Abstract:There has been a great interest in the synthesis and characterization of Ti 3AlC 2 and Ti 3SiC 2 lamellar ceramics due to their striking combination of merits of both metals and ceramics, such as good high-temperature strength, excellent oxidation resistance. In this study, dense and high purity polycrystalline Ti 3AlC 2 and Ti 3SiC 2 lamellar ceramics were prepared from Ti, Al (Si) and C powders by reactive hot pressing in vacuum at 1450 for 1.5 h under 30 MPa. Their phase constitution, mechanical characterization and thermal properties were investigated. In addition, plasma-sprayed monolayer ZrO 2 thermal barrier coatings free of metallic transition layer were prepared on the two ceramic substrates. The purity of the Ti 3AlC 2 and Ti 3SiC 2 were 91.5% and 90.3%, and the main impurity was TiC. The flexural strength and fracture toughness were 536 MPa, 7.8 MPa · m 1/2 and 457 MPa, 6.8 MPa · m 1/2 for Ti 3AlC 2 and Ti 3SiC 2, respectively. They took a respective average value of 8.77 × 10 -6 and 9.14 × 10 -6/°C for the coefficient of thermal expansion (CTE) without remarkable temperature dependence between 25 and 1000. Furthermore, the coatings contributed to a more than 60% decrease in the high temperature thermal conductivity compared to the two matrices. In general, Ti 3AlC 2 and ZrO 2-coated Ti 3AlC 2 displayed superior comprehensive properties to Ti 3SiC 2 and ZrO 2-coated Ti 3SiC 2. The temperature differences between the outside surface and the coating/matrix interfaces created by the thermal barrier coating were calculated to be 341 and 358 for Ti 3AlC 2 and Ti 3SiC 2 substrate, respectively. © Copyright.

Properties of Ti 3XC 2 (X=Al, Si) with plasma sprayed ZrO 2 thermal barrier coating