Abstract:PTFE adheres poorly to other materials due to its low surface energy and chemical inertness,which leads to failure of PTFE in many industrial applications.To spread the applications,numerous methods for surface modification have been developed to activate the PTFE surface for improving its wettability and adhesion ability.This study focused on the surface modification of expanded poly(tetrafluoroethylene)(ePTFE)film by a two-step process based on low-pressure plasma treatment followed by acrylic acid(AAc)graft copolymerization.The influences of different plasma treatments and graft copolymerization conditions on the hydrophilicity of film surface were studied.The wettability of the ePTFE film surface was determined by water contact angle,and the surface elemental compositions and the type of functional groups on the surface of the treated ePTFE samples were evaluated by X-ray photoelectron spectroscopy(XPS).The results indicated that the contact angle of ePTFE film declined from 145° to 102° when it was only treated by plasma treatment.After AAc grafted copolymerization,the contact angle decreased further to a smaller value.And the wettability of the film was improved obviously and kept constant.The condition of plasma treatment was He,100 W,90 s.The condition of AAc graft copolymerization was 30%(vol.),70℃,3 h.XPS analysis showed that the element ratio of F/C declined from 1.960 to 0.853,while the element ratio of O/C rose from 0 to 0.147.The result indicated that plasma treatment could greatly change the surface chemistry as well as morphology of ePTFE films.The surface roughness increased with plasma treatment time.From XPS measurements,it could be seen that the polar hydrophilic groups had been successfully grafted onto the ePTFE surface.The inert fluorine elements were partly replaced by oxygen polar groups,which was the fundamental reason for the improvement of hydrophilicity of ePTFE film.

Graft Polymerization of Acrylic Acid on A Polytetrafluoroethylene Panel by an Inductively Coupled Plasma

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

Ar Plasma-induced Graft Polymerization of Acrylic Acid Onto PTFE Films

Improving the Hydrophilicity of Poly(vinylidene Fluoride) Porous Membranes by Electron Beam Initiated Surface Grafting of AA/SSS Binary Monomers

Surface Modification Of Poly (Tetrafluoroethylene) Function Materials By Plasma-Induced Graft Copolymerization Of Acrylic Acid

Controlled Grafting of Comb Copolymer Brushes on Poly(tetrafluoroethylene) Films by Surface-Initiated Living Radical Polymerizations.

The Modification of PTFE Films Grafted Acrylic Acid with Ar Plasma

Surface Modification of Poly(tetrafluoroethylene) Microporous Membranes by Acrylic Acid Liquid-Phase Graft Copolymerization

Surface Modification of Plasma-Pretreated Poly(Tetrafluoroethylene) Films by Graft-Copolymerization

Plasma-Induced Direct-Grafting on Polytetrafluoroethylene Films by Quasi-Glow Discharge at Atmospheric Pressure

Studies on Surface Graft Polymerization of Acrylic Acid Onto PTFE Film by Remote Argon Plasma Initiation

Surface Modification And Functionalization Of Polytetrafluoroethylene Films Via Graft Copolymerization

Plasma-induced Graft Polmerization of Acrylic Acid Onto PTFE Films for Immobilized Enzyme

Surface modification of low temperature plasma-pretreated ePTFE film by AAc graft copolymerization

Surface Modification And Functionalization Of Polytetrafluoroethylene Films

Kinetics Study On Remote Argon Plasma-Induced Graft Polymerization Of Acrylic Acid Onto Ptfe Films

Surface Modification of Polymer Films by Graft Copolymerization for Adhesive-Free Adhesion

Surface Modification of Polytetrafluoroethylene Films Via Graft Copolymerization for Auto-Adhesion

Study On Surface Modification Of Polytetrafluoroethylene Film By Ar Remote-Plasma

Surface Structures and Adhesion Enhancement of Poly(Tetrafluoroethylene) Films after Modification by Graft Copolymerization with Glycidyl Methacrylate

Surface Modification of Poly(Tetrafluoroethylene) Films by Graft Copolymerization for Adhesion Improvement with Sputtered In-Sn Oxides