Abstract:This work reports a facile approach to fabricate a perpendicularly aligned and highly ordered TiO(2) nanorod/nanotube (NR/NT) adjacent film by directly anodizing a modified titanium foil. The titanium foil substrate was modified with a layer of crystalline TiO(2) film via a hydrothermal process in 0.05 M (NH(4))(2)S(2)O(8). The resultant NR/NT architecture consists of a highly ordered nanorod top layer that directly adjoins to a highly ordered nanotube array bottom layer. The thickness of the top nanorod layer was approximately 90 nm with average nanorod diameter of 22 nm after 20 min of anodization. The thickness of the bottom nanotube array layer was found to be ca. 250 nm after 20 min of anodization, having an average outer and inner tubular diameters of 120 and 80 nm, respectively. A broad implication of the method is that a simple modification to the substrate surface can lead to new forms of nanostructures. For as-anodized NR/NT samples, XRD analysis reveals that the nanorods are of anatase TiO(2) crystalline form while the nanotubes are amorphous. Anatase TiO(2) crystalline form of NR/NT film with high crystallinity can be obtained by thermally treating the as-anodized sample at 450 degrees C for 2 h in air. The resultant NR/NT film was used as a photoanode for photoactivity evaluation. Comparing with a nanotube array photoanode prepared by direct anodization of unmodified titanium foil, the NR/NT photoanode exhibits a unique feature of selective photocatalytic oxidation toward organics, which makes it very attractive to photocatalytic degradation of organic pollutants, sensing, and other applications.

Ti Nanorod Arrays with Periodic Density Fabricated Via Anodic Technology

Silver-Decorated Tio2 Nanorod Array Films with Enhanced Photoelectrochemical and Photocatalytic Properties

Anodic Formation of Ti Nanorods with Periodic Length

A Facile Method for Fabrication of Self-Ordered Aluminum Nanodimple Arrays with Continuously Tunable Period from 60 to 89 Nm

Synthesis of Various Metal/TiO2 Core/shell Nanorod Arrays

Structural Engineering of Highly Ordered TiO2 Nanotube Array by Periodic Anodization of Titanium

Fabrication of Highly Ordered TiO2 Nanorod/nanotube Adjacent Arrays for Photoelectrochemical Applications.

Fabrication of a TiO2/Au Nanorod Array for Enhanced Photocatalysis

Of periodic metal nanodots arrays

Preparation and Mineralization Properties of Titanium Nanorod Arrays with Controllable Density

Anodic Fabrication of Ti-Nb-Zr-O Nanotube Arrays

One-Step Fabrication of Ni/Tio2 Core/Shell Nanorod Arrays in Anodic Aluminum Oxide Membranes

Electrochemical Fabrication Of Highly Ordered Semiconductor And Metallic Nanowire Arrays

Fabrication of a Regular Tripod Ni–P Nanorod Array and an AAO Template with Regular Branched Nanopores Using a Current-Controlled Branching Method

Large-area alloy nanotube arrays with highly-ordered periodicity: Fabrication and characterization

Anodic Fabrication of Ti-Ni-O Nanotube Arrays on Shape Memory Alloy

Fabrication of Free-Standing Cu Nanorod Arrays on Cu Disc by Template-Assisted Electrodeposition

Periodic TiO2 Nanorod Arrays with Hexagonal Nonclose‐Packed Arrangements: Excellent Field Emitters by Parameter Optimization

Hydrophilicity reinforced adhesion of anodic alumina oxide template films to conducting substrates for facile fabrication of highly ordered nanorod arrays

Fabrication of TiO 2 nanotubes with extended periodical morphology by alternating-current anodization

Study on preparation of TiO_2 nanotube arrays by anodizing processes