Abstract:Thermoelectric properties of substitutional compounds ( Zn0.98M0.02) Sb-4(3) ( M = Al, Ga and In) were investigated at temperatures from 5 to 310 K. The results indicate that substitution of M for Zn in Zn4Sb3 leads to a decrease in electrical resistivity rho, thermopower S and thermal conductivity lambda. The decrease in rho and S of ( Zn0.98M0.02) 4Sb3 would originate from increased electron contribution caused by introduction of donor levels due to substitution of M3+ for Zn2+. Nevertheless, our experiments revealed that as the dopant changed from Al to Ga and then to In, the resistivity of (Zn0.98M0.02) Sb-4(3) increased monotonically, which could be caused by reduced mobility due to the increase in the ionic radius from Al to In. Meanwhile, lambda of ( Zn0.98M0.02) 4Sb3 at low temperatures ( especially at T< similar to 50 K) decreased continuously as the dopant changed from Al to In, which could be ascribed to the enhancement of phonon scattering by dopants with greater atomic weight. In addition, it was found that the anomalies appearing in the plots of rho-T and S-T for Zn4Sb3 disappeared by doping of either Ga or In, implying that the beta to alpha/alpha' phase transition of Zn4Sb3 was completely prohibited. In particular, the thermoelectric figure of merit of beta-( Zn0.98Al0.02) Sb-4(3) is found to be larger than that of beta-Zn4Sb3 at T > 250K due to the large reduction in its resistivity, indicating that the thermoelectric properties of beta-Zn4Sb3 can be enhanced by Al doping.

Resistivity, Thermopower, and Thermal Conductivity of Nickel Doped Compounds Cr1−xNixSb2 at Low Temperatures

The Electrical and Thermal Conductivity and Thermopower of Nickel Doped Compounds (nixti1−x)1+ys2at Low Temperatures

Enhanced power factor and suppressed lattice thermal conductivity of CoSb3 Skutterudite by Ni substitution and nanostructuring for high thermoelectric performance

Enhanced thermoelectric performance of Cu12Sb4S13-delta tetrahedrite via nickel doping

Enhanced Thermoelectric Properties of Co 1− X − Y Ni X + Y Sb 3− X Sn X Materials

Crystal growth, characterization and physical properties of PrNiSb3, NdNiSb3 and SmNiSb3

Enhanced thermoelectric performance of Cu12Sb4S13___etrahedrite via nickel doping

Effect of Ni Doping on the Thermoelectric Properties of YbCo2Zn20

Enhanced thermoelectric performance of Cu 12 Sb 4 S 13− δ tetrahedrite via nickel doping

Effects of Silicon Addition on Thermoelectric Properties of Bulk Zn4Sb3 at Low-Temperatures

Effects of Substitution of Zn for Ni in NiMnSb Alloys

The Transport and Thermoelectric Properties of Cd Doped Compounds (Cdxti1−x)1+ys2

Effect of Antimony Doping on Thermoelectric Properties of Zr0.5Ti0.5Sn Multi-Element Alloys

Improved thermoelectric properties of doped A0.5B0.5NiSn (A, B = Ti, Zr, Hf) with a special quasirandom structure

Improved Thermoelectric Performance in the Zintl Phase Compounds YbZn2−xMnxSb2 Via Isoelectronic Substitution in the Anionic Framework

Thermoelectric Properties Of (Zn0.98m0.02) Sb-4(3) (M=Al, Ga And In) At Low Temperatures

Low-Temperature Electrical Conductivity in Mn-Doped Bi0.9Sb0.1 Solid Solutions

Impact of Cr content on the thermoelectric properties of the Cr/Sb co-doped Mg2.2−xCrx(Si0.3Sn0.7)0.98Sb0.02 compound

Synthesis and characterization of nanocrystalline NiSb and NiSb2 at low temperature

Enhanced Thermoelectric Properties of Neodymium Intercalated Compounds NdxTiS2

Enhanced Thermoelectric Properties of BiCoO 3 by Nickel Substitution