Effect of aging on microstructure and tensile properties of Ti-6Cr-5Mo-5V-4Al Alloy

Chenglin Li,Songxiao Hui,Wenjun Ye,WeiQi Wang,Yulan Yang,Pinghui Zhang

DOI: https://doi.org/10.3969/j.issn.0258-7076.2011.01.005

2011-01-01

Abstract:Effect of aging on microstructure and tensile properties of a new type Ti-6Cr-5Mo-5V-4Al Alloy was studied. The experimental results showed that the typical microstructure of Ti-6Cr-5Mo-5V-4Al alloy with α/β solution and aging treatment was broken β grains, continuous and discontinuous necklace-like primary α phase at the β grain boundary, discontinuous spherical primary α phase in the intragranular, and small crossing secondary α phase precipitated during the aging treatment. And the typical microstructure of Ti-6Cr-5Mo-5V-4Al alloy with β solution and aging treatment was equiaxed β grain and secondary α phase precipitated at the equiaxed β grain boundary with a certain orientation, and small crossing secondary α phase homogeneous distributed in the intragranular. Ti-6Cr-5Mo-5V-4Al alloy dissolved in the β area and aging treatment, would be helpful to reinforce alloys when aging at temperature higher than 500°C for a long time, or aging at lower than 500°C for a short time. When dissolved in the α/β area and aging treatment, it would be useful to reinforce alloy aged at temperature lower than 500°C for a short time; aging at temperature higher than 500°C or for a long time would reduce the strength of the alloy, and also, there was is a good strength and plastic match for the alloy in a quite wide range of aging temperature. Ti-6Cr-5Mo-5V-4Al alloy, when aged at temperature lower than 500°C, the strength and plastic matched with α/β solution and aging was much better than that with β solution and aging, and when aged at temperature higher than 500°C, the results might be inverse. In addition, the short time direct aging treatment could rapidly increase the strength of the alloys, meanwhile, maintaining excellent ductility, such as the alloy directly aged at 500°C/2h,strength reached to 1590 MPa, while the elongation maintained 6.5%.