Abstract:The microstructures, mechanical properties and tribological behaviors of the NiAl-based composite coatings with various addition of Nb were investigated. Particularly, the coatings registered a typically fine lamellar morphology and a dense microstructure, of which the microhardness increased with the Nb content increasing. Moreover, the coatings with various Nb contents registered different tribological properties and wear mechanisms at different test temperatures. The wear mechanisms of the coatings transferred from serious abrasive wear (NA1), brittle fracture accompanied with abrasive wear (NA2), abrasive wear (NA3) to serious fracture and abrasive wear (NA4) with the increment of Nb content at room temperature. At 400 degrees C, the coatings with low contents of Nb (NA1, NA2) possessed low friction coefficients but high wear rates due to the plastic deformation and micro-cutting. However, the coatings with high contents of Nb (NA3, NA4) possessed higher friction coefficients but low wear rates due to the reinforcement and anti-wear effect of metal Nb, and the wear mechanism was dominated by adhesive wear. At 800 degrees C, the coatings possessed the wear mechanism of slight abrasive wear, and a series of bimetallic oxides, e.g. AgNbO3 and NiNb2O6 generated through the high-temperature tribochemical reactions. The synergistic lubrication of oxides was responsible for the lower COFs of the coatings at 800 degrees C. But higher wear rate of the NA1 coating was ascribed to the low hardness and adhesive strength due to the low content of metal Nb. As a whole, metal Nb could observably enhance the wear resistance of the coatings at different temperatures.

Plasma Alloying of Tial with Niobium and Its Wear Resistance

Effect of Plasma Niobizing on Oxidation Resistance of Tial Intermetallics

Synthesis, Structure, and Properties of the High Nb–TiAl Alloy after Ni Coatings by Plasma Surface Alloying Technique

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

Tribological Properties of 2024 Aluminum Alloy Plasma-Based Ion Implanted with Nitrogen then Titanium

Oxidation Resistance of TiAl-Inconel625 Graded Alloying Layer

Microstructure, Mechanical, and Tribological Properties of Nb-Doped TiAl Alloys Fabricated via Laser Metal Deposition

Effects of Niobium on Phase Composition and Improving Mechanical Properties in TiAl Alloy Reinforced by Ti2AlC

Microstructure and Tribology Property of Plasma Nickelized Alloy Layer on Pure Titanium Surface

Microstructure, Oxidation Behavior and Adhesion of a CoNiCrAlTaY Coating Deposited on a High Nb–TiAl Alloy by Plasma Surface Metallizing Technique

Surface Modification of a Ti–Al–Zr Alloy by Niobium Ion Implantation

High-Temperature Oxidation Behavior of Plasma Surface Nb-Cr-(Si) Alloying System on γ-TiAl

Effects of Ni-5 wt% Al/Bi2O3 addition and heat treatment on mechanical and tribological properties of atmospheric plasma sprayed Al2O3 coating

Microstructure and Wear-Resistant Behaviors of Al2O3-TiO2 Reinforced Ni-based Composite Coating Plasma-Sprayed on 6061 Aluminum Alloy

High Temperature Gas Nitridation and Wear Resistance of TiAl Based Alloys

Tribological properties of Ti-N compound layer formed on Ti6Al4V by HCD assisted plasma nitriding

Microstructures, Mechanical Properties and Tribological Behaviors of NiAl-based Composite Coatings with Various Addition of Nb

Double-Glow Plasma Surface Alloying of BTi-62421S Alloys: Regulation of Microstructure Properties

Growth, mechanical properties, and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

Effect of aluminum addition on microstructure, mechanical properties and high temperature tribological properties of nickel-rich NiTi alloy