Abstract:In the present study, we report the systematic investigation of the effect of chemical oxidation on the structure of single-walled carbon nanotubes (SWNTs) by using different oxidants. The oxidation procedure was characterized by using infrared spectroscopy and transmission electron microscopy (TEM). The SWNTs were produced by chemical vapor deposition (CVD) and oxidized with three kinds of oxidants: (1) nitric acid (2.6 M), (2) a mixture of concentrated sulfuric acid (98 wt %) and concentrated nitric acid (16 M) (v/v = 3/1) and (3) KMnO4. The results reveal that the different functional groups can be introduced when the SWNTs are treated with different oxidants. Refluxing in dilute nitric acid can be considered as a mild oxidation for SWNTs, introducing the carboxylic acid groups only at those initial defects that already exist. The abundance of the carboxylic acid groups generated with this oxidant remained constant along with the treating time. In contrast, sonication of SWNTs in H2SO4/HNO3 increased the incidence of carboxylic acid groups not only at initial defect sites but also at newly created defect sites along the walls of SWNTs. Compared to the two oxidants above, when KMnO4 in alkali was used as the oxidant, which is relatively mild, different amounts of −OH, −CO, and −COOH groups were introduced. The oxidation processes begin mainly with the oxidation of the initial defects that arise during the CVD growth of the SWNTs and are accompanied by processes that can be roughly divided into two steps: (1) the defect-generating step and (2) the defect-consuming step. Specifically, during the defect-generating step, the oxidants attack the graphene structure by electrophilic reactions and generate active sites such as −OH and −CO. This step depends on the oxidant's ability to generate −C−OH groups and to transform them into −CO groups. During the defect-consuming step, the graphene structure of the tube was destroyed by the oxidation of the generated active sites in step 1. The defect-consuming step mostly counts on the ability of the oxidant to etch/destroy the graphite-like structure around the already generated −CO and their neighborhood groups.

Diameter-Dependent Thermal-Oxidative Stability of Single-Walled Carbon Nanotubes Synthesized by A Floating Catalytic Chemical Vapor Deposition Method

Cvd Synthesis and Diameter Distribution of Single-Walled Carbon Nanotubes

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Tuning the Diameter of Single-Walled Carbon Nanotubes by Temperature-Mediated Chemical Vapor Deposition

Effect of Chemical Oxidation on the Structure of Single-Walled Carbon Nanotubes

Oxidation stability of confined linear carbon chains, carbon nanotubes, and graphene nanoribbons as 1D nanocarbons

Synthesis of Carbon Nanotubes by Decomposing Alcohol

Diameter Controlled Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes.

The influence of ethanol on the growth and structure of carbon nanotubes

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Boron Nitride Nanotubes Versus Carbon Nanotubes: A Thermal Stability and Oxidation Behavior Study

Stability of Carbon Nanotubes: How Small Can They Be?

Diameter Controlled CVD Synthesis of Single-Walled Carbon Nanotubes

The Effect of Oxidation on Physicochemical Properties and Aqueous Stabilization of Multiwalled Carbon Nanotubes:Comparison of Multiple Analysis Methods

Controlling the Diameters in Large-Scale Synthesis of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4

Effect of the reaction atmosphere on the diameter of single-walled carbon nanotubes produced by chemical vapor deposition

Controllable preparation and properties of single-/double-walled carbon nanotubes

Preparation of Short Single Walled Carbon Nanotubes by CVD Growth and by Chemical Oxidation

Growth of Single-Walled Carbon Nanotubes from Discrete Catalytic Nanoparticles of Various Sizes

Towards the preparation of single-walled carbon nanotubes with average diameter of 1.2 nm

Supramolecular Nanotubes with High Thermal Stability: a Rigidity Enhanced Structure Transformation Induced by Electron-Beam Irradiation and Heat