Self-Assembled Perovskite Epitaxial Multiferroic BiFeO3 Nanoislands

Qiming Hang,Xinhua Zhu,Zhenjie Tang,Ye Song,Zhiguo Liu

DOI: https://doi.org/10.4028/www.scientific.net/amr.197-198.1325

2011-01-01

Abstract:Perovskite epitaxial multiferroic BiFeO 3 nanoislands were grown on SrTiO 3 (100) and Nb-doped SrTiO 3 (100) single crystal substrates by chemical self-assembled method. Their phase structure and morphology were characterized by X-ray diffraction, scanning electron microscopy, and atomic force microscopy, respectively. The results showed that epitaxial multiferroic BiFeO 3 nanoislands were obtained via post-annealing process in the temperature range of 650 - 800°C, and their lateral sizes were in the range of 50 - 160 nm and height of 6 -12 nm. With increasing the post-annealing temperature, the morphology of BiFeO 3 nanoisland in the (100) growth plane evolved from tri-angled to squared, and then to plated shapes. By using piezo-force microscopy, ferroelectric characteristics of a single epitaxial BiFeO 3 nanoisland (with lateral size of ~ 50 nm and height of 12 nm) grown on Nb-doped SrTiO 3 (100) single crystal substrate, was characterized. The results demonstrated that fractal ferroelectric domains existed in the single BiFeO 3 nanoisland, and self-biased polarization was also observed within this multiferroic nanoisland. This phenomenon can be ascribed to the interfacial stress caused by the lattice misfit between the BiFeO 3 nanoisland and the SrTiO 3 single crystal substrate.