Low-voltage cathodoluminescence properties of green-emitting ZnAl2O4:Mn2+ nanophosphors for field emission display

Xiaojun Wang,Mingchang Zhang,Hui Ding,Huili Li,Zhuo Sun
DOI: https://doi.org/10.1016/j.jallcom.2011.03.076
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:A low-cost ZnAl2O4:Mn2+ green nanophosphor for field emission display (FED) was successfully synthesized by the coprecipitation method and a two-step firing, firstly calcining at 1200°C for 2h in air and then annealing at 900°C for 3h in flowing NH3 gas. The effects of the preparation process and the Mn2+ concentration on optical properties of ZnAl2O4:Mn2+ were investigated. The phase composition, particle morphology, photoluminescence (PL) spectra of the ZnAl2O4:Mn2+ phosphor as well as low-voltage field emission properties of the FED device prepared by using the synthesized ZnAl2O4:Mn2+ phosphor were examined. Similar to ZnGa2O4:Mn2+, Mn2+-doped ZnAl2O4 showed two green emission bands centered at 508 and 517nm, respectively, which originate from 4T1(4G)→6A1(6S) transitions of Mn2+ on Td and Oh sites. The PL intensity reached the maximum at 0.5 at.% Mn2+. Under the low-voltage excitation, the FED device exhibited bright green emission, high voltage brightness saturation, and high color purity.
What problem does this paper attempt to address?