Optical and ESR Properties of Novel Cumulenes and Poly(p-Phenylene-cumulenes) (PCC).

Smith, A.V.,Shinar, J.,Lin, J.,Barton, T.J.

DOI: https://doi.org/10.1109/stsm.1994.834704

1994-01-01

Abstract:Summary form only given. The optical absorption, ESR, and LESR of novel PPC, with the repeat unit - [Ph (PhORC)=C=C=(CPhOR)]-, is described and discussed. The absorption edge is very broad, with onset at /spl sim/-710 nm, and pronounced peaks at 543, 483, and 437 nm, i.e., split by 0.28 eV. This value should be compared to the C=C=C=C stretch vibration frequency of 1950 cm/sup -1/ (0.24 eV). While some variants of the cumulene oligomers luminesce, no photoluminescence is detectable from PPC powder or solutions, and it is believed that the radiative decay rate of the polymer is very slow in comparison to nonradiative paths. Upon doping by exposure to iodine vapor, the conduclivity immediately increases from /spl sim/10/sup -7/ to /spl sim/1 S/cm. The undoped defect ESR density is very low, N/sup 8/ /spl p/ 3.4 x 10 /sup 14/ spins/g (2.7 x 10/sup -7/ pins per repeat unit), and /spl utri/H/sub pp//sp ap/2.7G. Upon doping, it increases N/sub 8//spl ap/1.2x 10/sup 17/ spins/g (1 spin per 10/sup 4/ repeat units), and /spl utri/H/sub PP/ increases to 5.9 G. The absence of detectable PL, the conductivity, and doping-induced ESR are all similar to the behavior of polydiethynylsilanes (PDES); the nature of the optical and electronic properties of PPC is thus discussed in relation to that latter system.