Efficient quantum dot sensitized solar cells via improved loading amount management
Wei Wang,Yiling Xie,Fangfang He,Yuan Wang,Weinan Xue,Yan Li
DOI: https://doi.org/10.1016/j.gee.2021.04.002
2021-04-01
Abstract:A relative thin photoanode prepared by the cationic surfactant-assisted multiple deposition procedure has achieved a high QD loading which is comparable to that of the thick photoanode commonly used.Under AM 1.5G illumination, Zn−Cu−In−Se and Zn−Cu−In−S based QDSCs with optimized 11.8 μm photoanodes show the PCE of 10.03% and 8.53%, respectively, which are comparable to the corresponding highest PCE of Zn−Cu−In−Se and Zn−Cu−In−S QDSCs (9.74% and 8.75%) with over 25.0 μm photoanodes.An impressive PCE of 6.14% was obtained for the CdSe based QDSCs with a 4.1 μm photoanode, which is slightly lower than the best PCE (7.05%) of reference CdSe QDSCs with 18.1 μm photoanode.The results implied that the manufacturing cost of QDSCs could be reduced.High light-harvesting efficiency and low interfacial charge transfer loss are essential for the fabrication of high-efficiency quantum dot-based solar cells (QDSCs). Increasing the thickness of mesoporous TiO<sub>2</sub> films can improve the loading of pre-synthesized QDs on the film and enhance the absorbance of photoanode, but commonly accompanied by the increase in the unfavorable charge recombination due to prolonged electron transmission paths. Herein, we systematically studied the influence of the balance between QD loading and TiO<sub>2</sub> film thickness on the performance of QDSCs. It is found that the relative thin photoanode prepared by the cationic surfactant-assisted multiple deposition procedure has achieved a high QD loading which is comparable to that of the thick photoanode commonly used. Under AM 1.5G illumination, Zn−Cu−In−Se and Zn−Cu−In−S based QDSCs with optimized 11.8 μm photoanodes show the PCE of 10.03% and 8.53%, respectively, which are comparable to the corresponding highest PCE of Zn−Cu−In−Se and Zn−Cu−In−S QDSCs (9.74% and 8.75%) with over 25.0 μm photoanodes. Similarly, an impressive PCE of 6.14% was obtained for the CdSe based QDSCs with a 4.1 μm photoanode, which is slightly lower than the best PCE (7.05%) of reference CdSe QDSCs with 18.1 μm photoanode.By controlling the times of HTAC assisted depositions, the performance of an optimized QD/nH/QD photoanode with a thin photoanode is close to or slightly lower than that of the thick reference one<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2468025721000649-ga1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (298KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S2468025721000649-ga1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>
energy & fuels,engineering, chemical,green & sustainable science & technology,chemistry, physical