Abstract:Ultra-long single-crystalline trigonal selenium submicrotubes were synthesized using a facile one-step solution-phase approach with the assistance of nonionic surfactant Polyoxyethylene(20)sorbitan monolaurate (Tween-20), which turned out to be significant for the formation of ultra-long Se submicrotubes. XRD, Raman, SEM, and TEM were adopted to characterize the morphology, structure and phase composition of the as-prepared Se products. It was found that the length of the obtained Se submicrotubes was over 100 pm. By variation of the experimental parameters, the t-Se spheres, nanowires, and broken microtubes can be prepared. The possible growth mechanism of the ultra-long selenium submicrotubes was explained. In addition, we have also demonstrated that the synthesized Ultra-long t-Se submicrotubes using the Tween-20-assisted approach can electrochemically charge and discharge with the high capacity of 265 mAh/g (corresponding to 0.97 wt % hydrogen in SWNTs) under normal atmosphere at room temperature. Cyclic voltammetry was adopted to investigate the adsorption-ox idation behavior of ultra-long selenium submicrotubes. It was observed that the morphology of the synthesized selenium products had a remarkable influence on their capacity of electrochemical hydrogen storage. These differences in hydrogen storage capacity are likely due to the size and density of tubes as well as the microcosmic morphology of different Se samples. The as-obtained ultralong Se submicrotubes are expected to find wide applications in hydrogen storage, high-energy batteries, and optoelectronic, biologic, and catalytic fields as well as in the studies of structure-property relationships. This simple Tween-assisted approach might be extended to the preparations of one-dimensional nanostructures of tellurium and other anisotropic materials.

Fabrication of Selenium/carbon Core-Shell Submicrowires and Carbon Submicrotubes by a Facile Solution Process.

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Investigation of the Fabrication and Structure of Double-Wall Carbon Nanotubes

Aqueous-Based Coaxial Electrospinning of Genetically Engineered Silk Elastin Core-Shell Nanofibers

Direct Fabrication of Tellurium/Carbon Nanocables Through a Facile Solution Route

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Solution-phase synthesis and electrochemical hydrogen storage of ultra-long single-crystal selenium submicrotubes.

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Development of Microsturcture Based on Single-Wall Carbon Nanotube.

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Fabrication of Ag2SiO3/SiO2 Composite Nanotubes Using a One-Step Sacrificial Templating Solution Approach

One-Step Synthesis Of Single-Wall Carbon Nanotube-Zns Core-Shell Nanocables

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Synthesis of Copper-Core/Carbon-Sheath Nanocables by a Surfactant-Assisted Hydrothermal Reduction/Carbonization Process

Fabrication and microstructure analysis of SeO 2 nanowires

Confined self-assembly approach to produce ultrathin carbon nanofibers.

One-Step Microwave Synthesized Core-Shell Structured Selenium@Carbon Spheres As Cathode Materials for Rechargeable Lithium Batteries

Microfabrication Of Single-Wall Carbon Nanotube One-Dimensional Unit

Conical Carbon Fibers with Carbon Nanotubes As Their Cores: Fabrication, Characterization and Field Emission

Templated Fabrication of Core–Shell Magnetic Mesoporous Carbon Microspheres in 3-Dimensional Ordered Macroporous Silicas

Fabrication of carbon nanofibers with Si nanoparticle-stuffed cylindrical multi-channels via coaxial electrospinning and their anodic performance