Abstract:The deterioration process and deterioration mechanism of magnesium oxychloride cement (MOC) in an alkaline environment were studied using a scanning electron microscope (SEM), an X-ray diffractometer (XRD), a Fourier transform infrared spectrometer (FT-IR) and a micro-electro-hydraulic servo pressure testing machine to investigate the effects of soaking time in 10 wt.% NaOH solution on the macro- and micro-morphology, phase composition and compressive strength of MOC samples. The results show that the deterioration of MOC samples under an alkaline environment is mainly caused by the alkaline environment providing more OH- ions, which can react with 5Mg(OH)2·MgCl2·8H2O (P 5) in the sample. The resulting reaction gives rise to a faster decomposition of 5Mg(OH)2·MgCl2·8H2O (P 5) and a substantial reduction in the strength of the sample, and finally leads to a gradual deterioration of MOC samples. Meanwhile, immersion time exhibits a significant effect on MOC samples. The extension of immersion time coincides with more OH- ions entering the sample, and the greater presence of OH ions increases the likelihood that more P 5 will produce a hydrolysis reaction, further resulting in the increased deterioration of the sample. After soaking for 6 h in alkaline media, the main phase composition of the surface layer of an MOC sample changes to MgO and Mg(OH)2, and its microscopic morphology is also dominated by round sheets, giving rise to a sharp decrease in its compressive strength (52.2%). When the immersion time is prolonged to 72 h, OH- ions have already immersed into the inner core of the sample, causing the disappearance of P 5 from the whole sample. At the same time, both the surface and inner core of the sample exhibit a disc-shaped morphology, and chalking phenomena also appear on the surface of the sample. This reduces the compressive strength of the sample to 13.5 MPa, only 20% of its compressive strength in water. The compressive strength of the sample after 120 h of immersion is as low as 8.6 MPa, which is lower than that of the sample dipped in water for 21 days (9.5 MPa). As a result, the MOC samples studied in alkaline environments exhibit a faster deterioration rate, mainly because of a faster hydrolysis reaction by P 5, caused by more OH- ions.

Effect of nano-silica@ chitosan phosphate ester on the mechanical properties and water resistance of magnesium oxychloride cement

Effects of fly ash, phosphoric acid, and nano-silica on the properties of magnesium oxychloride cement

Mechanical Properties, Microstructure, and Mechanism of Nanosilica-Modified Low-Carbon Magnesium Silicate Hydrate Cement

Effect of Phosphoric Acid and Soluble Phosphate on the Properties of Magnesium Oxychloride Cement

Study on Bonding Performance of Magnesium Phosphate Cement Mortar in Chloride Corrosion Environment

Effects of inert silica powder on the properties of magnesium oxysulfate cement

INVESTIGATING THE EFFECT OF NANO SILICA ON THE MECHANICAL PROPERTIES OF HARDENED CEMENT PASTE

Assessment of the mechanical properties and water stability of nano-Al2O3 modified high ductility magnesium potassium phosphate cement-based composites

Effect and mechanism of colloidal silica sol on properties and microstructure of the hardened cement-based materials as compared to nano-silica powder with agglomerates in micron-scale

Effects of Bauxite Tailings and Sodium Silicate on Mechanical Properties and Hydration Mechanism of Magnesium Phosphate Cement

Effect of Nano-SiO2 on the Mechanical Properties, Microstructure, and Hydration Process of Cementitious Materials Incorporating Hydrophobic Admixture

Properties and hydration mechanism of foamed magnesium oxysulfate cement under acid modification

Hydration properties of magnesium phosphate cement paste mixed with metakaolin and silica fume

Study on the reinforcing mechanisms of nano silica to cement-based materials with theoretical calculation and experimental evidence

Improved Hydration Resistance of Synthesized Magnesia-Calcia Clinker by Surface Modification

Evaluation of the Hydration Characteristics and Anti-Washout Resistance of Non-Dispersible Underwater Concrete with Nano-SiO2 and MgO

Study on the Deterioration Mechanism of Magnesium Oxychloride Cement under an Alkaline Environment

Effect of colloidal nanosilica as an admixture on chloride ion diffusion of Portland cement–fly ash mortars

Synthesis of Nano-Sio2@ptpeg-vpa Copolymer and Its Effects on Early-Age Cement Hydration

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Effect of Metakaolin on the Water Resistance of Magnesium Phosphate Cement Mortar