Abstract:Metal organic frameworks (MOFs) are of significant interest for photocatalysis using visible light, but they are typically limited by the instability and high recombination ratio of photoexcited pairs. Integrating MOFs into an inorganic semiconductor is one of the most widespread methods to promote their activity. In this study, a core-shell structured MOF@TiO2 (NH2-UiO-66@TiO2) was synthesized as an efficient photocatalyst for the degradation of toluene. Pristine NH2-UiO-66 was synthesized by a hydrothermal method as the core, which was then coated with an amorphous TiO2 shell. Compared with pristine NH2-UiO-66 and other samples prepared by the direct mixing of NH2-UiO-66 and TiO2, NH2- UiO-66@TiO2 exhibited a higher degradation rate of toluene. Using NH2- UiO-66@TiO2 as a catalyst, the degradation efficiency of toluene reached 76.7% within 3 h, which is 1.48 times higher than that of NH2-UiO-66. The degradation performance was also stable in four repeated reuse experiments, and the slight deactivation was reactivated after washing with ethanol. A series of characterization methods were used to determine the physicochemical properties of NH2-UiO-66@TiO2, including X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Using the measured physicochemical properties, the photocatalytic mechanism of NH2-UiO-66@TiO2 was explored. NH2-UiO-66 is an ideal photocatalyst, with visible-light response and a huge specific surface area (914.9 m(2).g(-1)), which is favorable for the utilization of sunlight as well as the absorption of pollutants in indoor air. In addition, a new interface formed between the two components (NH2-UiO-66 and TiO2), which efficiently broaden the light absorption area and enhanced the utilization of photogenerated species. The photogenerated holes and electrons could transfer through the interlayer as soon as they were formed. It is speculated that holes would transfer to the HOMO of NH2-UiO-66, and then combine with H2O molecules to form hydroxyl radicals (center dot OH). At the same time, more electrons tended to combine with oxygen molecules in the conduction band of TiO2 rather than recombine with holes. Consequently, the recombination rate of electrons and holes decreased, while the quantity of oxygen radicals and hydroxyl radicals increased. Toluene was efficiently oxidized by these two types of radicals. Owing to the outstanding properties mentioned above, the strategy of constructing NH2-UiO-66@TiO2 is considered to be an effective approach. This work may provide new insights into the design of core-shell structured MOF@photocatalysts for the photocatalytic degradation of indoor air pollutants.

Controllable synthesis various morphologies of 3D hierarchical MnOx-TiO2 nanocatalysts for photothermocatalysis toluene and NO with free-ammonia

Enhancement of Toluene Removal over Α@δ-Mno2 Composites Prepared Via One-Pot by Modifying the Molar Ratio of KMnO4 to MnSO4·H2O

Highly active nanostick-assembled TiO2@MnOx hollow-sphere structure for photothermocatalysis of ethyl acetate and NO with free-ammonia at low temperature: Resistence, key reaction steps and mechanisms

Effects of the Morphology of MnO 2 Nanostructures on the Catalytic Oxidation of Toluene

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Hierarchical TiO2-g-C3N4 Photocatalyst with Purification Effect for NOx Oxidation Under Cyan Light

Catalytic oxidation of NO over SmMn2O5 nanostructures derived from different Mn precursors

Multifunctional Core-Double-Shell C@Mno@Tio2 Catalysts with Enhanced Full-Light Conversion for the Highly Efficient Photothermal Oxidation of Toluene

Atomically dispersed Mn sites on TiO 2 (B) microspheres enables efficient photocatalytic abatement of NOx

Enhancing Low-Temperature Catalytic Performance for Toluene Oxidation Using In-Situ Pyrolyzed Mn-Doped MOF-74 Derived MCNOx Catalysts

Performance and Mechanism of Co and Mn Loaded on Fe-Metal-Organic Framework Catalysts with Different Morphologies for Simultaneous Degradation of Acetone and NO by Photothermal Coupling

Core-Shell Structured NH2-UiO-66@TiO2 Photocatalyst for the Degradation of Toluene under Visible Light Irradiation

Titanate Nanowire As A Precursor for Facile Morphology Control of Tio2 Catalysts with Enhanced Photocatalytic Activity

Synthesis, Characterization and Catalytic Performance of Femntiox Mixed Oxides Catalyst Prepared by A Ctab-Assisted Process for Mid-Low Temperature Nh3-Scr

Morphology Control Studies of MnTiO3 Nanostructures with Exposed {0001} Facets As a High-Performance Catalyst for Water Purification.

Biomolecule-controlled hydrothermal synthesis of C-N-S-tridoped TiO2 nanocrystalline photocatalysts for NO removal under simulated solar light irradiation.

Amorphous/crystalline Cu1.5Mn1.5O4 with rich oxygen vacancies for efficiently photothermocatalytic mineralization of toluene

Advanced Mnox/Tio2 Catalyst with Preferentially Exposed Anatase {001} Facet for Low-Temperature Scr of No

Enhanced Low-Temperature Activity of Toluene Oxidation over the Rod-like MnO2/LaMnO3 Perovskites with Alkaline Hydrothermal and Acid-Etching Treatment

Directed Synthesis of Hierarchical Nanostructured TiO2 Catalysts and Their Morphology-Dependent Photocatalysis for Phenol Degradation.

Preparation of Ti-Hms Mesoporous Molecular Sieves and Their Photocatalytic Activity for Decomposition of Nitrogen Oxide