Abstract:Recent advances in dental resin based restorative materials have given rise to development of composites for bulk placement, to replace the need for incremental layering. Clinical consequences of microleakage are secondary caries, pulp inflammation, marginal discoloration, postoperative sensitivity, and the longevity of filling. Surface hardness is one of the mechanical properties of the restoration that should always be taken into account, particularly when they are faced with large areas of heavy masticatory forces. Accordingly, the current study was conducted to investigate the effect of packing technique and curing time on the marginal sealing and surface hardness of two bulk fill resin composites.Standardized class II proximal box cavities were prepared on the mesial and distal surface of the selected premolar teeth with the total of 48 cavities. The prepared cavities were randomly divided into 2 main groups, 24 cavities each, according to the placement technique used for cavity restoration either placement of bulkfill single increment of 4 mm depth or incremental placement of two increments of 2 mm each. Each group was subdivided into 2 subgroups, 12 cavities each, according to the bulk fill composite resin used; X-trafil bulkfill composite and Quixfil bulkfill composite. These subgroups were then subdivided into two smaller groups, 6 cavities each, according to the curing times either curing for 10 seconds following the manufacturers’ instructions or curing for 20 seconds. For all specimens, after bonding procedures, bulk-fill resin composites were manipulated and applied in cavities as the previously assigned methodology, specimens were then immersed in 2% methylene blue dye for 24 hours. Teeth were sectioned and viewed under a binocular stereomicroscope. Readings were recorded.A total of 80 cylindrical resin composite specimens were prepared. samples were divided into 4 groups according to the type of bulk fill composite (X-tra fil or Quixfil) and irradiation time (10s or 20s). The resin composite was applied in the mold, covered with mylar strips and light cured using LED light curing unit with an intensity of 1200mW/cm2. Vickers Microhardness tester was used with microindentation carried out using a load of 500g. Three readings for each surface were taken and an average reading was calculated. X-trafil bulkfill composite showed significantly lower degree of leakage than Quixfil bulkfill composite. No significant difference in microleakage was shown between different curing times nor different application techniques. X-trafil bulkfill composite showed significantly higher microhardness than Quixfil bulkfill composite Curing for 10 seconds showed significantly higher microhardness. Bulk-fill single increment of 4 mm recorded significantly higher microhardness value. Within the limitations of the current study, we can conclude that 4-mm bulk fill packing of bulkfill composite resin, cured for 10 seconds, had adequate marginal sealing performance. Surface microhardness of bulkfill composite resin packed at 4-mm bulk fill, cured for 10 seconds, is acceptable.

Effect of Filler Content on the Microtensile Bond Strength of Composite Resin and Dentin in Class I Cavities.

Influence of Casein Phosphopeptide-Amorphous Calcium Phosphate Application, Smear Layer Removal, and Storage Time on Resin-Dentin Bonding

Evaluation of micro-tensile bond strengths of composite materials in comparison to their polymerization shrinkage

Influence of Filler Content on Physicomechanical and Bonding Properties of an Experimental Dental Resin Cement

Effect of Bulk-filling on the Bonding Efficacy in Occlusal Class I Cavities

Incremental Filling Technique and Composite Material—Part I: Cuspal Deformation, Bond Strength, and Physical Properties

Correlation between Dental Composite Filler Percentage and Strength, Modulus, Shrinkage Stress, Translucency, Depth of Cure and Radiopacity

Mechanical Properties of Bulk-Fill Resin Composites with Single Increment Up to 4 Mm: A Novel Mechanical Strength Test

3D micro-CT and O-PTIR spectroscopy bring new understanding of the influence of filler content in dental resin composites

Effect of Polywave and Monowave Light Curing Units on the Microtensile Bond Strength and Failure Types of Different Bulk-Fill Resin Composites: An in vitro Study

Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites

Effect of packing technique and curing time on the marginal sealing and surface hardness of two bulk-fill resin composites

Evaluation of Microtensile Bond Strength and Microleakage of a Self-adhering Flowable Composite.

Finite Element Stress Analysis of Three Filling Techniques for Class V Light-cured Composite Restorations

Influence of Filler Particle Sizes on the Physical Properties of Bulk-Fill Composites Compared to Conventional Composites

Evaluation of Two Resin Composites Having Different Matrix Compositions

Microtensile Bond Strength, Marginal Leakage, and Antibacterial Effect of Bulk Fill Resin Composite with Alkaline Fillers versus Incremental Nanohybrid Composite Resin

[Effect of Filler Content of Composite Resins on Polymerization Shrinkage Measured by a Video Imaging Apparatus (Acuvol)].

The Effect of Inorganic Filler Content on the Properties of BPA-Free Bulk-Fill Dental Resin Composites

Micro-tensile bond testing of resin cements to dentin and an indirect resin composite

Effect of Porous Glass–ceramic Fillers on Mechanical Properties of Light-Cured Dental Resin Composites