Abstract:We report a one-pot method to synthesize CoO/C hybrid microspheres via a solvothermal approach. The resulting samples were characterized by thermogravimetric analysis, X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, transmission electron microscopy and charge–discharge test. X-ray diffraction analysis revealed that the as-prepared samples possessed poor crystalline characteristics and were transformed into crystalline materials after thermal treatment. Field-emission scanning electron microscope images showed that the surfaces of these as-prepared spheres were relatively smooth and of about 2.2μm in diameter. The diameters of the spheres kept unchanged after being annealed at 800°C in a high purity nitrogen atmosphere under ambient pressure. The preliminary electrochemical test found that the annealed CoO/C hybrid microspheres exhibited an ultrahigh initial discharge capacity of 1481.4mAhg−1 in the potential range of 3.0–0.01V. This value was much higher than that of CoO nanoparticles. Although the capacity of the second discharge cycle decayed to 506.2mAhg−1, the annealed CoO/C hybrid microspheres anode exhibited very stable reversible capacity at about 345mAhg−1 only after 10 cycles. This rapid stabilization ability was attributed to the matrix effect of carbon, which may effectively prevent the aggregation of small particles during charging–discharging process.

One-Pot Synthesis of Uniform Carbon-Coated Moo2 Nanospheres for High-Rate Reversible Lithium Storage

One-pot synthesis of uniform carbon-coated MoO(2) nanospheres for high-rate reversible lithium storage

ChemInform Abstract: One‐Pot Synthesis of Uniform Carbon‐Coated MoO2 Nanospheres for High‐Rate Reversible Lithium Storage.

Synthesis of Co3O4@SnO2@C core-shell nanorods with superior reversible lithium-ion storage

Construction of Moo2 Quantum Dot-Graphene and Mos2 Nanoparticle-Graphene Nanoarchitectures Toward Ultrahigh Lithium Storage Capability

Interconnected Moo2 Nanocrystals with Carbon Nanocoating As High-Capacity Anode Materials for Lithium-Ion Batteries

One-pot synthesis of uniform Fe3O4 nanocrystals encapsulated in interconnected carbon nanospheres for superior lithium storage capability

One-pot Synthesis of Uniform Fe₃O₄ Nanospheres with Carbon Matrix Support for Improved Lithium Storage Capabilities.

Uniform Moo2@Carbon Hollow Nanospheres With Superior Lithium-Ion Storage Properties

Synthesis of Co2SnO4@C core-shell nanostructures with reversible lithium storage

Controlled Synthesis of N-doped Carbon and TiO2 Double-Shelled Nanospheres with Encapsulated Multi-Layered MoO3 Nanosheets As an Anode for Reversible Lithium Storage

Local-ordering MoO2 Nanostructures Within Porous N-doped Carbon Nanotubes for High-Rate Reversible Lithium Storage

Preparation of Carbon Coated Moo2 Nanobelts and Their High Performance As Anode Materials for Lithium Ion Batteries

One‐Pot Hydrothermal Synthesis of FeMoO4 Nanocubes as an Anode Material for Lithium‐Ion Batteries with Excellent Electrochemical Performance

One-Pot Synthesis of Uniform Mose2 Nanoparticles As High Performance Anode Materials for Lithium/Sodium Ion Batteries

Confining MoS2 nanocrystals in MOF-derived carbon for high performance lithium and potassium storage

One-Pot Synthesis Of Carbon-Coated Sno2 Nanocolloids With Improved Reversible Lithium Storage Properties

Facile Synthesis of Carbon-Coated MoS2 Nanorods with Enhanced Lithium Storage Properties

One-pot Synthesis of CoO/C Hybrid Microspheres As Anode Materials for Lithium-Ion Batteries

Mo‐Based Ultrasmall Nanoparticles on Hierarchical Carbon Nanosheets for Superior Lithium Ion Storage and Hydrogen Generation Catalysis

Facile synthesis of transition-metal oxide nanocrystals embedded in hollow carbon microspheres for high-rate lithium-ion-battery anodes.