Abstract:This study was carried out to evaluate the effect of acid etching versus laser etching of dentin surface on the bonding of Composite and Compomer restorative materials to dentin surface by studying microleakage at the dentin-filling interface, compositional analysis of dentin surface, and Scanning Electron Microscopic (SEM) study of the bonding area. 120 freshly extracted premolar teeth were divided according to surface treatment into three groups. Group I (Acid etching group) contained thirty teeth. Twenty teeth were selected to assess microleakage by forming standardized class V cavity on the buccal surface of the selected teeth. Then, teeth were subdivided into two subgroups with 10 teeth in each. Subgroup (i) delivered composite filling while subgroup (ii) delivered compomer filling according to manufacturer instructions. microleakage at the dentin-filling interface of teeth was examined using dye penetration method. dye penetration scores at occlusal and gingival margins were recorded and tabulated. Five dentin surfaces of five teeth from group I were etched by acid then prepared for compositional analysis of dentin surface by Infra-Red (IR) Spectroscopy. Another Five dentin surfaces were etched by acid then prepared for (SEM) assessment. Group II (Laser etching group) contained ninety teeth, twenty teeth were used for assessing microleakage after laser etching taking similar steps to that of acid etching. Thirty dentin surfaces of thirty teeth were etched by laser with different parameters then prepared for compositional analysis of dentin surface by IR Spectroscopy. Thirty dentin surfaces of thirty teeth were etched by laser with different parameters then prepared for SEM assessment. Group III (Untreated group) contained ten teeth that were left untreated. Five dentin surfaces of five teeth were subjected to IR Spectroscopy assessment. Five dentin surfaces of five teeth were prepared for SEM assessment. The results revealed that acid etching of dentin surface resulted in significant less leakage compared to laser etching. IR Spectroscopy revealed changes in dentin surface structure indicating that there was a reaction occurred by the acid and laser etching. SEM assessment showed more openings of dentinal tubules in case of acid etching, while in case of laser etching, there were a surface structural changes with a melting and fusion dentin surface. Acid etching of dentin gives better results on the bonding of Composite and Compomer filling materials than laser etching and thus gives more successful clinical condition. Further investigations are needed by using different types of laser to get more benefit from applications of laser clinically.

Dentin Surface Modification Using the Er,Cr:Ysgg Laser and A Meshwork Mask: Light and Sem Microscopic Observations

The Bond Strength Experiment of Enamel and Dentin Exposed to Pulsed Nd :YAG Laser

Bond Strength Experiment of Human Dentin Following Pulsed Nd:YAG Laser

Enamel and Dentin Exposed to Pulsed Nd∶YAG Laser

Er,Cr:YSGG Laser Surface Modification Effect on Dentin Bonding to Zirconia: An In Vitro Study

[Ultrastructural Study of Sclerotic Dentin Surface Following the Application of the Er, Cr: YSGG Laser].

Effect of Er,Cr:YSGG laser parameters on shear bond strength and microstructure of dentine.

SEM Evaluation of Tooth Surface after a Composite Filling Removal Using Er:YAG Laser, Drills with and without Curettes, and Optional EDTA or NaOCl Conditioning

Effect of Er∶YAG Laser Treatment on Dentin Surface and Bonding Strength

Preliminary Exploration of a Laser-Based Surface Microtexturing Strategy for Improving the Wear Resistance of Dentin: an in Vitro Study.

Topographical Analysis of Human Enamel after Phosphoric Acid Etching and Er,Cr:YSGG Laser Irradiation

Comparative study of the effect of laser irradiation and acid etching surface treatment on bonding of some dental restorative materials To dentin surface

Laser etching of enamel for direct bonding with an Er,Cr:YSGG hydrokinetic laser system

Er:YAG Laser Physical Etching and Ultra-High-Molecular-Weight Cross-Linked Sodium Polyacrylate Chemical Etching for a Reliable Dentin Dry Bonding

Influence of Er∶ YAG Laser Treatment on Enamel Surface and Shear Bond Strength of Resin

Dentin pretreatment with Er:YAG laser and sodium ascorbate to improve the bond strength of glass fiber post

Morphological Analysis of Irradiated Dentin by Scanning Electron Microscope under Anhydrous Condition

Occluding Efficiency of Different Desensitizing Agents and Er,Cr:YSGG Laser on Dentin Tubules

[Scanning Electron Microscopy Was Used to Observe Dentin Morphology in Primary and Permanent Teeth Treated by Erbium: Yttrium-Aluminum-garnet Laser].

Effects of Er,Cr:YSGG Laser on the Root Surface of Periodontitis and Healthy Teeth

The Effect Of Er,Cr:YSGG Laser Conditioning on Dentin Bond Strength and Nanoleakage of Universal Adhesive Systems: An In Vitro Study