Abstract:The evolution in microstructure and composition of the milled Ti-Al composite powder with different milling time were investigated. It shows that with the milling time increasing, the initial powder underwent a successive change in its morphology from a flattened shape (2 h) to a fine, equiaxed and uniform one (above 6 h). The milled Ti-Al composite powder was nanocrystalline with the average crystallite size of about 17 nm after milling for 8 h. The evolution mechanism of Ti-Al composite powder was elucidated. The Ti(Al) solid solution is formed through a gradual and progressive solution of Al into Ti lattice. By differential thermal analysis on the ignition temperature of the reaction between Ti and Al as a function of milling time, it indicates that mechanical milling of the powders significantly lowered the ignition temperature of the reaction by refining its Ti-Al composite structure.

Structure and Morphology of Ti-Al Composite Powders Treated by Mechanical Alloying