Abstract:Objective(s): Bioglass scaffolds, which contain a significant percentage of porosity for tissue engineering purposes, have low strength. For increasing the strength and efficiency of such structures for use in tissue engineering, fabrication of hierarchical meso/macro-porous bioglass scaffolds, developing their mechanical strength by hydrothermal treatment and adjusting pH method, and achieving the appropriate mesopore size for loading large biomolecules, were considered in this study. Materials and Methods: Mesoporous bioglass (MBG) powders were synthesized using cetyltrimethylammonium bromide as a surfactant, with different amounts of calcium sources to obtain the appropriate size of the mesoporous scaffolds. Then MBG scaffolds were fabricated by a polyurethane foam templating method, and for increasing scaffold strength hydrothermal treatment (90 °C, for 5 days) and adjustment pH (pH=9) method was used to obtain hierarchical meso/macro-porous structures. The sample characterization was done by Simultaneous thermal analysis, Fourier transform infrared spectroscopy, Field Emission Scanning electron microscopy, small and wide-angle X-ray powder diffractions, transmission electron microscopy, and analysis of nitrogen adsorption-desorption isotherm. The mechanical strength of scaffolds was also determined. Results: The MBG scaffolds based on 80.28 (wt.) % SiO2- 17.89 (wt.) % CaO- 1.81 (wt.) % P2O5 presented interconnected large pores and pores in the range of 100-150 μm and 6-18 nm, respectively and 0.4 MPa compressive strength. Conclusion: The total pore volume and specific surface area were obtained from the Brunauer-Emmett-Teller theory, 0.709 cm3 g-1 and 213.83 m2 g-1, respectively. These findings could be considered in bone-cartilage tissue engineering.

Resorbable, porous glass scaffolds by a salt sintering process

Borophosphate glass-ceramic scaffolds by a sodium silicate bonding process

Porous β-NaCaPO4 containing borate glass-ceramic scaffolds

Salt leaching using powder (SLUP) process for glass/chitosan scaffold elaboration for biomaterial applications

RESEARCH ON POROUS BONE-TISSUE ENGINEERING SCAFFOLDS MADE FROM POLYHYDROXYALKANOATE/BIOACTIVE GLASS COMPOSITES

Bioactive Borosilicate Glass Scaffolds: in Vitro Degradation and Bioactivity Behaviors

Pore graded borosilicate bioactive glass scaffolds: in vitro dissolution and cytocompatibility

Highly porous bio-glass scaffolds fabricated by polyurethane template method with hydrothermal treatment for tissue engineering uses

Fabrication of porous apatite-wollastonite glass ceramics using a two steps sintering process

Stiff macro-porous bioactive glass-ceramic scaffold: Fabrication by rapid prototyping template, characterization and in vitro bioactivity

In Vitro Bioactivity and Cytocompatibility of Porous Scaffolds of Bioactive Borosilicate Glasses

Robust Hierarchical Porous MBG Scaffolds with Promoted Biomineralization Ability.

Foam-Replicated Diopside/Fluorapatite/Wollastonite-Based Glass–Ceramic Scaffolds

Porous polymeric structures for tissue engineering prepared by a coagulation, compression moulding and salt leaching technique

Polymer Sponge Replication Technology Derived Strontium-Substituted Apatite (Sr-HAP) Porous Scaffolds for Bone Tissue Engineering

Microstructure and Controllable Degradation of Bioglass Reinforced Calcium Phosphate Scaffolds

A new generation of sodium chloride porogen for tissue engineering

Study on Poly(β-Hydroxybutyrate-Co-β-Hydroxyvalerate)/Bioglass Composites As Scaffold for Tissue Engineering

Mimicking the Architecture and Dissolution Chemistry of Cancellous Bone Tissue to Optimize the Biocompatibility of Bioactive Scaffolds

In vitro and in vivo dissolution of biocompatible S59 glass scaffolds

Biodegradable borosilicate bioactive glass scaffolds with a trabecular microstructure for bone repair.