Tailoring polyelectrolyte architecture to promote cell growth and inhibit bacteria adhesion.
Shanshan Guo,Min Yi Kwek,Zi Qian Toh,Dicky Pranantyo,En-Tang Kang,Xian Jun Loh,Xiaoying Zhu,Dominik Jańczewski,Koon Gee Neoh
DOI: https://doi.org/10.1021/acsami.8b00666
IF: 9.5
2018-01-01
ACS Applied Materials & Interfaces
Abstract:An important challenge facing the application of implanted biomaterials for tissue engineering is the need to facilitate desirable tissue interactions with the implant while simultaneously inhibiting bacterial colonization, which can lead to implant-associated infection. In this study, we explore the relevance of physical parameters of polyelectrolyte multilayers, surface charge, wettability and stiffness, in tissue cell/surface and bacteria/surface interactions, and investigate the tuning of the multilayer architecture to differentially control such interactions. Polyions with different side chain chemical structures were paired with polyethylenimine to assemble multilayers with parallel control over surface charge and wettability under controlled conditions. The multilayers can be successfully crosslinked to yield stiffer (the apparent Young's modulus was increased more than 3 times its original value) and more stable films while maintaining parallel control over surface charge and wettability. The initial adhesion and proliferation of 3T3 fibroblast cells were found to be strongly affected by surface charge and wettability on the non-crosslinked multilayers. On the other hand, these cells adhered and proliferated in a similar manner on the crosslinked multilayers (apparent Young's modulus ~2 MPa) regardless of surface charge and wettability. In contrast, Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) adhesion was primarily controlled by surface charge and wettability on both crosslinked and non-crosslinked multilayers. In both cases, negative charge and hydrophilicity inhibited its adhesion. Thus, a surface coating with a relatively high degree of stiffness from covalent crosslinking coupled with negative surface charge and high wettability can serve as an efficient strategy to enhance host cell growth while resisting bacterial colonization.