high controllability and easy functionalization, LBL film is widely used in separation technology, sensor, controlled drug release, surface modification of biomaterials and so on. However, its inherent shortcomings, such as poor stability, easy decomposition, etc., greatly limit their applications. To solve the above problems, a kind of photo crosslinking antibacterial LBL membrane was designed and prepared by alternating deposition of photosensitive o-nitrobenzyl alcohol modified hyaluronic acid (HANB) and quaternized chitosan (ACS) on the glass substrate through electrostatic interaction. The photoligation reaction of o-nitrobenzyl alcohol to amine of chitosan enables the crosslinking of the assembled polyelectrolyte membrane, which stabilizes and maintains the integrity of the membrane for a long time in salt solutions with different pH values. The antibacterial property of chitosan endows LBL membrane with good antibacterial property and strong electrostatic supramolecular interactions with HANB. Cytotoxicity analysis confirms the cytocompatibility of the LBL membranes. Antibacterial experiments show that the non-photocrosslinked LBL membrane shows higher release-sterilization due to the release of quaternized chitosan to the solution. However, the photocrosslinked LBL membrane shows better contact-sterilization due to the membrane stability, which is more friendly to the environment. Compared with other chemical crosslinking methods, o-nitrobenzyl alcohol photocrosslinldng strategy has better biocompatibility without the introduction of any initiator or additive, which provides a new idea for the construction of antibacterial coating on the surface of medical implants. [GRAPHICS] .