Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation and Photocatalysis Property of Yttrium-Doped Ordered Macroporous TiO2 Balls

Preparation and Photocatalysis Property of N-doped Ordered Porous TiO2 Balls by Microwave Treatment

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Yellow–colored Mesoporous Pure Titania and Its High Stability in Visible Light Photocatalysis

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Study on Y-doped TiO2 Nanoparicles and Their Photocatalytic Properties

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation of Ordered Macroporous Y_2O_3 Balls by Sol-Gel Templating Method

Preparation and Characterization of Low-Amount Yb 3+ -Doped TiO 2 Photocatalyst

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Preparation and Visible Light Photocatalytic Activity of TiO;/C Composite Millimetre Balls

Preparation and Photocatalytic Activities of Low Amount Yb3+-Doped Tio2 Composite Nano-Powders

Preparation and Property of S-doped Ordered Porous TiO2 by Microwave Treatment

Preparation,Characterization and Photocatalytic Activity of Three-dimensionally Ordered Mesoporous/Macroporous TiO2 Microspheres

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Preparation and photocatalytic activity of mesoporous TiO2 derived from hydrolysis condensation with TX-100 as template

Preparation of Tm2Ti2O7 by Sol-Gel Method and Its Photocatalytic Activity

Study on photodegradation of methyl orange using co-doped TiO2 with Y3+ and N

Ordered Macroporous Bi2o3/Tio2 Film Coated on A Rotating Disk with Enhanced Photocatalytic Activity under Visible Irradiation

Effects of Yb 3+ -Doping on Phase Transformation and Photocatalytic Activities of TiO 2 Nano-Powders