Abstract:A robust nanocasting approach is demonstrated to synthesize encapsulated nanoparticles in metal oxides. First, colloidal nanoparticles are encapsulated in a porous polymer matrix. Then, metal oxide precursor is infiltrated, and materials are calcined to form a porous metal oxide network. Various combinations of nanoparticles encapsulated in metal oxide materials can be synthesized, and their surface area and porosity can be tuned using this method. Encapsulation of metal nanoparticles within oxide materials has been shown as an effective strategy to improve activity, selectivity, and stability in several catalytic applications. Several approaches have been proposed to encapsulate nanoparticles, such as forming core‐shell structures, growing ordered structures (zeolites or metal‐organic frameworks) on nanoparticles, or directly depositing support materials on nanoparticles. Here, a general nanocasting method is demonstrated that can produce diverse encapsulated metal@oxide structures with different compositions (Pt, Pd, Rh) and multiple types of oxides (Al2O3, Al2O3‐CeO2, ZrO2, ZnZrOx, In2O3, Mn2O3, TiO2) while controlling the size and dispersion of nanoparticles and the porous structure of the oxide. Metal@polymer structures are first prepared, and then the oxide precursor is infiltrated into such structures and the resulting material is calcined to form the metal@oxide structures. Most Pt@oxides catalysts show similar catalytic activity, demonstrating the availability of surface Pt sites in the encapsulated structures. However, the Pt@Mn2O3 sample showed much higher CO oxidation activity, while also being stable under aging conditions. This work demonstrated a robust nanocasting method to synthesize metal@oxide structures, which can be utilized in catalysis to finely tune metal‐oxide interfaces.

Controlled Incorporation of Nanoparticles in Metal-Organic Framework Hybrid Thin Films.

Porous Two-Dimensional Monolayer Metal-Organic Framework Material and Its Use for the Size-Selective Separation of Nanoparticles

Imparting Functionality to a Metal–organic Framework Material by Controlled Nanoparticle Encapsulation

General Incorporation of Diverse Components Inside Metal-Organic Framework Thin Films at Room Temperature.

Regulating the spatial distribution of metal nanoparticles within metal-organic frameworks to enhance catalytic efficiency

Controlling Nanoparticle Synthesis Derived from Bimetallic Metal–organic Frameworks

Synthesis of Ultrafine and Highly Dispersed Metal Nanoparticles Confined in a Thioether-Containing Covalent Organic Framework and Their Catalytic Applications

Mechanistic Insights into Nanoparticle Formation from Bimetallic Metal–Organic Frameworks

In situ biosynthesis of ultrafine metal nanoparticles within a metal-organic framework for efficient heterogeneous catalysis

Immobilizing Metal Nanoparticles on Hierarchically Porous Organic Cages with Size Control for Enhanced Catalysis

Immobilization of Metal Nanoparticles to an Ultrathin Two-Dimensional Conjugated Metal-Organic Framework for Synergistic Electrocatalysis

A General Approach for Metal Nanoparticle Encapsulation Within Porous Oxides

Hollow Metal-Organic Framework Nanospheres Via Emulsion-Based Interfacial Synthesis and Their Application in Size-Selective Catalysis

Incorporating metal nanoparticles in porous materials via selective heating effect using microwave

Metal–Organic Framework Nanoparticles

Time-resolved control of nanoparticle integration in titanium-organic frameworks for enhanced catalytic performance

Nanoarchitectonics and catalytic performances of metal–organic frameworks supported metal nanoparticles

Controlling Nanocluster Growth through Nanoconfinement: The Effect of the Number and Nature of Metal-Organic Framework Functionalities

General Immobilization of Ultrafine Alloyed Nanoparticles within Metal–Organic Frameworks with High Loadings for Advanced Synergetic Catalysis

Encapsulation of C-N-decorated Metal Sub-Nanoclusters/single Atoms into a Metal-Organic Framework for Highly Efficient Catalysis.

Highly catalytic metal-organic framework coating enabled by liquid superwetting and confinement