In vitro physicochemical properties, osteogenic activity, and immunocompatibility of calcium silicate-gelatin bone grafts for load-bearing applications.

Shinn-Jyh Ding,Ming-You Shie,Chung-Kai Wei

DOI: https://doi.org/10.1021/am201017v

IF: 9.5

2011-01-01

ACS Applied Materials & Interfaces

Abstract:The use of a composite made of natural polymer gelatin and bioactive calcium silicate resembling the morphology and properties of natural bone may provide a solution to the problem of ceramic brittleness for load-bearing applications. The in vitro bioactivity, degradability, osteogenic activity, and immunocompatibility of three types of calcium silicate-gelatin composite bone grafts were characterized. The osteogenic activity and immunocompatibility were evaluated by incubating the bone grafts with human dental pulp cells. After soaking in a simulated body fluid (SBF) for 1 day, all materials were covered with clusters of "bone-like" apatite spherulites. The control material without gelatin exhibited an insignificant change in strength, degradability, and porosity and a small weight loss of 6% after 180 days of soaking in the SBF solution. In contrast, the soaking time imposed in this study did have a statistically significant effect on compressive strength, porosity, and weight loss of the gelatin-containing composites. After 180 days of soaking, the composite with 10 wt % gelatin lost 47% and 10% in compressive strength and weight, respectively, with a porosity of 23%. However, the presence of gelatin promoted greater cell attachment and proliferation on the composite bone grafts. Pulp cells on the calcium silicate-gelatin bone grafts expressed higher levels of osteocalcin, osteopontin, and bone sialoprotein. The inhibition of inducible nitric oxide synthase and interleukin-1 expression and the activation of interleukin-10 were increased with increasing gelatin content. Overall, these findings provide evidence that composite bone grafts containing 10 wt % gelatin with a high initial strength were bioactive, nontoxic, and osteogenic and may be able to promote bone healing for load-bearing applications.