Nafion-polyfurfuryl alcohol nanocomposite membranes with low methanol permeation.

Jin Liu,Huanting Wang,Shaoan Cheng,Kwong-Yu Chan

2004-01-01

Abstract:Nafion-polyfurfuryl alcohol nanocomposite membranes with low methanol permeability and high proton conductivity were synthesized by in-situ polymerisation of furfuryl alcohol inside commercial Nafion membranes.

What problem does this paper attempt to address?

Nafion?polyfurfuryl alcohol nanocomposite membranes with low methanol permeationElectronic Supplementary Information (ESI) available: Preparation and test methods of membrane electrode assemblies. See http://www.rsc.org/suppdata/cc/b3/b315742c/

Jin Liu,Huanting Wang,Shaoan Cheng,Kwong-Yu Chan

DOI: https://doi.org/10.1039/b315742c

IF: 4.9

2004-01-01

Chemical Communications

Abstract:Nafion-polyfurfuryl alcohol nanocomposite membranes with low methanol permeability and high proton conductivity were synthesized by in-situ polymerisation of furfuryl alcohol inside commercial Nafion membranes.
A modified Nafion membrane with extremely low methanol permeability via surface coating of sulfonated organic silica.

Yuwei Zhang,Weiwei Cai,Fengzhan Si,Junjie Ge,Liang Liang,Changpeng Liu,Wei Xing

DOI: https://doi.org/10.1039/c2cc17230e

IF: 4.9

2012-01-01

Chemical Communications

Abstract:We developed a method to significantly decrease the methanol permeability of a Nafion membrane that does not require sacrificing its proton conductivity and mechanical stability. The Nafion membrane modified by the coating of a thin layer of sulfonated organic silica on the membrane surface exhibits significantly decreased methanol permeability-the permeability is decreased to an undetectable level-while retaining an acceptable ionic conductivity of 0.029 S cm(-1).
Ultrathin proton-conducting sandwich membrane with low methanol permeability based on perfluorosulfonic acid polymer and phosphosilicate

Haibin Li,Minghuan Ai,Fengjing Jiang,Lijun Yu,Hengyong Tu,Qingchun Yu,Hong Wang

DOI: https://doi.org/10.1016/j.jpowsour.2011.01.056

IF: 9.2

2011-01-01

Journal of Power Sources

Abstract:An ultra-thin, free-standing proton-conductive membrane of Nafion®/Phosphosilicate/Nafion® (NPN) with a sandwich structure has been prepared. The NPN membrane of thickness 960nm shows extremely low methanol permeability of 1×10−8cm2s−1, and area specific resistance (ASR) smaller than 0.2Ωcm2.
Novel Nafion composite membranes with mesoporous silica nanospheres as inorganic fillers

Yonggang Jin,Shizhang Qiao,Lei Zhang,Zhi Ping Xu,Simon Smart,João C. Diniz da Costa,Gao Qing Lu

DOI: https://doi.org/10.1016/j.jpowsour.2008.08.094

IF: 9.2

2008-01-01

Journal of Power Sources

Abstract:Novel Nafion composite proton exchange membranes are prepared using mesoporous MCM-41 silica nanospheres as inorganic fillers. The novelty of this study lies in the structural design of inorganic silica fillers: the nanosized and monodisperse spherical morphology of fillers facilitates the preparation of homogenous composite membranes, whilst the superior water adsorption of the mesostructure in fillers consigns enhanced water retention properties to the polymer membranes. Scanning electron microscopy images of the composite membranes indicate that well-dispersed silica nanospheres are embedded in the Nafion matrix, but a large amount of added fillers (3wt.%) causes some agglomeration of the nanospheres. Compared with the Nafion cast membrane, the composite membranes offer improved thermal stability, enhanced water retention properties, and reduced methanol crossover. Despite the enhancement of water retention, the composite membranes still exhibit a proton conductivity reduction of 10–40% compared with pristine Nafion. This is likely due to the incorporation of much less conductive silica fillers than Nafion. The composite membrane containing 1wt.% of fillers displays the best cell performance in direct methanol fuel cell tests; it gives a maximum power density of 21.8mWcm−2, i.e., ∼20% higher than the Nafion cast membrane. This is attributed to its similar conductivity to Nafion, and its markedly reduced methanol crossover, namely, ∼1.2 times lower.
Nanocomposite Membranes of Nafion and Fe3o4-Anchored and Nafion-Functionalized Multiwalled Carbon Nanotubes Exhibiting High Proton Conductivity and Low Methanol Permeability for Direct Methanol Fuel Cells

Chia-Ming Chang,Hsieh-Yu Li,Juin-Yih Lai,Ying-Ling Liu

DOI: https://doi.org/10.1039/c3ra40438b

IF: 4.036

2013-01-01

RSC Advances

Abstract:Fe3O4 magnetic nanoparticle-anchored and Nafion-functionalized multiwalled carbon nanotubes (MWCNT-MNP-Nafion) have been prepared and used as a nano-additive for Nafion. The addition of 0.1 wt% of MWCNT-MNP-Nafion to Nafion results in the membranes showing a reduction of methanol permeability from 30.1 x 10(-7) cm(2) s(-1) to 6.8 x 10(-7) cm(2) s(-1) and an increase of proton conductivity from 31 mS cm(-1) to 78 mS cm(-1). The presence of MWCNT-MNP-Nafion reduces the ionic cluster sizes and decreases the free volume element concentration of the modified Nafion membrane. Both have been verified with small angle X-ray scattering spectroscopy and positron annihilation lifetime spectroscopy and contribute to the reduction of the methanol permeability of the membrane. The increase in the proton conductivity originates from the formation of proton-conducting pathways on the MWCNT bundles. For the membrane fabricated under a magnetic field, its proton conductivity further increases to 85 mS cm(-1) due to the magnetically-driven alignment of MWCNT-MNP-Nafion in the Nafion matrix (A-Nafion-NM-0.1). Compared to the plain recast Nafion membrane, the A-Nafion-NM-0.1 membrane has a 15-fold membrane selectivity, an 8.7-fold maximum power density, and a 6.6-fold current density at an operating voltage of 0.4 V in the tests for direct methanol fuel cells (DMFC). The high performance of the membrane in the DMFC tests demonstrates that the MWCNT-MNP-Nafion is a highly efficient additive for the preparation of Nafion-based membranes for DMFCs.
Amino-MIL-53(Al)-Nanosheets@Nafion Composite Membranes with Improved Proton/Methanol Selectivity for Passive Direct Methanol Fuel Cells

Xiuli Guo,Yong Fan,Jianing Xu,Li Wang,Jifu Zheng

DOI: https://doi.org/10.1021/acs.iecr.0c02741

2020-01-01

Industrial & Engineering Chemistry Research

Abstract:Using AMA nanosheets and Nafion as raw materials, several AMA-x@Nafion composite membranes were successfully synthesized by polymer solution casting and corresponding mechanical property, proton conductivity, water uptake and swelling, methanol permeability, and single-cell performance were investigated. It was found that AMA nanosheets were well dispersed in the matrix of the Nafion membrane due to strong electrostatic interactions among functional groups, including -SO3H and -NH2, overcoming the problem of poor dispersion of the composite membrane. Moreover, the content of AMA nanosheets had an important influence on the membrane performances, especially for methanol permeability. Among the prepared composite membranes, AMA-2.0@Nafion showed improved cell performance in contrast to recast Nafion. Notably, freezing water existed in the confined environment of the prepared composite membrane, which was significantly different from normal hydrocarbon-based PEMs. This provided a new idea and reference for the development of DMFCs used for a low-temperature cold startup.
Permeabilities of methanol, ethanol and dimethyl ether in new composite membranes: A comparison with Nafion membranes

S XUE,G YIN,K CAI,Y SHAO

DOI: https://doi.org/10.1016/j.memsci.2006.11.036

IF: 9.5

2007-01-01

Journal of Membrane Science

Abstract:New composite membranes were prepared by solution casting from sulfonated poly(ether ether ketone), poly(vinylidene fluoride) and phosphotungstic acid. Their structures were characterized using XRD, DSC and FT-IR. The permeability of methanol, ethanol and dimethyl ether in composite membranes ranged from 1.9 to 3.7×10−7, 7.4 to 20×10−8 and 1.6 to 3.2×10−8cm2/s, respectively. These values were about or more than one order of magnitude lower than those of Nafion® 117 membrane measured under the same condition. The water uptake and the swelling ratio of composite membranes were also studied, and composite membranes showed good water stability within measurement range of temperature. Higher selectivity values were observed for composite membranes compared with Nafion® 117 membrane.
Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Yang Li,Xu Zhang,Xuan Chen,Kaijie Tang,Qin Meng,Chong Shen,Guoliang Zhang

DOI: https://doi.org/10.1021/acsami.8b20422

IF: 9.5

2019-01-01

ACS Applied Materials & Interfaces

Abstract:Poly(vinyl alcohol)-sodium alginate composite hydrogels were first introduced to synthesize robust and well-intergrown zeolite imidazolate framework (ZIF)/polymer hollow fiber membranes. Through enough adsorption interaction with metal ions by chelation, sufficient nucleation sites for in situ metal-organic framework (MOF) preparation are provided. Using this method, we can not only easily prepare defect-free MOF membranes ignoring the complex modification process and seed deposition but also structurally fix crystalline MOF layers and greatly improve the stiffness and durability of MOF composite membranes. The strategy also gives the appropriate level of generality for synthesis of versatile dense MOF membranes on a variety of polymeric supports. The fabricated ZIF-8/polyethersulfone membrane presented remarkable gas separation performance with H2 permeance of as high as 9.66 × 10-7 mol m-2 s-1 Pa-1 and a high H2/CO2 separation factor of up to 29.0.
Fabrication and characterization of a novel Nafion‐PTFE composite hollow fiber membrane

Sha Yu,Zhihao Zhu,Meiqing Zhou,Haijun Yu,Guodong Kang,Yiming Cao

DOI: https://doi.org/10.1002/app.50254

IF: 3

2020-11-24

Journal of Applied Polymer Science

Abstract:Nafion has been widely used in electrochemistry, but there are only a few reports on its application in other fields, such as, gas separation, even though it exhibits good performance. The primary reason for that is the high cost of Nafion and making a composite membrane with a thin Nafion layer is a potential solution to solve this problem. In this study, a novel Nafion‐PTFE composite hollow fiber membrane, which had a thin (~5 μm) and detect‐free Nafion layer on PTFE surface, without Nafion filling substrate pores was developed, differing from the reported ones in which Nafion resin was required to impregnate into porous PTFE membrane as thorough as possible to ensure the ion conductivity and operation stability. The surface morphology, crystallite, solubility in ethanol/water mixture, and water uptake of membranes were systemically investigated. The gas permeance tests were also conducted. The permeances of different gasses of prepared composite membranes were significantly enhanced compared with the commercial membranes due to the decrease of Nafion thicknesses, while the selectivity remained the same, verifying the detect‐free structure of Nafion layer on PTFE substrate. This study provided a good reference for the preparation and application of low‐cost Nafion composite membranes.

polymer science
Dimethylamine-tuned guanidinium arylphosphonate iHOFs and superprotonic conduction Nafion hybrid membranes for DMFCs

Xiang-Tian Bai,Li-Hui Cao,Xu-Yong Chen,Shu-Hui Li,Jia-Hao Zhang

DOI: https://doi.org/10.1016/j.cej.2024.150747

IF: 15.1

2024-05-01

Chemical Engineering Journal

Abstract:The fabrication of proton exchange membranes (PEMs) with excellent conductivity and low methanol permeability is critical but challenging for the further development of high-performance direct methanol fuel cells (DMFCs). In this work, two ionic hydrogen-bonded organic frameworks (iHOF-14 and iHOF-15) are obtained from 1,3,5-tris(4-phosphonophenyl)benzene and guanidine hydrochloride under the control of dimethylamine cations. Due to the abundant hydrogen bonding network, iHOF-14 and iHOF-15 exhibit good proton conductivity of over 10–2 S cm−1. In addition, we dope the iHOFs into Nafion matrix to get the PEMs with richer proton transport pathways and good methanol barrier properties. At 100 °C and 98 % RH, the conductivity of 9 %-iHOF-14/Nafion and 9 %-iHOF-15/Nafion reaches up to 1.53 × 10–1 and 1.78 × 10–1 S cm−1, respectively. The 72 h permeation experiment results show that the methanol permeability of the composite membranes is 73.7 % lower than that of the recast Nafion. The maximum power densities of hybrid membranes for DMFCs reach about 80 mW cm−2, which is 1.5 times higher compared to the recast Nafion. This work not only enriches the high proton conductivity of arylphosphonate iHOFs, but also expands iHOFs/Nafion PEMs materials for DMFCs.

engineering, chemical, environmental
Supramolecular Modifying Nafion with Fluoroalkyl‐Functionalized Polyoxometalate Nanoclusters for High‐Selective Proton Conduction

Haibo He,Shihao Song,Liang Zhai,Zexu Li,Sihan Wang,Peng Zuo,Youliang Zhu,Haolong Li

DOI: https://doi.org/10.1002/anie.202409006

2024-06-21

Angewandte Chemie International Edition

Abstract:Proton exchange membranes with high selectivity are urgently required in energy and electronic technologies. Nafion, a state-of-the-art commercial proton exchange membrane material, faces significant challenges. It suffers from the permeation of undesirable substances, like hydrogen in fuel cells and vanadium ions in redox flow batteries, due to the unmatched sizes between its ionic domains (3~5 nm) and these substances. In this work, we present a supramolecular modification strategy that simultaneously enhances the proton conductivity and selectivity of Nafion. We employ fluoroalkyl-grafted polyoxometalate (POMs) nanoclusters as supramolecular additives to modify Nafion via co-assembly. These POMs can precisely and robustly decorate at Nafion ionic domains, with their fluoroalkyl chains anchoring into the perfluorinated matrix while their inorganic clusters stay in the ionic regions. The hybrid membranes, with continuous proton hopping sites and nanoscale steric hindrance offered by POMs, exhibit a 56% increase in proton conductivity and a 100% improvement in proton/vanadium selectivity. This leads to significantly enhanced power density and energy efficiency in fuel cells and vanadium flow batteries, respectively. These results underscore the intriguing potential of molecular cluster additives in improving the functions of ion-conducting membranes.

chemistry, multidisciplinary
Property Enhancement Effects of Side-Chain-Type Naphthalene-Based Sulfonated Poly(arylene ether ketone) on Nafion Composite Membranes for Direct Methanol Fuel Cells

Baolong Wang,Lihua Hong,Yunfeng Li,Liang Zhao,Chengji Zhao,Hui Na

DOI: https://doi.org/10.1021/acsami.7b08566

2017-09-20

Abstract:Nafion/SNPAEK-x composite membranes were prepared by blending raw Nafion and synthesized side-chain-type naphthalene-based sulfonated poly(arylene ether ketone) with a sulfonation degree of 1.35 (SNPAEK-1.35). The incorporation of SNPAEK-1.35 polymer with ion exchange capacity (IEC) of 2.01 mequiv·g-1 into a Nafion matrix has the property enhancement effects, such as increasing IECs, improving proton conductivity, enhancing mechanical properties, reducing methanol crossover, and improving single cell performance of Nafion. Morphology studies show that Nafion/SNPAEK-x composite membranes exhibit a well-defined microphase separation structure depending on the contents of SNPAEK-1.35 polymer. Among them, Nafion/SNPAEK-7.5% with a bicontinuous morphology exhibits the best comprehensive properties. For example, it shows the highest proton conductivities of 0.092 S cm-1 at 25 °C and 0.163 S cm-1 at 80 °C, which are higher than those of recast Nafion with 0.073 S cm-1 at 25 °C and 0.133 S cm-1 at 80 °C, respectively. Nafion/SNPAEK-5.0% and Nafion/SNPAEK-7.5% membranes display an open circuit voltage of 0.77 V and a maximum power density of 47 mW cm-2 at 80 °C, which are much higher than those of recast Nafion of 0.63 V and 24 mW cm-2 under the same conditions. Nafion/SNPAEK-5.0% membrane also has comparable tensile strength (12.7 MPa) to recast Nafion (13.7 MPa), and higher Young's modulus (330 MPa) than that of recast Nafion (240 MPa). By combining their high proton conductivities, comparable mechanical properties, and good single cell performance, Nafion/SNPAEK-x composite membranes have the potential to be polymer electrolyte materials for direct methanol fuel cell applications.
Nafion® Nanocomposite Membranes: Effect of Fluorosurfactants on Hydrophobic Silica Nanoparticle Dispersion and Direct Methanol Fuel Cell Performance

Chi Hoon Park,Hong Keon Kim,Chang Hyun Lee,Ho Bum Park,Young Moo Lee

DOI: https://doi.org/10.1016/j.jpowsour.2009.06.053

IF: 9.2

2009-01-01

Journal of Power Sources

Abstract:Nafion®–silica nanocomposite membranes are successfully prepared by adding hydrophobic silica nanoparticles to a Nafion® solution. To distribute these nanoparticles evenly in the Nafion® matrix, various fluorosurfactants of different ionic character are employed. Fluorosurfactants with acid groups such as phosphonic acid and sulfonic acid play an important role in simultaneously increasing the homogeneous dispersion of silica nanoparticles, enhancing proton conductivity, and reducing the methanol permeability of the nanocomposite membranes. Therefore, the dispersion properties of inorganic fillers such as silica can significantly affect nanocomposite performance in direct methanol fuel cell (DMFC) applications, whereas surfactants, if used properly, can improve the nanocomposite membrane properties. In particular, a commercial fluorosurfactant containing a sulfonic acid group (Zonyl® TBS) at the end of the surfactant chain exhibits better miscibility with the Nafion® ionomer. This feature results in a reduction in the dimensional change of the nanocomposite membrane due to relatively lower water swelling and significantly reduced methanol permeability through the membrane. A membrane–electrode assembly (MEA) prepared from a Nafion®–silica nanocomposite membrane with TBS shows the highest DMFC performance in terms of voltage vs. current density (V–I) and power density vs. current density (P–I). The current densities at 0.4V and 90°C are 342, 508, and 538mAcm−2 with 1, 3 and 5M methanol being fed at the anode side, respectively.
Naphthalene‐based Poly(arylene Ether Ketone) Copolymers Containing Sulfobutyl Pendant Groups for Proton Exchange Membranes

Ke Shao,Jing Zhu,Chengji Zhao,Xianfeng Li,Zhiming Cui,Yang Zhang,Hongtao Li,Dan Xu,Gang Zhang,Tiezhu Fu,Jing Wu,Hui Na,Wei Xing

DOI: https://doi.org/10.1002/pola.23621

2009-01-01

Abstract:A new monomer 1,5-bis(4-fluorobenzoyl)-2,6-dimethoxynaphthalene (DMNF) was prepared and further polymerized to form naphthalene-based poly(arylene ether ketone) copolymers containing methoxy groups (MNPAEKs). The side-chain-type sulfortated naphthalene-based poly(arylene ether ketone) copolymers (SNPAEKs) were obtained by demethylation and sulfobutylation. Flexible and tough membranes with reasonably high mechanical strength were prepared. The SNPAEKs membrane showed anisotropic membrane swelling with larger swelling in thickness than in plane. Transmission electron microscopy (TEM) analysis revealed clear nano-phase separated structure of SNPAEKs membranes, which composed of hydrophilic side chain and hydrophobic main-chain domains. Proton conductivities of copolymers increased gradually with increase in temperature. The highest conductivity of 0.179 S/cm was obtained for SNPAEK-80 (IEC = 1.82 mequiv/g) at 80 degrees C, which is higher than that of Nafion117 (0.146 S/cm). The SNPAEKs membranes exhibit the methanol permeability in the range of 3.42 x 10(-8) - 4.49 x 10(-7) cm(2)/s, which are much lower than that of Nafion117. They could be the promising materials as alternative to Nafion membrane for direct methanol fuel cells applications. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5772-5783, 2009
Composite silica/Nafion® membranes prepared by tetraethylorthosilicate sol–gel reaction and solution casting for direct methanol fuel cells

Ruichun Jiang,H. Russell Kunz,James M. Fenton

DOI: https://doi.org/10.1016/j.memsci.2005.07.026

IF: 9.5

2006-03-01

Journal of Membrane Science

Abstract:Composite silica/Nafion® membranes were prepared using a tetraethylorthosilicate (TEOS) hydrolysis sol–gel reaction followed by solution casting. Physico-chemical properties of the composite membranes were characterized by TGA, XRD, FT-IR, SEM-EDX and water uptake. Membranes were investigated in direct methanol fuel cells (DMFCs). Lower silica loadings (3 and 5wt.%) in the composite membranes helped to inhibit methanol crossover through the membrane, while higher silica loadings demonstrated a smaller contribution to lowering the methanol crossover. Proton conductivity of the composite membranes decreased with increasing silica content, in spite of the increasing membrane water uptake. DMFC performance using the composite membrane with 5wt.% silica loading was higher than using a pure Nafion® membrane.

engineering, chemical,polymer science
Porous Nafion nanofiber composite membrane with vertical pathways for efficient through-plane proton conduction

Jingtao Wang,Ping Li,Yafang Zhang,Yarong Liu,Wenjia Wu,Jindun Liu

DOI: https://doi.org/10.1016/j.memsci.2019.05.041

IF: 9.5

2019-09-01

Journal of Membrane Science

Abstract:Nafion has been the benchmark of proton exchange membrane for decades due to the excellent proton conduction and physicochemical properties. While the strong dependence of transfer channel continuity on humidity always causes serious conductivity drops and hampers the wide application. Herein, a combination of electrospinning and soft template (ionic liquid) methods is proposed to fabricate porous Nafion nanofiber. The resultant nanofiber mat is then impregnated with chitosan (CS) to prepare porous nanofiber composite membrane (PNFCM). This is different from traditional nanofiber composite membrane (NFCM), of which through-plane conductivity is much lower than in-plane one (i.e., strong transfer anisotropy). The abundant pores inside porous nanofibers provide numerous vertical transfer channels at interfaces between CS and pore walls. Meanwhile, the –NH/–NH2 groups on CS form acid-base pairs with –SO3H groups along pore walls. These stable vertical pathways significantly facilitate the through-plane proton conduction at both hydrated and anhydrous conditions. Particularly, PNFCM attains perpendicular conductivities of 307 mS cm−1 at 90 °C and 100% RH, and 150 mS cm−1 at 120 °C and 0% RH, which are, respectively, 3.2 and 2.7 times of that of NFCM. Consequently, the transfer anisotropy coefficient decreases and fuel cell performances enhance obviously.

engineering, chemical,polymer science
A nanocomposite proton exchange membrane based on PVDF, poly(2-acrylamido-2-methyl propylene sulfonic acid), and nano-Al2O3 for direct methanol fuel cells

Shen J,Xi J,Zhu W,Chen L,Qiu X.

DOI: https://doi.org/10.1016/j.jpowsour.2005.11.070

IF: 9.2

2006-01-01

Journal of Power Sources

Abstract:A proton exchange membrane based on poly(vinylidene fluoride) filled with nano-sized ceramic fillers and a kind of polymeric acid was prepared and characterized with FT-IR, TGA, and SEM. The membrane shows high and stable conductivity at room temperature. The role of the ceramic filler and the polymer acid in the enhancement of the proton productivity is discussed. Proton conductivities and methanol permeabilities of membranes with different contents of ceramic fillers were investigated. The ratio between the conductivity and methanol permeability shows the membranes with over 16wt.% content of alumina fillers are the best membranes prepared in this work for use in a direct methanol fuel cell.
Nafion®/SiO2/m-BOT composite membranes for improved direct methanol fuel cell performance

yituo wang,guimei han,zhe tian,meng wang,jianling li,xindong wang

DOI: https://doi.org/10.1039/c4ra06365a

IF: 4.036

2014-01-01

RSC Advances

Abstract:Bentonite (BOT) has excellent hygroscopicity and large specific surface, so it is chosen as a dopant of Nafion (R) membranes in this paper. By using the sol-gel method, bentonite has been modified by dodecylamine and fixed to the Nafion 212 membrane to prepare a Nafion/SiO2/m-BOT composite membrane. The results of SEM and FT-IR shows that m-BOT is successfully synthesized and bound well with the Nafion 212 membrane. The limiting current density of cathode methanol oxidation indicates that the methanol permeability of the composite membrane is 20.40% lower than that of the Nafion 212 membrane. Although the conductivity of the composite membrane (6.67 x 10(-2) S cm(-1)) declines slightly compared with that of Nafion 212 (9.91 x 10(-2) S cm(-1)), the performance of the cell using the composite membrane (135.17 mW cm(-2)) is better than the Nafion 212 membrane (118.7 mW cm(-2)) at 55 degrees C. Besides, as the anode methanol concentration increases, higher performance is obtained, which indicates that the composite membrane is more suitable for cells running with a high concentration of methanol.
Methanol Permeability Of Alkali Ion-Doped Poly(Perfluorosulfonate) Membrane

M Shi,Xp Qiu,Wt Zhu,Yc Liu

2000-01-01

Abstract:Poly(perfluorosulfonate acid) membranes were respectively doped with alkali ions. These membranes were investigated in relation to methanol permeability. Results indicate that the methanol permeability was reduced to different degrees with different alkali ions and that of the Cs-doped membrane was reduced by over one order of magnitude. If further experiment can prove the proton conductivity of the alkali ion-doped membranes were also ideal, the power density and the energy efficiency of DMFCs are promised to enhance significantly.
A “H2O Donating/methanol Accepting” Platform for Preparation of Highly Selective Nafion-based Proton Exchange Membranes

Kai Feng,Beibei Tang,Peiyi Wu

DOI: https://doi.org/10.1039/c5ta04916d

IF: 11.9

2015-01-01

Journal of Materials Chemistry A

Abstract:For a proton exchange membrane (PEM), the ratio of its proton conductivity to its fuel permeability usually defines the membrane selectivity. Generally, a highly selective PEM is preferred for application in direct methanol fuel cells. Herein, sulfonated SiO2@polystyrene core–shell (SiO2@sPS) nanoparticles were synthesized and then imbedded into a Nafion membrane by a blending–casting method. SiO2@sPS partakes in strong interactions with the Nafion polymer, which benefits its dispersion in the membrane matrix. The as-prepared SiO2@sPS + Nafion composite PEM presents a large increase in its proton conductivity owing to the introduction of additional –SO3H groups and hence has optimized channels for proton transport. Meanwhile, a reduced methanol crossover was also observed for the SiO2@sPS + Nafion composite PEM because of the formation of obstructed transport channels for bulk methanol. Besides this, a deep investigation on further enhancement of the membrane’s performance was conducted by etching the SiO2 core and hence forming well-dispersed uniform hollow spheres inside the membrane matrix. The intact hollow sulfonated PS spheres (h-sPS) acted as water reservoirs which in turn could gradually release water to hydrate the membrane under high-temperature and low-humidity conditions. Therefore, compared to the SiO2@sPS + Nafion membrane, the h-sPS + Nafion one presented a further increased proton conductivity at 100 °C under 40% RH. Meanwhile, h-sPS further suppressed methanol penetration by trapping it inside the hollow spheres. Herein, a “H2O donating/methanol accepting” mechanism was proposed for the first time, providing a promising platform to alleviate critical disadvantages of Nafion membranes and thereby fabricate highly selective Nafion-based PEMs.

Nafion-polyfurfuryl alcohol nanocomposite membranes with low methanol permeation.

Nafion?polyfurfuryl alcohol nanocomposite membranes with low methanol permeationElectronic Supplementary Information (ESI) available: Preparation and test methods of membrane electrode assemblies. See http://www.rsc.org/suppdata/cc/b3/b315742c/

A modified Nafion membrane with extremely low methanol permeability via surface coating of sulfonated organic silica.

Ultrathin proton-conducting sandwich membrane with low methanol permeability based on perfluorosulfonic acid polymer and phosphosilicate

Novel Nafion composite membranes with mesoporous silica nanospheres as inorganic fillers

Nanocomposite Membranes of Nafion and Fe3o4-Anchored and Nafion-Functionalized Multiwalled Carbon Nanotubes Exhibiting High Proton Conductivity and Low Methanol Permeability for Direct Methanol Fuel Cells

Amino-MIL-53(Al)-Nanosheets@Nafion Composite Membranes with Improved Proton/Methanol Selectivity for Passive Direct Methanol Fuel Cells

Permeabilities of methanol, ethanol and dimethyl ether in new composite membranes: A comparison with Nafion membranes

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Fabrication and characterization of a novel Nafion‐PTFE composite hollow fiber membrane

Dimethylamine-tuned guanidinium arylphosphonate iHOFs and superprotonic conduction Nafion hybrid membranes for DMFCs

Supramolecular Modifying Nafion with Fluoroalkyl‐Functionalized Polyoxometalate Nanoclusters for High‐Selective Proton Conduction

Property Enhancement Effects of Side-Chain-Type Naphthalene-Based Sulfonated Poly(arylene ether ketone) on Nafion Composite Membranes for Direct Methanol Fuel Cells

Nafion® Nanocomposite Membranes: Effect of Fluorosurfactants on Hydrophobic Silica Nanoparticle Dispersion and Direct Methanol Fuel Cell Performance

Naphthalene‐based Poly(arylene Ether Ketone) Copolymers Containing Sulfobutyl Pendant Groups for Proton Exchange Membranes

Composite silica/Nafion® membranes prepared by tetraethylorthosilicate sol–gel reaction and solution casting for direct methanol fuel cells

Porous Nafion nanofiber composite membrane with vertical pathways for efficient through-plane proton conduction

A nanocomposite proton exchange membrane based on PVDF, poly(2-acrylamido-2-methyl propylene sulfonic acid), and nano-Al2O3 for direct methanol fuel cells

Nafion®/SiO2/m-BOT composite membranes for improved direct methanol fuel cell performance

Methanol Permeability Of Alkali Ion-Doped Poly(Perfluorosulfonate) Membrane

A “H2O Donating/methanol Accepting” Platform for Preparation of Highly Selective Nafion-based Proton Exchange Membranes