Abstract:NiO/Al2O3 catalysts with different NiO loadings were prepared by impregnation method. The monolayer dispersion capacity of NiO is determined to be about 9 wt.% through XRD quantitative phase analysis. Positron lifetime spectra measured for NiO/Al2O3 catalysts comprise two long and two short lifetime components, where the long lifetimes τ3 and τ4 correspond to ortho-positronium (o-Ps) annihilation in microvoids and large pores, respectively. With increasing loading of NiO from 0 to 9 wt.%, τ4 drops drastically from 88 to 38 ns. However, when the NiO loading is higher than 9 wt.%, τ4 shows a slower decrease. Variation of λ4 (1/τ4) as a function of the NiO content can be well fitted by two straight lines with different slopes. The relative intensity of τ4 also shows a fast decrease followed by a slow decrease for the NiO content lower and higher than 9 wt.%, respectively. The coincidence Doppler broadening measurements reveal a continuous increase of S parameter with increasing NiO loading up to 9 wt.% and then a decrease afterwards. This is due to the variation in intensity of the narrow component contributed by the annihilation of para-positronium (p-Ps). Our results show that the annihilation behavior of positronium is very sensitive to the dispersion state of NiO on the surface of γ-Al2O3. When the NiO loading is lower than monolayer dispersion capacity, spin conversion of positronium induced by NiO is the dominant effect, which causes decrease of the longest lifetime and its intensity but increase of the narrow component intensity. After the NiO loading is higher than monolayer dispersion capacity, the spin conversion effect becomes weaker and inhibition of positronium formation by NiO is strengthened, which results in decrease of both the long lifetime intensity and the narrow component intensity. The reaction rate constant is determined to be (1.50 ± 0.04) × 1010 g mol−1s−1 and (3.43 ± 0.20) × 109 g mol−1 s−1 for NiO content below and above monolayer dispersion capacity, respectively.

Chemical Quenching and Inhibition of Positronium in Cr2O3/Al2O3 Catalysts

Chemical Quenching of Positronium in CuO/Al2O3Catalysts

Chemical Quenching of Positronium in CuO/Al2O3 Catalysts

Chemical quenching of positronium in Fe2O3/Al2O3 catalysts

Spin Conversion of Positronium in Nio/Al2o3 Catalysts Observed by Coincidence Doppler Broadening Technique

Reaction Between NiO and Al2O3 in NiO/γ-Al2O3 Catalysts Probed by Positronium Atom

Positron Annihilation Study of Mo Dispersion in Moo3/Al2o3 Catalysts

Three-gamma Annihilation of Ortho-Positronium in NiO/γ-Al2O3 Catalysts Detected by Positron Lifetime and Coincidence Doppler Broadening Measurements

Monolayer dispersion of CoO on Al2O3 probed by positronium atom

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

Observation on the Interface of Α-Al2o3/cr2o3: Prepared by Oxidation of Al45Cr7

Monolayer Dispersion of NiO in NiO/Al2O3 Catalysts Probed by Positronium Atom

Ambient-temperature NO Oxidation over Amorphous CrOx-ZrO2 Mixed Oxide Catalysts: Significant Promoting Effect of ZrO2

Kinetics study of positronium o-Ps on MoNi/Al2O3 hydrotreating catalyst by PASCA

Studies of the Dispersion State of CrOx on ZrO2 and NO-CO Reaction on CrOx/ZrO2 Catalyst

Accelerating Catalytic Oxyanion Reduction with Inert Metal Hydroxides

STUDIES ON THE PROMOTER EFFECT OF ZRO2 IN PD/AL2O3 CATALYSTS

Positron annihilation spectroscopic investigation of pillared clay-based catalytic hybrid nanocomposites

Evaluating the catalytic performances of supported transition metal catalysts by positron annihilation lifetime spectroscopy

Effect of ZrO2 on CuO/gamma-Al2O3 catalyst in carbon monoxide oxidation

Tuning Adsorption and Catalytic Properties of Α-Cr2o3 and ZnO in Propane Dehydrogenation by Creating Oxygen Vacancy and Doping Single Pt Atom: A Comparative First-Principles Study