Abstract:OBJECTIVE:To fabricate in situ crosslinking hyaluronic acid hydrogel and evaluate its biocompatibility in vitro.METHODS:The acrylic acid chloride and polyethylene glycol were added to prepare crosslinking agent polyethylene glycol acrylate (PEGDA), and the molecular structure of PEGDA was analyzed by Flourier transformation infrared spectroscopy and 1H nuclear magnetic resonance spectroscopy. Hyaluronic acid hydrogel was chemically modified to prepare hyaluronic acid thiolation (HA-SH). And the degree of HA-SH was analyzed qualitatively and quantitatively by Ellman method. HA-SH solution in concentrations (W/V) of 0.5%, 1.0%, and 1.5% and PEGDA solution in concentrations (W/V) of 2%, 4%, and 6% were prepared with PBS. The two solutions were mixed in different ratios, and in situ crosslinking hyaluronic acid hydrogel was obtained; the crosslinking time was recorded. The cellular toxicity of in situ crosslinking hyaluronic acid hydrogel (1.5% HA-SH and 4% PEGDA mixed) was tested by L929 cells. Meanwhile, the biocompatibility of hydrogel was tested by co-cultured with human bone mesenchymal stem cells (hBMSCs).RESULTS:Flourier transformation infrared spectroscopy showed that most hydroxyl groups were replaced by acrylate groups; 1H nuclear magnetic resonance spectroscopy showed 3 characteristic peaks of hydrogen representing acrylate and olefinic bond at 5-7 ppm. The thiolation yield of HA-SH was 65.4%. In situ crosslinking time of hyaluronic acid hydrogel was 2 to 70 minutes in the PEGDA concentrations of 2%-6% and HA-SH concentrations of 0.5%-1.5%. The hyaluronic acid hydrogel appeared to be transparent. The toxicity grade of leaching solution of hydrogel was grade 1. hBMSCs grew well and distributed evenly in hydrogel with a very high viability.CONCLUSIONS:In situ crosslinking hyaluronic acid hydrogel has low cytotoxicity, good biocompatibility, and controllable crosslinking time, so it could be used as a potential tissue engineered scaffold or repairing material for tissue regeneration.

Biocompatibility and biodegradation of cross-linked gelatin/hyaluronic acid sponge in rat subcutaneous tissue.

Preparation and biocompatibility study of gelatin/kappa-carrageenan scaffolds

Covalently crosslinked human-like collagen hydrogel: Properties of biocompatibility

Studies on gelatin-containing artificial skin: II. Preparation and characterization of cross-linked gelatin-hyaluronate sponge.

Study the Biodegradation of a Injection Human-Like Collagen Hydrogel

Crosslinking of hyaluronic acid and human-like collagen with divinyl sulfone

Biological properties, degradation and absorption of collagen spongesin vivo

PREPARATION AND BIOCOMPATIBILITY OF IN SITU CROSSLINKING HYALURONIC ACID HYDROGEL

The Effects of Chemical Crosslinking Manners on the Physical Properties and Biocompatibility of Collagen Type I/hyaluronic Acid Composite Hydrogels.

Surface Coating with Hyaluronic Acid-Gelatin-Crosslinked Hydrogel on Gelatin-Conjugated Poly(dimethylsiloxane) for Implantable Medical Device-Induced Fibrosis

Fabrication, Characterization, and Biocompatibility Study of Gelatin-Blended Fibroin Scaffold

Synthesis and Characterization of Hyaluronic Acid/Human-Like Collagen Hydrogels

Preparation and biocompatibility of sodium hyaluronate gel cross-linked by divinylsulfone

Activated Hyaluronic Acid/collagen Composite Hydrogel with Tunable Physical Properties and Improved Biological Properties

Fabrication of Gelatin-Hyaluronic Acid Hybrid Scaffolds with Tunable Porous Structures for Soft Tissue Engineering.

Study on gelatin-containing artificial skin: I. Preparation and characteristics of novel gelatin-alginate sponge

Studies on Gelatin-Based Sponges. Part III: A Comparative Study of Cross-Linked Gelatin/alginate, Gelatin/hyaluronate and Chitosan/hyaluronate Sponges and Their Application As a Wound Dressing in Full-Thickness Skin Defect of Rat

Augmented physical, mechanical, and cellular responsiveness of gelatin-aldehyde modified xanthan hydrogel through incorporation of silicon nanoparticles for bone tissue engineering

Fabrication and Evaluation of Thermosensitive Chitosan/collagen/α, Β-Glycerophosphate Hydrogels for Tissue Regeneration

Subcutaneous toxicity of a dual ionically cross-linked atelocollagen and sodium hyaluronate gel

Self-reinforcement and Protein Sustained Delivery of Hyaluronan Hydrogel by Tailoring a Dually Cross-Linked Network.