Abstract:We develop a simple chemical method to obtain bulk quantities of N-doped, reduced graphene oxide (GO) sheets through thermal annealing of GO in ammonia. X-ray photoelectron spectroscopy (XPS) study of GO sheets annealed at various reaction temperatures reveals that N-doping occurs at a temperature as low as 300C, while the highest doping level of ~5% N is achieved at 500C. N-doping is accompanied by the reduction of GO with decreases in oxygen levels from ~28% in as-made GO down to ~2% in 1100C NH3 reacted GO. XPS analysis of the N binding configurations of doped GO finds pyridinic N in the doped samples, with increased quaternary N (N that replaced the carbon atoms in the graphene plane) in GO annealed at higher temperatures (>900C). Oxygen groups in GO were found responsible for reactions with NH3 and C-N bond formation. Pre-reduced GO with fewer oxygen groups by thermal annealing in H2 exhibits greatly reduced reactivity with NH3 and lower N-doping level. Electrical measurements of individual GO sheet devices demonstrate that GO annealed in NH3 exhibits higher conductivity than those annealed in H2, suggesting more effective reduction of GO by annealing in NH3 than in H2, consistent with XPS data. The N-doped reduced GO shows clearly n-type electron doping behavior with Dirac point (DP) at negative gate voltages in three terminal devices. Our method could lead to the synthesis of bulk amounts of N-doped, reduced GO sheets useful for various practical applications.

Controllable S-doping of Graphene Through Annealing with Hydrogen Sulfide

Reversible Sulfuric Acid Doping of Graphene Probed by in-situ Multi-Wavelength Raman Spectroscopy

Synthesis of S-doped graphene by liquid precursor.

Synthesis of Nitrogen-Doped Graphene Via Thermal Annealing Graphene with Urea

Current‐Induced Complementary Doping to Graphene from Hydrogen Silsesquioxane Passivation Layer

Controlled assembly of SiOx nanoparticles in graphene

UV–annealing synthesis of sulfur-doped graphene for bisphenol A electrocatalytic degradation

High Fluorescent Sulfur Regulating Graphene Quantum Dots with Tunable Photoluminescence Properties.

Elemental Superdoping of Graphene and Carbon Nanotubes.

Preparation and electrochemical properties of sulfur-doped three-dimensional graphene

Controlling doping in graphene through a SiC substrate: A first-principles study

Atmospheric Oxygen Binding and Hole Doping in Deformed Graphene on a SiO2 Substrate

Substitutional Doping of Ag into Epitaxial Graphene on 6H-Sic Substrates During Thermal Decomposition

Simultaneous Nitrogen-Doping and Reduction of Graphene Oxide

Semiconducting Single-Walled Carbon Nanotubes Synthesized by S-Doping

Reversible N-Type Doping of Graphene by H2o-Based Atomic-Layer Deposition and Its Doping Mechanism

Doping Monolayer Graphene with Single Atom Substitutions

Investigation of Sulfur Doping in Mn-Co Oxide Nanotubes on Surface-Enhanced Raman Scattering Properties

Reduction of Graphene Oxide by Hydrogen Sulfide: A Promising Strategy for Pollutant Control and as an Electrode for Li‐S Batteries

Tuning the Adatom-Surface and Interadatom Interactions in Hydrogenated Graphene by Charge Doping

Facile and Highly Effective Synthesis of Controllable Lattice Sulfur-Doped Graphene Quantum Dots Via Hydrothermal Treatment of Durian