Abstract:Given their wide range of biomedical applications, hydroxyapatite (HA) nanoparticles are an attractive material widely used in many fields. Therefore, a simple, inexpensive, and stable process for the synthesis of HA nanoparticles is necessary to meet current needs. Herein, we studied HA synthesis assisted by four surfactants, namely cation, anion, non-ionic, and zwitterion templates, to verify the synthesis phase, aspect ratio, morphology, and biocompatibility under different environments (i.e., pH 4 and 9) before and after calcination. Results showed that before calcination, the surfactant-free groups could not produce HA but showed an abundant dicalcium phosphate anhydrous (DCPA) phase at pH 4. Except for the anionic group containing a small amount of DCPA, all surfactant-assistant groups presented single-phase HA in acidic and alkaline environments. The diameter of HA synthesized at pH 4 was significantly larger than that of HA synthesized at pH 9, and the effect of aspect ratio changes after calcination was more significant than that before calcination. The uncalcined rod-shaped HA synthesized with a non-ionic template at pH 4 demonstrated excellent cell viability, whereas anionic, cationic, and non-ionic surfactants exhibited biocompatibility only after calcination. At pH 9, non-ionic and uncalcined zwitterion-assisted rod-shaped HA showed excellent biocompatibility. In conclusion, the uncalcined HA rod-shaped nanoparticles synthesized from the non-ionic template at pH 4 and 9 and the zwitterion template at pH 9, as well as all surfactant-assisted HA after calcination, had no cytotoxicity. These tailor-made non-toxic HA types can meet the different requirements of apatite composite materials in biomedical applications.

Synthesis Conditions of Nano-Hydroxyapatite Using Chondroitin Sulfate by Co-Precipitation Method

Template Induced Synthesis of Nano-Hydroxyapatite by Co-Precipitation Method

Influence of Templates on Morphology of Nano-Hydroxyapatite Synthesized by Co-Precipitation Method

Preparation and Characterization of Chitosan/nano-Hydroxyapatite Composite Used for Bone Repair by Co-Precipitation Method

Effect of Ph and Temperature on the Morphology and Phases of Co-Precipitated Hydroxyapatite

Kinetics and Template Nucleation of Self-Assembled Hydroxyapatite Nanocrystallites by Chondroitin Sulfate*

Preparation and characterization of nano-sized hydroxyapatite powder

Preparation and Characterization of Chitosan/nano-Hydroxyapatite Composite Used As Bone Substitute Materials

EFFECTIVE FACTORS OF PREPARATION FOR CARBONATED HYDROXYAPATITE BY THE AQUEOUS PRECIPITATION METHOD

Effect of Process Parameters on the Microstructure and Property of Hydroxyapatite Precursor Powders and Resultant Sintered Bodies

Preparation and crystallization control of nanoparticle hydroxyapatite

Preparation of Nano Hydroxyapatite by Coprecipitation

Hydrothermal Synthesis of Hydroxyapatite Fibers Precipitated by Propionmide

Morphologies of Hydroxyapatite Nanoparticles Adjusted by Organic Additives in Hydrothermal Synthesis

Effect of pH on the In Vitro Biocompatibility of Surfactant-Assisted Synthesis and Hydrothermal Precipitation of Rod-Shaped Nano-Hydroxyapatite

Synthesis and application of nanometer hydroxyapatite in biomedicine

Reverse Microemulsion-Directed Synthesis of Hydroxyapatite Nanoparticles under Hydrothermal Conditions

Controllable Synthesis of Spherical Hydroxyapatite Nanoparticles Using Inverse Microemulsion Method

Influence of Citric Acid on Synthesis of Powdered Hydroxyapatite with Ca(NO_3)_2-P_2O_5 System

Nano-hydroxyapatite Formation Via Co-Precipitation with Chitosan-G-poly( N -Isopropylacrylamide) in Coil and Globule States for Tissue Engineering Application

Preparation of in situ-deposited hydroxyapatite on chitosan scaffold