Abstract:Natural porous mineral supported (TiO2/diatomite) photocatalyst was prepared via a modified sol–gel method using titanium (IV) butoxide (TBOT) and diatomite. The effect of TBOT dosage on adsorption capacity and photocatalytic activity for Rhodamine B (RhB) solution was investigated. The morphology and elemental distribution were determined by scanning electron microscopy with attached energy-dispersive X-ray detector. The porous and crystalline structures were characterized using nitrogen adsorption–desorption and X-ray diffraction techniques, respectively. The prepared TiO2/diatomite hybrid catalyst has shown relatively even porous structure and dispersion of TiO2 over the surface. This suggests that the diatomite matrix prevented the agglomeration of TiO2 particles. Initially, the surface area and pore volume of the hybrid catalyst were increased by adding TBOT then decreased for dosages higher than 1.0ml. The crystalline size of TiO2 immobilized on diatomite matrix by sol–gel method was around 20nm. When the experiments were carried out in the absence of diatomite, this value was increased to 33.73nm. The use of diatomite also promoted an increase of the transformation temperature of the crystalline phase anatase to rutile for the TiO2. The as-prepared TiO2/diatomite composite exhibited high photocatalytic activity (96.0% for 0.5h UV-light irradiation) for the degradation of RhB from wastewater as a result of its unique porous structure and optimum TiO2 loading. In addition, it can be easily separated from suspension and possess a good durability. This hybrid material holds great promise in the engineering field for the environmental remediation.

Photoelectrocatalytic degradation of Rhodamine B using mesh Ti/TiO2 electrode]

[Photoelectrocatalytic Degradation of Rhodamine B Using Mesh Ti/TiO2 Electrode].

Preparation of Mesh TiO2/Ti Electrode and Photoelectro- Catalytic Degradation of Dye

Preparation of TiO2/Ti Mesh Photoelectrode and Properties.

Photocatalytic and photoelectrocatalytic degradation of aqueous Rhodamine B by low-temperature deposited anatase thin films

The Promoted Photoelectrocatalytic Degradation of Rhodamine B over Tio2 Thin Film under the Half-Wave Pulsed Direct Current

Photoelectrocatalytic Degradation of Rose Bengal

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

The Improved Photoelectrocatalytic Degradation of Rhodamine B Driven by the Half-Rectified Square Wave

Decolorization of Rhodamine B in a Thin-Film Photoelectrocatalytic (PEC) Reactor with Slant-Placed TiO2 Nanotubes Electrode

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Discussion on the degradation mechanism of Rhodamine B in the photoelectrocatalytic process using a slant-placed TiO2/Ti anode thin-film reactor

Photoelectrocatalytic degradation of Rhodamine B with the slant-placed TiO_2/Ti anode thin-film reactor

Photodegradation of Rhodamine B in Water Assisted by Titania Films Prepared Through a Novel Procedure

Preparation of novel TiO2/Ti photoelectrode and photoelectrocatalytic degradation of Rhodamine B

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

Electric-Agitation-Enhanced Photodegradation of Rhodamine B over Planar Photoelectrocatalytic Devices Using A Tio2 Nanosized Layer

Fabrication of Tio2/Ti Electrode by Laser-Assisted Anodic Oxidation and Its Application on Photoelectrocatalytic Degradation of Methylene Blue

Electrochemical oxidation of Rhodamine B on RuO 2 –PdO–TiO 2 /Ti electrode

Interactive Oxidation of Photoelectrocatalysis and Electro-Fenton for Azo Dye Degradation Using TiO2–Ti Mesh and Reticulated Vitreous Carbon Electrodes

Photoelectrocatalytic degradation of rhodamine B on TiO 2 photonic crystals