Abstract:A series of compounds with the ${\mathrm{ThMn}}_{12}$-type structure, R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ (R=Y, Sm, Gd, Tb, Dy, Ho, Er, and Lu), were synthesized. The corresponding nitrides, obtained by gas-solid reactions, retained the same structure as their parent compounds, but with a relative volume expansion of 3%. The Nb atoms occupy the 8i sites in the ${\mathrm{ThMn}}_{12}$ structure. The highest Curie temperatures are 597 K and 773 K for ${\mathrm{GdFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ and its nitride, respectively. The average iron magnetic moment ${\mathrm{\ensuremath{\mu}}}_{\mathrm{Fe}}$ at T=1.5 K is 1.9${\mathrm{\ensuremath{\mu}}}_{\mathit{B}}$ for parent compounds and 2.1${\mathrm{\ensuremath{\mu}}}_{\mathit{B}}$ for the nitrides. By the introduction of nitrogen, the Fe-Fe exchange interaction is much strengthened while the R-Fe exchange interaction is slightly weakened. The enhancement of ${\mathrm{\ensuremath{\mu}}}_{\mathrm{Fe}}$ by the influence of interstitial nitrogen is about 11%. The Fe sublattices of R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compounds and their nitrides have an easy c-axis anisotropy. At T=1.5 K, the anisotropy constant ${\mathit{K}}_{1}$(Fe) is 25.7 K/f.u. for the parent compounds and 21.9 K/f.u. for the nitrides. The reduction of ${\mathit{K}}_{1}$(Fe) by the influence of interstitial nitrogen is about 17%. Spin-reorientation transitions were observed in ${\mathrm{DyFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ and ${\mathrm{ErFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compounds. The complex magnetic behavior of R${\mathrm{Fe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ at low temperatures can be explained by exchange and crystal-field-interaction models. The ${\mathrm{SmFe}}_{11.35}$${\mathrm{Nb}}_{0.65}$ compound has an anisotropy field of 10.0 T at room temperature. Its high Curie temperature and magnetization make it a potential candidate for applications as a permanent magnet.

Magnetic Phase-Transitions, Magnetocrystalline Anisotropy, and Crystal-Field Interactions in the Rfe11ti Series (where R = Y, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, or Tm)

Spin-reorientation transitions in RFe11Mo (R=rare earth and Y) intermetallic compounds

Crystallographic and Magnetic Properties of R3Fe29-xTx and Their Nitrides, Carbides and Hydrides

Structure And Magnetic-Properties Of Rfe(11.35)Nb(0.65) And Rfe(11.35)Nb(0.65)N(Y) (R=Y, Sm, Gd, Tb, Dy, Ho, Er, And Lu)

STRUCTURAL AND MAGNETIC PROPERTIES OF RTiFe 11 ,rtico 11 AND RTi(Fe 1-X Ni X ) 11 COMPOUNDS(R=Nd,Sm,Gd,Tb,Dy,Ho,Er AND Y)

Hydrogenation and Anisotropic Expansions in R3fe29-Xtx (R = Y, Ce, Nd, Sm, Gd, Tb and Dy; T = V and Cr)

Reentrant spin reorientation transition and Griffiths-like phase in antiferromagnetic TbFe$_{0.5}$Cr$_{0.5}$O$_3$

Theoretical Explanations Of Magnetocrystalline Anisotropy Behaviors In Rtife11nx Compounds

873 K isothermal section of phase diagram for Y-Fe-Ti ternary system

Structural And Magnetic Properties Of The R < Sub > 10 </Sub > Fe < Sub > 90-X </Sub > Si < Sub > X </Sub > Alloys With R = Y, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, And Er

Structual and Magnetic Properties of RMo1.5Fe10.5Nx

Magnetic Properties of R Ions in RCo5 Compounds (r=pr, Nd, Sm, Gd, Tb, Dy, Ho, and Er).

STUDY ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF RFe10.5V1.5Nx

Magnetic-Properties of New Series R-Mo-Fe Nitrides with the Thmn12-Type Structure at A Lower Mo Content

Twofold Spin Reorientation and Field-Induced Incomplete Phase Transition in Single-Crystal Dy0.5pr0.5feo3

The Magnetocrystalline Anisotropy Of R2co17-Xmnx (R = Pr, Nd, Tb, Dy And Ho) Compounds

Temperature And Field Induced Spin Reorientation And Dielectric Properties In Ycr0.88fe0.12o3 Single Crystal

Magnetic and transport anomalies in the compounds, RCuAs2 (R= Pr, Nd, Sm, Gd, Tb, Dy, Ho, and Er)

Field tuning magnetic phase transition in Dy0.5Tb0.5FeO3 single crystal

Magnetic properties of RFe$_2$Zn$_{20}$ and RCo$_2$Zn$_{20}$(R = Y, Nd, Sm, Gd - Lu)

Rare-earth/transition-metal magnetic interactions in pristine and (Ni,Fe)-doped YCo5 and GdCo5