Cheap, Gram-Scale Fabrication of BN Nanosheets Via Substitution Reaction of Graphite Powders and Their Use for Mechanical Reinforcement of Polymers.

Fei Liu,Xiaoshu Mo,Haibo Gan,Tongyi Guo,Xuebin Wang,Bin Chen,Jun Chen,Shaozhi Deng,Ningsheng Xu,Takashi Sekiguchi,Dmitri Golberg,Yoshio Bando

DOI: https://doi.org/10.1038/srep04211

IF: 4.6

2014-01-01

Scientific Reports

Abstract:As one of the most important two-dimensional (2D) materials, BN nanosheets attracted intensive interest in the past decade. Although there are many methods suitable for the preparation of BN sheets, finding a cheap and nontoxic way for their mass and high-quality production is still a challenge. Here we provide a highly effective and cheap way to synthesize gram-scale-level well-structured BN nanosheets from many common graphite products as source materials. Single-crystalline multi-layered BN sheets have a mean lateral size of several hundred nanometers and a thickness ranging from 5 nm to 40 nm. Cathodoluminescence (CL) analysis shows that the structures exhibit a near band-edge emission and a broad emission band from 300 nm to 500 nm. Utilization of nanosheets for the reinforcement of polymers revealed that the Young's modulus of BN/PMMA composite had increased to 1.56 GPa when the BN's fraction was only 2 wt.%, thus demonstrating a 20% gain compared to a blank PMMA film. It suggests that the BN nanosheet is an ideal mechanical reinforcing material for polymers. In addition, this easy and nontoxic substitution method may provide a universal route towards high yields of other 2D materials.