Pii: s1359-6462(00)00653-9
Bing-Yun Li,Li-Jian Rong,Yi-Yi Li
2001-01-01
Abstract:Porous Ni-Ti shape-memory alloys (SMAs) have promising applications in medical field (such as cranial-facial replacement and prosthesis, dental roots, and medical instruments) due to their good biocompatibility, unique shape-memory effect (SME) as well as superelasticity (SE), and good mechanical properties (1,2). It is well known that Ni-Ti SMAs show a crystalline transition from parent phase to martensite phase and vice versa when they are subjected to cooling or heating processes, respectively. It is reported that porous Ni-Ti SMAs also show the SME when they are mechanically deformed at low temperature, in the martensitic phase, and successively heated up to the parent phase; and they present SE if deformed in the parent phase within a definite temperature range (3,4). That is to say, SME and SE of Ni-Ti SMAs are associated with transformation temperatures, and therefore the transformation temperatures are very important for the medical and engineering applications of Ni-Ti SMAs. However, the transformation temperatures of Ni-Ti SMAs are very sensitive to composition. For example, a 0.1at.% nickel change in composition or presence of 0.1at.% oxygen can result in about a 10°C change in transformation temperatures (5,6). The transformation behavior of cast Ni-Ti SMAs has been studied extensively (5,7–11). Nevertheless, to the authors’ knowledge, there are very few reports about the transformation behavior of porous Ni-Ti SMAs. In the present study, the transformation behavior of porous Ni-Ti SMAs prepared by self-propagating high-temperature synthesis (SHS) is investigated in detail for the first time using electrical resistance versus temperature, differential scanning calorimetry (DSC) and thermal expansion.