Growth, Spectroscopy and 2 Μm Laser Operation of Monoclinic Tm3+:ZnWO4 Crystal
Ghassen Zin Elabedine,Kirill Subbotin,Pavel Loiko,Zhongben Pan,Kirill Eremeev,Yulia Zimina,Yana Didenko,Sergei Pavlov,Anatoly Titov,Elena Dunina,Liudmila Fomicheva,Aleksey Kornienko,Alain Braud,Rosa Maria Sole,Magdalena Aguilo,Francesc Diaz,Weidong Chen,Pavel Volkov,Valentin Petrov,Xavier Mateos
DOI: https://doi.org/10.1016/j.optmat.2024.116039
IF: 3.754
2024-01-01
Optical Materials
Abstract:We report on the crystal growth, polarized spectroscopy, and laser operation of monoclinic Tm3+, Na+(Li+) codoped zinc monotungstate (ZnWO4) crystals. The Li+ codoping with an optimized Tm/Li ratio enables almost complete local charge compensation leading to better crystal quality, higher Tm segregation coefficient, and longer luminescence lifetime and ultimately the demonstration of laser operation. The modified Judd-Ofelt theory was employed to calculate the Tm3+ transition probabilities yielding a radiative lifetime of the F-3(4) state of 2.59 ms. The corresponding intensity parameters are Omega(2) = 5.194, Omega(4) = 0.658, Omega(6) = 0.471 [10(-20) cm(2)] and alpha = 0.110 [10(-4) cm]. Tm,Li:ZnWO4 features strongly polarized emission spectra extending beyond 2 mu m owing to a large total Stark splitting of the ground-state, Delta E (H-3(6)) = 644 cm(-1). The stimulated-emission cross-section in this spectral range reaches 0.47 x 10(-20) cm(2) at 2015 nm for light polarization E || N-p. The continuous-wave Tm,Li:ZnWO4 laser generated 282 mW at 1.98 mu m with a slope efficiency of 14.7 %, and laser emission at 2.03 mu m was also achieved.