Magnetic Property of Nanocrystalline Nickel Prepared by Surface Mechanical Attrition Treatment

LI Wei,LIU Ping,MA Feng-cang,LIU Xin-kuan,CHEN Xiao-hong,RONG Yong-hua

DOI: https://doi.org/10.13251/j.issn.0254-6051.2011.03.002

2011-01-01

Abstract:A nanocrystalline surface layer was formed on Ni plate by surface mechanical attrition treatment(SMAT).The characterization of microstructure and composition indicates that Fe and Cr elements from stainless steel balls can diffuse and permeate into the Ni surface layer during SMAT.Fe and Cr can further diffuse and homogenize when annealing at high temperature,leading to the formation of new alloy with Ni,which results in the different magnetic property of Ni plate.The results show that the value of curie temperature(Tc) for nanocrystalline Ni surface layer induced by SMAT can exceed 600 ℃,much higher than that for the coarse-grained pure Ni(354.3 ℃),which indicates that SMAT is not only a process for surface nanocrystallization,but also an effective method for surface modification.