Influence of Different Synthesis Methods on Structure, Morphology and Photocatalytic Properties of BiOCl Photocatalytic Materials

Li Jing,Xia Zhiguo,Wang Le,Chen Xichao,Yang Huanhuan

2011-01-01

Abstract:The pure tetragonal phase photocatalytic materials BiOCl and Nd 3+-doped BiOCl were prepared by solvothermal synthesis, solid-phase synthesis and sol-gel synthesis method, respectively. The as-prepared products by different synthesis methods were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and ultraviolet-visible (UV-Vis) absorption spectroscopy, respectively. The photocatalytic performance of the as-prepared products was evaluated via the UV degradation experiment of the given methyl orange solution. The results indicated that the BiOCl particles by solvothermal method were composed of numerous BiOCl nanoplates with the dimension of less than 1μm. The crystalline of BiOCl particles prepared by solid state synthesis was higher than that prepared by sol-gel method, and their plate sizes were about 6μm and 3~4μm, respectively. Further, their UV-vis absorption boundaries were 335, 430 and 430 nm for the three synthesis methods, respectively. The phase structures and photocatalyst properties of Nd 3+-doped BiOCl materials were also investigated. The red-shift of the absorption profile was clearly observed for the three kinds of products by different synthesis methods, and the obtained sample by sol-gel method had the best absorption property, which also led to the optimum photocatalys performance from the degradation experiment.