Platinum-based electrocatalysts with core-shell nanostructures.
Hong Yang
DOI: https://doi.org/10.1002/anie.201005868
2011-03-14
Angewandte Chemie
Abstract:The development of low-temperature hydrogen fuel cells for automotive applications has witnessed tremendous progress over the past several years, and the total distance driven by fuel-cell-operated vehicles exceeded the million-mile mark in 2009. New cell modules continue to reduce the cost, volume, and weight of fuel cells at a rapid pace. One driving force for this fast development lies in the great progress made in making active cathode catalysts for proton exchange membrane fuel cells (PEMFCs). Improvement of the activity and durability of electrocatalysts for the oxygen reduction reaction (ORR) remains a key research area for the creation of future generations of PEMFCs for automotive applications. As there is still no viable alternative to the replacement of catalysts made of Pt group metals (PGMs), the need of low cost, highly active, and durable fuel-cell electrodes heightens the design criteria. In this regard, multicomponent nanostructures can play important roles in the design of ORR catalysts with high activity and durability. 2] Core–shell or core–shell-like nanostructures are a convenient way to build multifunctionality into the electrocatalysts of metallic nanoparticles, which have a typical average diameter between 2 and 5 nm. With the increasing complexity of core–shell nanoparticles, the study of structure–property relationships becomes even more important and essential than before in the design of new catalysts. Sun and co-workers recently reported a synthesis of multimetallic core–shell nanoparticles, which is the latest of several recent investigations into the synthesis and electrocatalytic properties of multimetallic core–shell nanoparticles. Spherical Pd/Au and Pd/Au/FePt core–shell nanoparticles were synthesized in octadecene using oleylamine and oleic acid as the capping agents. The structures were characterized by high-resolution transmission electron microscopy (TEM) and aberrationcorrected high-angle annular dark-field scanning TEM (HAADF-STEM). The core–shell nanoparticles were fairly monodisperse in size and had overall diameters of about 7 nm for Pd/Au bimetallic core–shell nanoparticles. Furthermore, 11 nm Pd/Au/FePt multimetallic core–shell nanoparticles were also readily produced by using a similar solution-phase synthesis. The size of these bimetallic or multimetallic core– shell nanoparticles can also be easily tuned within a certain range by changing the reaction conditions. To date, reports on the synthesis of well-defined multimetallic core–shell nanoparticles with sizes below about 10 nm are still relatively uncommon. In principle, the synthesis of multimetallic core–shell nanoparticles or core–shelllike heterogeneous nanostructures including dendrite, particle-on-particle, raspberry, or flower, however, is usually thermodynamically favored. The synthesis is possible as the heterogeneous nucleation of second metal component on the existing nanoparticle seed or core has a lower critical energy barrier, that is, the overall excess free energy, than the homogenous nucleation. Depending on the overall excess energy, which is largely related to the surface and interfacial energy terms, and the strain energy because of lattice mismatch at the interface, three different major types of nanostructures form, namely, layer-by-layer, island-on-wetting layer, and island growth modes (Figure 1). When the interfacial structures are not known or cannot be well defined, or the shape of the nanostructure is important, a generic description based on the morphology, such as raspberry, nanoflower, dendrite, particle-on-particle, or core–shell nanoparticle, is often used. In the solution-phase synthesis and with the use of capping ligands, metallic cores can exist in ordered or disordered forms, and can be formed from metal alloys (Figure 1). Heterogeneous deposition of a metal or metal alloy on the core occurs through one of the three growth modes to form core–shell or core–shell-like nanostructures. So why have relatively few multimetallic core–shell nanoparticles with sizes less than 10 nm been reported? Besides the intrinsic challenges in the synthesis, one important reason perhaps lies in the difficulty of characterizing multimetallic core–shell nanoparticles in detail. Yang and coworkers have previously reported shape-controlled Pt/Pd core–shell nanoparticles. Pt/Pd core–shell nanocubes, cuboctahedra, and octahedra could be made by using Pt cube seed crystals. High-resolution TEM (HRTEM) images revealed [*] Prof. Dr. H. Yang Department of Chemical Engineering University of Rochester Gavett Hall 206, Rochester, NY 14627 (USA) Fax: (+ 1)585-273-1348 E-mail: hongyang@che.rochester.edu Homepage: http://www.che.rochester.edu/~hongyang/