Crystal Growth and Luminescent Properties of ZnO Sub-microrods and Microrods
Jian-gang CHEN,Chang-xin GUO,Lin-li ZHANG,Jun-tao HU,Peng GUO
DOI: https://doi.org/10.3321/j.issn:1000-7032.2005.01.015
2005-01-01
Chinese Journal of Luminescence
Abstract:Various size ZnO hexagonal microrods have been synthesized onto glass substrates through aqueous growth method with the thermal decomposition of an aqueous solution of equimolar zinc nitrate(Zn(NO_3)_2·(4H_2O)) and methenamine ((CH_2)_6N_4) by controlling the experimental conditions. The ZnO microrods grow from one center to form radial clusters, which consist of more than 2 pair rods symmetrically grown from the center to both sides, and the rods have a flat top end perpendicularly. When the growth time reached two days, we found that the microrods turned into hollow microtubes with the tube-thickness of tenth of diameter. XRD patterns, SEM images, Raman spectrum have been measured, which revealed all samples were hexa-(gonal) microrods of ZnO with length of 5～6 μm and diameter of 0.8～5 μm. The Raman spectrum showed four peaks at 332.2, 377.6, 435.4 and 577.8 cm~(-1), assigned to the 2E_2,A_1,E_2 and E_1(LO)modes, (respectively.) The growth mechanism is discussed, Zn(NO_3)_2 dissolves and forms growth units of tetrahedron Zn-(OH)_4 under the reaction of the surface activator (CH_2)_6N_4, then the incorporation of growth units leads to the formation of the ZnO crystal lattice at the interface through a dehydration reaction (OH~-+OH~-(H_2O+)O~(2-)). The fastest of the growth velocity along [0001] direction leads to the formation of the ZnO microrods. The excitation spectra showed that except the intrinsic inter-band excitation of shorter than 370 nm, there was a strong exciton excitation peak located at 387 nm with FWHM 30 nm at room temperature. The photoluminescent spectra showed that there was a wide orange-red emission with peak at 630 nm and FWHM 250 nm when the excitaion wavelength at 387 nm. The cathodoluminescent spectra showed a strong orange (emission) peak at 580 nm with FWHM 140 nm and a weak UV emission peak at 395 nm with FWHM 20 nm. Compared with the calculated data of these intrinsic defects by the literature with the theory of FP-LMTO, we (attribute) the orange-red and red emission to the luminescent transition from oxygen vacancies to the valence band.