Energy transfer processes in Ce3+ and Tb3+ co-doped Ln2Si2O7 (Ln = Y, Gd)
Yong Li,Xiantao Wei,Min YIN,Ye Tao
DOI: https://doi.org/10.1016/j.optmat.2011.02.017
IF: 3.754
2011-01-01
Optical Materials
Abstract:Research highlights ► The Ce 3+ and Tb 3+ co-doped Ln 2 Si 2 O 7 (Ln = Y, Gd) samples were prepared by sol-gel method. ► Energy transfer only conducts from Ce 3+ to Tb 3+ in Y 2 Si 2 O 7 host. ► Energy can transfer mutually between Ce 3+ and Tb 3+ in Gd 2 Si 2 O 7 host. ► The Tb 3+ excitation energy could be transferred to Ce 3+ ion via Gd 3+ ion as a bridge in Gd 2 Si 2 O 7 host. ► The Gd 2 Si 2 O 7 host can convert more VUV and UV radiation into visible light than Y 2 Si 2 O 7 host. Abstract The Ce 3+ and Tb 3+ co-doped Ln 2 Si 2 O 7 (Ln = Y, Gd) samples were prepared by sol–gel method. Structure characterization of the phosphor was carried out by X-ray diffraction. The luminescence properties of samples were analyzed by measuring the excitation and emission spectra. It was observed that excitation energy can transfer mutually between Ce 3+ and Tb 3+ in GPS: Ce 3+ , Tb 3+ samples, while in Y 2 Si 2 O 7 :Ce 3+ , Tb 3+ samples the energy transfer only progresses from Ce 3+ to Tb 3+ . Based on the energy level diagrams of respective Ce 3+ , Tb 3+ and Gd 3+ ion, the detailed pathways for energy transfer are explained. Keywords Energy transfer Luminescence Silicate Rare earth 1 Introduction Rare earth silicates have attracted much attention due to their excellent properties. Cerium doped orthosilicates Re 2 SiO 5 :Ce 3+ (Re = Lu, Y, Gd) have been developed due to their ideal qualities for ionizing radiation detection, such as their high density, relative high light yield and short decay time [1–3] . Recently, Ce-doped pyrosilicate Re 2 Si 2 O 7 :Ce 3+ (Re = Lu, Y, Gd), which is another kind of host material in Re 2 O 3 –SiO 2 binary system (Re 2 O 3 :SiO 2 = 1:2), shows much better scintillation performance than orthosilicates Re 2 SiO 5 :Ce 3+ [4–6] . These materials demonstrate much lower afterglow level and absence of luminescence quenching in the wide temperature range [4] . On the other hand, rare earth silicates are also good physical system for studying energy transfer from Ce 3+ to Tb 3+ . The luminescence properties and energy transfer mechanisms between Ce 3+ and Tb 3+ are reported in rare earth silicates powders samples [2,7–9] . It is well known that Ce 3+ ion can be used as a sensitizer for Tb 3+ ion. The energy transfer from Ce 3+ to Tb 3+ ion is usually very effective which results in bright luminescence of Tb 3+ . Actually, some Ce 3+ –Tb 3+ codoped materials have been applied as blue and green-light emitting phosphors [10] . At the same time, there are some other reports regarding the energy transfer from Tb 3+ to Ce 3+ in yttrium aluminum garnet [11,12] , which has been attributed to the cross relaxation between Ce 3+ and Tb 3+ ion [12] . Energy transfer from Ce 3+ to Tb 3+ or Tb 3+ to Ce 3+ also depends on the nature and crystal structure of host. In recent decades, with the developing of mercury-free phosphorescent lamp and plasma display panel, luminescent materials of rare-earths in the vacuum ultraviolet region has received much attention. Such phosphors would have the ability to absorb vacuum ultraviolet energy and efficiently transfer the energy to the luminescent ions. Rare earth silicates have good thermal, chemical stability and are a good host for luminescent materials under vacuum ultraviolet (VUV) and ultraviolet (UV) excitation [7,8,13] . In the present work, luminescence properties of Ln 2 Si 2 O 7 :Ce 3+ , Tb 3+ (Ln = Y, Gd) samples obtained by sol–gel method were studied. The research primarily focused on energy transfer mechanisms between Tb 3+ and Ce 3+ ions, and the efficiency of energy transfer was discussed. 2 Experimental The Ce 3+ and Tb 3+ co-doped Ln 2 Si 2 O 7 (Ln = Y, Gd) samples were prepared by sol–gel method. The purity of raw materials Gd 2 O 3 , Y 2 O 3 , CeO 2 , and Tb 4 O 7 was 99.99%. The Si(OC 2 H 5 ) 4 was analytical pure. The oxides were dissolved in dilute nitric acid separately, and corresponding nitrate solutions were obtained. After mixing the required amount of the above solutions, certain citric acid (the molar ratio of citric acid to total metal cation was 2:1) were added to the mixed nitrate solution. The Si(OC 2 H 5 ) 4 was dissolved in alcohol, and then mixed with the obtained solution. Ammonia or nitric acid was used to keep the pH value of the resulting solution at about 2.0. The mixture was stirred to achieve a uniform mixing and form a sol. The sol turned into gel after the process of water bath at 70 °C. The dried gel was preheated to get rid of alcohol, water and citric acid at 450 °C for 2 h, then was ground into fine powder and heated in a high temperature tube furnace at different temperature for 2 h, respectively. The prepared samples appeared to be white color in body. X-ray diffraction (XRD) patterns were obtained on a rotating anode X-ray diffractometer (MAC Science Co. Ltd. MXP18AHF) under Cu Kα radiation. The VUV–UV excitation spectra and emission spectra were measured at the VUV spectroscopy station of Beijing Synchrotron Radiation Facility, Institute of High Energy Physics, Chinese Academy of Sciences. The electron energy of the storage ring is 2.5 GeV and the beam current is approximately from 160 to 60 mA in measurement. An ARC-VM-502-S monochromator (1200 g/mm) was used for the excitation spectra; an ARC SP-308 monochromator (1200 g/mm) was used for the emission spectra and the signal was detected by a Hamamatsu H7421–50 photomultiplier. The integration time of 1 s and wavelength step of 1 nm were applied for all the spectrum measurements. The excitation spectra were corrected with the photo flux of the excitation beam using the excitation spectrum of sodium salicylate as standard in the same excitation conditions. All the spectra were recorded at room temperature. 3 Results and discussion The structure and phase purity of the products were examined by X-ray diffraction analysis. Fig. 1 a shows the XRD patterns of the Y 2 Si 2 O 7 (YPS) powders annealed at various temperatures. For the sample prepared at 900 °C, an obvious broad weak peak is observed, indicating that the samples begin to crystallize. At 1000 °C, the characteristic peaks of YPS phase appear which are well consistent with the standard XRD pattern of α-YPS (JCPDS 21-1457). The XRD patterns of Gd 2 Si 2 O 7 (GPS) present same characteristic with that of YPS , as shown at Fig. 1 b. It can be seen that the powders remain amorphous up to 900 °C. At 1000 °C, the diffraction peaks appear, this pattern is similar to that of α-YPS phase, indicating that it has same structure with YPS samples prepared at 1000 °C, above 1100 °C, continued refinement of peak shapes and enhancement of intensity are observed, indicating the growth of crystallite with the increase of synthesis temperature. The excitation spectrum and emission spectrum of YPS: Ce 3+ 1% and GPS: Ce 3+ 1% are shown in Fig. 2 . The excitation spectrum monitored 404 nm emission contains five broad bands. The band at higher energy is attributed to host absorption. The other four broad bands from 200 nm to 350 nm are characteristic of transitions from 4f 1 ground state to four lower crystal field splitting levels of the 5d states of Ce 3+ ions. Compared excitation spectrum of GPS: Ce 3+ 1% with that of YPS: Ce 3+ 1%, it can be found that Ce 3+ in both hosts with same crystal structure shows the similar splitting behavior. Beside the bands originating from Ce 3+ ion described above, the peaks at about 273 nm in the excitation spectrum, which is superimposed over broad Ce 3+ excitation bands, correspond to the 8 S 7/2 → 6 I J transitions of Gd 3+ in the GPS matrix, which suggests the energy transfer from Gd 3+ to Ce 3+ ion. The emission of Ce 3+ in the two hosts consist of a broad band with a maximum at 404 nm , which can be assigned to the parity allowed transitions of lowest component of 5d states to the spin–orbit components of the ground state 2 F 5/2 , 2 F 7/2 of Ce 3+ , respectively. Fig. 3 shows the excitation and emission spectra of YPS: Tb 3+ 0.5% and GPS: Tb 3+ 0.5% powders. The characteristic luminescence observed in the emission spectra corresponds with the 5 D 3 → 7 F J and 5 D 4 → 7 F J line emissions of the Tb 3+ ions, and the strongest emission at 543 nm originates from the 5 D 4 → 7 F 5 transition. The excitation spectrum monitored 543 nm in two different hosts both contains two broad bands. The band at higher energy is also attributed to host absorption in the two different hosts. Another band centered 228 nm can be ascribed to the transitions of Tb 3+ from the lower level of 4f 8 configuration to the energy levels of 4f 7 5d configuration. Beside the bands described above, the peaks at about 273 nm and 313 nm in the excitation spectrum correspond to the 8 S 7/2 → 6 I J and 8 S 7/2 → 6 P J transitions of Gd 3+ in the GPS matrix, which suggests that there is energy transfer from Gd 3+ to Tb 3+ ion. The VUV region of excitation spectra of Ce 3+ or Tb 3+ doped YPS and GPS is attributed to host absorption with same maximum around 175 nm. It indicated that energy is transferred from the hosts to luminescent ions under VUV excitation. And the efficiency of energy transfer is different in two matrices. As shown in Figs. 2 and 3 , the GPS matrix can convert more UV radiation into visible light. It better satisfies the performance requirements of plasma displays and mercury-free fluorescent lamps phosphors than YPS. The excitation spectra and emission spectra of YPS: Ce 3+ 0.5%Tb 3+ 1% are shown in Fig. 4 . The excitation spectrum monitored the 543 nm emission of Tb 3+ show 4f 8 –4f 7 5d transition band at 228 nm from Tb 3+ ion and other weak bands from Ce 3+ ion, indicating that energy transfer from Ce 3+ to Tb 3+ ions occurs. The energy transfer can be also proved by the emission spectrum with excitation of Ce 3+ band ( λ ex = 340 nm), the absorption of 340 nm light promotes the Ce 3+ ions to the excited states from the ground states. The energy is then transferred to the Tb 3+ ions. As a result, the emission of Tb 3+ is also observed in the emission spectrum. The excitation spectrum monitored by the 404 nm emission of Ce 3+ is similar to one of Ce 3+ singly doped YPS sample, consisting of host absorption and the excitation bands of Ce 3+ ions. With excitation of Tb 3+ band ( λ ex = 228 nm), the emission spectrum presents only characterization of the Tb 3+ emissions. All the experiment results indicate the absence of back energy transfer from Tb 3+ to Ce 3+ ion. Fig. 5 represents the excitation spectrum and the emission spectra of GPS: Ce 3+ 0.5%Tb 3+ 1%. Compared with the Tb 3+ singly doped samples, the excitation spectrum of Ce 3+ –Tb 3+ codoped sample monitored at 543 nm consists of four parts: the band of host absorption at higher energy; the bands with peak at 228 nm which is assigned to the transitions from the 7 F 6 ground state of Tb 3+ (4f 8 ) to the excited states of the 4f 7 5d configuration; the peaks at about 273 nm which correspond to the 8 S 7/2 → 6 I J transitions of Gd 3+ ion, suggesting that there is energy transfer from Gd 3+ to Tb 3+ ion; the excitation bands of Ce 3+ ion from 280 nm to 350 nm, showing energy transfer from Ce 3+ to Tb 3+ ion upon excitation on the 5d states of Ce 3+ ion. Upon excitation on the 5d state of Ce 3+ at 304 nm and excitation on 6 I J state of Gd 3+ at 273 nm, the emission spectrum presents 5 D 4 → 7 F J transition of Tb 3+ ion and 5d → 4f transition of Ce 3+ ion, the 5 D 3 → 7 F J emission of Tb 3+ ion superimposes the intensive broad bands of Ce 3+ ion. It suggests that energy transfer from both Ce 3+ and Gd 3+ ion to Tb 3+ ion occurs. Upon excitation on the 4f 7 5d state of Tb 3+ at 228 nm, the emission spectrum should only consist of 5 D 3,4 → 7 F J emission of Tb 3+ ion, however, a weak broad band of Ce 3+ emission which superimposes the 5 D 3 → 7 F J emission of Tb 3+ ion is observed. Upon excitation at 228 nm, Ce 3+ ion is unable to be excited directly, it is assumedly due to the fact that Ce 3+ ion is excited by the energy transferred from the excited Tb 3+ ion. The energy transfer from Tb 3+ to Ce 3+ ion in GPS is further confirmed from the excitation spectrum of the sample monitored 404 nm, as shown in Fig. 6 . Compared with the excitation spectrum of Ce 3+ singly doped sample, the 4f 8 → 4f 7 5d transition of Tb 3+ ion was obviously observed. However, the Ce 3+ emission is not found in the emission spectra of Ce 3+ –Tb 3+ codoped YPS sample ( Fig. 4 ), showing that the Tb 3+ → Ce 3+ energy transfer do not occur, in spite of YPS samples have same crystal structure as GPS samples. The Tb 3+ → Ce 3+ energy transfer have not been observed in Ce 3+ –Tb 3+ dual ions activated Lu 2 Si 2 O 7 powders [9] . Obviously, the sensitization of Ce 3+ ion by Tb 3+ ion is not applicable for all hosts, thus it is clear that Tb 3+ → Ce 3+ energy transfer has to occur via Gd 3+ ion as a bridge in GPS samples, the role of Gd 3+ is substantial, the ion has a half-filled 4f shell which gives suitable excited states 8 I for energy transfer from Tb 3+ ion to Ce 3+ ion. While Y 3+ or Lu 3+ ion have a full-filled outermost shell, it need very high energy to be excited, the Y 3+ or Lu 3+ ion would not act as energy transmitter. It should be noted that the Ce 3+ emission is dominant in the emission spectra of Ce 3+ and Tb 3+ codoped pyrosilicates upon excitation on the 5d state of Ce 3+ . On the other words, in the two hosts Ce 3+ –Tb 3+ energy transfer occurs but is inefficient for the indicated concentrations. The Ce 3+ emission in two matrices have their emission maximum at 406 nm and the first excitation maximum at 350 nm, so that the Stokes shift is small (∼4750 cm −1 ). It results in the fact that the Ce 3+ –Ce 3+ transfer is more efficient than the Ce 3+ –Tb 3+ transfer under UV excitation [14] . Another point to be noted is that efficiency of energy transfer not only depends on sensitized ion but also on host matrix. Compared emission spectrum of YPS: Ce 3+ 0.5%Tb 3+ 1% ( Fig. 4 ) and that of GPS: Ce 3+ 0.5%Tb 3+ 1% ( Fig. 5 ) upon excitation on the 5d state of Ce 3+ , the intensity ratios of Tb 3+ and Ce 3+ emissions is greater in GPS matrix. The exchange of Y 3+ by Gd 3+ enhances the emission intensity of Tb 3+ ion; this indicates that energy transfer is more effectively in GPS matrix. And the use of Gd 3+ host lattices makes it possible to convert more UV radiation into visible light. It is useful from the application point of view. The reason for more efficiently energy transfer is that there are two ways of energy transfer from Ce 3+ to Tb 3+ ion in GPS matrix. In the first process energy is directly transferred from Ce 3+ to Tb 3+ ion. The Gd 3+ ions involve in another transfer process [15] . The Ce 3+ excitation energy is transferred to Gd 3+ ions in GPS matrix. Subsequently, the energy migrates over the Gd 3+ sublattice. It is trapped by the emitting Tb 3+ ions. Schematic energy level diagram showing luminescence mechanism in the Ce 3+ –Tb 3+ codoped GPS powders is presented in Fig. 7 . Main radiative transitions of Ce 3+ and Tb 3+ ion are designated with downward arrows. The 5d level of Ce 3+ lies near the excited 5 D 3 levels of the Tb 3+ in Ce 3+ and Tb 3+ codoped GPS sample. When the 5d energy level of Ce 3+ is excited with UV light at 304 nm, part of the energy relaxes to the 2 F J states by radiative transition and shows broad emission band at 404 nm. On the other hand, part of the energy in the 5d energy level of Ce 3+ is transferred to the 5 D 3 state of Tb 3+ and then partially relaxes rapidly to its 5 D 4 state, resulting in the luminescence behavior of Tb 3+ due to 5 D 3 → 7 F J and 5 D 4 → 7 F J emissions. The pumping light at 273 nm excites the electrons to the 6 I states of Gd 3+ ion which can transfer its energy to Ce 3+ ion, the excited Ce 3+ ion consecutively decays to the ground levels of the f shell emitting a broad band at 400 nm. Part of the energy is also transferred to Tb 3+ and followed by an irradiation behavior. Upon excitation on the 4f 7 5d state of Tb 3+ at 228 nm, the excited Tb 3+ nonradiatively decays to the lower levels 5 D 3 and 5 D 4 . Transitions from these excited levels to the 7 F J levels lead to the blue and green emissions. Due to the interaction between Gd 3+ and Tb 3+ ion, a part of excitation energy of Tb 3+ ion can be transferred to Gd 3+ ion, resulting in the excitation of the 6 I state Gd 3+ ion. Subsequently the excitation energy of Gd 3+ ion in the 6 I state is transferred to the ground state of Ce 3+ ion, The Ce 3+ ion is excited to the 5d state, and then the emission of Ce 3+ is observed. 4 Conclusions The phenomenon of the energy transfer between Ce 3+ and Tb 3+ ion is investigated in Ce 3+ and Tb 3+ co-doped Ln 2 Si 2 O 7 (Ln = Y, Gd) samples prepared by sol–gel method. In GPS:Ce 3+ , Tb 3+ codoped systems energy can transfer mutually between Ce 3+ and Tb 3+ , while in YPS host the energy transfer only progresses one way from Ce 3+ to Tb 3+ ion. It was demonstrated that the Tb 3+ excitation energy could be transferred to Ce 3+ ion via Gd 3+ ion as a bridge. The crucial role of energy transfer from Tb 3+ to Ce 3+ ion in GPS host is Gd 3+ ion, which provides suitable excited state for interacting with neighboring Ce 3+ and Tb 3+ ion. The GPS host would be a better choice than YPS from the application point of view, and it can convert more VUV and UV radiation into visible light. Acknowledgement This work was supported by National Nature Science Foundation of China (10774140, 11074245, and 11011120083), Knowledge Innovation Project of The Chinese Academy of Sciences (KJCX2-YW-M11), and Special Foundation for Talents of Anhui Province, China (2007Z021). References [1] P. Dorenbos C.W.E. van Eijk A.J.J. Bos C.L. Melcher J. Phys. Condens. Matter 6 1994 4167 4180 [2] C. Shi Z. Han S. Huang G. Zhang G. Zimmerer J. Beker M. Kamada L. Lu W.M. Yen J Elect Spectrosc Related Phenomena 101–103 1999 633 635 [3] V.A. Pustovarov B.V. Shulgin S.A. Smirnov E.I. Zinin Nucl. Instrum. Methods Phys. Res. A 405 1998 396 399 [4] L. Pidol A. Kahn-Harari B. Viana B. Ferrand P. Dorenbos J.T.M. de Haas C.W.E. van Eijk E. Virey J. Phys. Condens. Matter 15 2003 2091 2102 [5] S. Kawamura J.H. Kaneko M. Higuchi T. Yamaguchi J. Haruna Y. Yagi K. Susa F. Fujita A. Homma S. Nishiyama K. Kurashige H. Ishibashi M. Furusaka IEEE Trans. Nucl. Sci. 54 4 2007 1383 1386 [6] H. Feng D. Ding H. Li S. Lu S. Pan X Chen Guohao Ren J. Alloys Compd. 489 2010 645 649 [7] J. Sokolnicki M. Guzik Optic Mater 31 2009 826 830 [8] J. Sokolnicki J. Phys. Condens. Matter 22 2010 275301 [9] Y. Li B. You W. Zhang M. Yin J. Rare Earths 26 2008 455 458 [10] B. Wang L. Sun H. Ju Solid State Commun. 150 2010 1460 1462 [11] S. Mukherjee V. Sudarsan R.K. Vatsa A.K. Tyagi J. Lumin. 129 2009 69 72 [12] Heesun Yang Yong-Seog Kim J. Lumin. 128 2008 1570 1576 [13] Z. Zhang Y. Wang J. Zhang Mater Lett 62 2008 846 848 [14] G. Blasse B.C. Grabmaier Luminescent Materials 1994 Springer Verlag Berlin [15] C.K. Lin M. Yu M.L. Pang J. Lin Optic. Mater. 28 2006 913 918
What problem does this paper attempt to address?
-
[Spectra of Ce3+, Tb3+ and Gd3+ Ions in Ln(BO3,PO4) [ln = La, Y]].
Sj Ding,W Zhang,Bq Xu,Jt Wang
DOI: https://doi.org/10.3321/j.issn:1000-0593.2001.03.005
2001-01-01
Abstract:Emission and excitation spectra of Ce3+, Tb3+ and Gd3+ in lanthanum borophosphate and yttrium borophosphate are studied. The results show that Ce3+ emission weakens and Tb3+ emission enhances in La(BO3, PO4):Ce, Tb in the presence of Gd, and in Y(BO3, PO4):Ce, Tb, the Ce3+ and Tb3+ emissions are all enhanced, and the former increases more than the latter. In a whole, Gd3+ acts as intermediate of energy transfer from Ce3+ to Tb3+ and sensitizer in La(BO3, PO4):Ce, Tb, Gd; while in Y(BO3, PO4):Ce, Tb, Gd, Gd3+ acts only as sensitizer, and prevents energy transfer from Ce3+ to Tb3+. Compared with Y(BO3, PO4):Ce, Tb, Gd, La(BO3, PO4):Ce, Tb, Gd, phosphor absorbs ultraviolet radiation easily, and emits green light with higher purity and intensity under 254 nm excitation, so it is more suitable for green-emitting phosphor in fluorescent lamp.
-
Wide Concentration Range of Tb3+ Doping Influence on Scintillation Properties of (Ce, Tb, Gd)3Ga2Al3O12 Crystals Grown by the Optical Floating Zone Method
Tong Wu,Ling Wang,Yun Shi,Xintang Huang,Qian Zhang,Yifei Xiong,Hui Wang,Jinghong Fang,Jinqi Ni,Huan He,Chaoyue Wang,Zhenzhen Zhou,Qian Liu,Qin Li,Jianding Yu,Oleg Shichalin,Evgeniy Papynov
DOI: https://doi.org/10.3390/ma15062044
IF: 3.4
2022-03-10
Materials
Abstract:To obtain a deeper understand of the energy transfer mechanism between Ce3+ and Tb3+ ions in the aluminum garnet hosts, (Ce, Tb, Gd)3Ga2Al3O12 (GGAG:Ce, Tb) single crystals grown by the optical floating zone (OFZ) method were investigated systematically in a wide range of Tb3+ doping concentration (1–66 at.%). Among those, crystal with 7 at.% Tb reached a single garnet phase while the crystals with other Tb3+ concentrations are mixed phases of garnet and perovskite. Obvious Ce and Ga loss can be observed by an energy dispersive X-ray spectroscope (EDS) technology. The absorption bands belonging to both Ce3+ and Tb3+ ions can be observed in all crystals. Photoluminescence (PL) spectra show the presence of an efficient energy transfer from the Tb3+ to Ce3+ and the gradually quenching effect with increasing of Tb3+ concentration. GGAG: 1% Ce3+, 7% Tb3+ crystal was found to possess the highest PL intensity under excitation of 450 nm. The maximum light yield (LY) reaches 18,941 pho/MeV. The improved luminescent and scintillation characteristics indicate that the cation engineering of Tb3+ can optimize the photoconversion performance of GGAG:Ce.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
-
Synthesis, optical properties, and energy transfer of Ce(3+)/Tb(3+) co-doped MyGdFx (M=Li, Na, K)
Chunyan Cao,Zhiyang Luo,Siling Guo,Renping Cao,Hyeon Mi Noh,Jung Hyun Jeong,An Xie
DOI: https://doi.org/10.1016/j.saa.2014.06.050
2014-12-10
Abstract:Through a solid-state reaction method, the Ce(3+)/Tb(3+) co-doped MyGdFx (M=Li, Na, K; x=3, 4, 6; y=0, 1, 3) system samples have been synthesized by controlling the annealing temperatures and the ratios of raw materials. The samples were characterized by X-ray diffraction (XRD) patterns, photoluminescence (PL) excitation and emission spectra as well as luminescent dynamic decay curves. The experimental results suggest that the LiF is more difficult to react with the prepared material compared that of NaF or KF under similar reaction conditions. The samples crystallized in different crystalline phases. The energy transfer from Ce(3+) to Tb(3+) or Ce(3+) to Gd(3+) to Tb(3+) has been observed in all the samples. The Ce(3+) and Tb(3+) present different optical properties for they are sensitive to the local environment. In addition, the deduced lifetime of Tb(3+)(5)D4→(7)F5 transition decreases in the same system samples with the annealing temperature increasing. The deduced lifetime of Tb(3+)(5)D4→(7)F5 also decreases with the increase of the KF concentration in the KF system samples.
-
Crystal structure dependence of the luminescence of rare earth ions (Ce3+, Tb3+, Sm3+) in Y2SiO5
Jun Lin,Qiang Su,Hongjie Zhang,Shubin Wang
DOI: https://doi.org/10.1016/0025-5408(95)00178-6
IF: 5.6
1996-01-01
Materials Research Bulletin
Abstract:The luminescence properties of Ce3+, Tb3+, Sm3+ and energy transfer from Ce3+ to Tb3+ were studied in two modifications of Y2SiO5 (low temperature X1 type and high temperature X2 type). The Ce3+ cation shows lower emission energy and larger Stokes shift in X1-Y2SiO5 than in X2-Y2SiO5, and the emission intensities of Ce3+, Tb3+, Sm3+ in the former are weaker than those in the latter. There exists an energy transfer from Ce3+ to Tb3+ in both types of Y2SiO5, and the transfer efficiency in X2 type is higher than that in X1 type. All of these results are discussed in relation to the crystal structure of Y2SiO5.
-
Synthesis and Luminescence Properties of GdF3:Ce3+, Ln(3+)(Ln(3+)=Eu3+, Tb3+, Dy3+, Sm3+) Nanocrystals
Shen Huaxiang,Qiao Xusheng,Fan Xianping
2010-01-01
Rare Metal Materials and Engineering
Abstract:Synthesis and luminescence properties of GdF3:Ce3+, Ln(3+) (Ln(3+)=Eu3+, Tb3+, Dy3+, Sm3+) nanocrystals were investigated. The energy transfer efficiencies between Ce3+ ions and Tb3+ ions, Dy3+ ions, Eu3+ ions were relatively higher than that between Ce3+ ions and Sm3+ ions. Multicolor emissions could be obtained using 254 nm light as excitation source. Such multicolor emissions could be used as multicolor bio-label.
-
Crystal Structure and Photo-Luminescence of Gd3Ga2(Al3-ySiy)(O12-yNy):Ce3+ Phosphors for AC-warm LEDS
Aijun Mao,Zhengyan Zhao,Jiantao Wang,Changxing Yang,Jiejun Ren,Yuhua Wang
DOI: https://doi.org/10.1016/j.cej.2019.02.185
IF: 15.1
2019-01-01
Chemical Engineering Journal
Abstract:Solid solution phosphors Gd3Ga2(Al3-ySiy)(O12-yNy):Ce3+ were synthesized by introducing [Si4+ + N3-]/[Al3+ + O2-] co-substitution into the lattice of Gd3Ga2Al3O12:Ce3+center dot Gd3Ga2Al3O12:Ce3+, characteristic as outstanding light yield (about 50-60 kPh/MeV), and has been applied in computer tomography (CT), positron emission tomography (PET) nuclear medical detector, et al. With the increase of y value, the coordination environment around Gd3+(Ce3+) shrinked, which were confirmed by combining techniques of structure refinement, energy-dispersive spectrum, elements distribution mapping. As a result, stronger 5d orbital nephelauxetic effect (epsilon(c)) and bigger 5d energy level splitting (epsilon(cfs)) were induced. Thus resulting in longer wavelength of excitation and emission from Ce3+, and broadening of emission spectra. The typical sample Gd2.95Ga2Al2.5Si0.5O11.5N0.5:0.05Ce(3+) (GGASON(0.5):Ce3+) exhibits sufficient red component and persistent luminescence(> 10 ms), enables fabrication of warm white light suited for alternating-current (AC) when combined with blue light chip (460 nm).
-
Spectroscopic Studies of Rare Earth Ions in MgSiO3 Gel-Derived Crystals
XP Fan,MQ Wang,ZY Wang
DOI: https://doi.org/10.1016/s0921-5107(97)00035-4
1997-01-01
Abstract:The spectroscopic properties of Eu3+, Tb3+, Sm3+, Dy3+ and Er3+ ions in MgSiO3 gel and the MgSiO3 gel-derived crystals have been investigated. The main excitation band of Eu3+ ions and Tb3+ ions in the gel-derived crystal is attributed to a charge transfer transition and 4f–5d transition, respectively. The emission bands of Tb3+ ions in the gel appear at the same positions as in the gel-derived crystal and the relative intensities of the groups of bands are approximately the same. Similar to Eu3+ ions, however, the intensities of emission bands of Tb3+ ions in the gel-derived crystal are orders of magnitude greater than that in the gel since multiphonon relaxation effectively competes with radiative transitions due to the higher phonon energy in the gel. The energy level split caused by crystal field is observed clearly in the emission spectra of Eu3+ and Sm3+ ion activated gel-derived crystals. The excitation and emission spectra of Sm3+ and Dy3+ ions in the gel-derived crystal are predominantly different from that in the gel. In contrast, the excitation and emission spectra of Er3+ ions in gel-derived crystal are approximately the same as that in the gel with respect to the positions, numbers and intensities of excitation and emission bands.
-
Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process
Dai Jun,Lin Xiang,Qiao Xusheng,Fan Xianping
2010-01-01
Rare Metal Materials and Engineering
Abstract:Preparation of CaYAl3O7:Ce3+, Tb3+ phosphors by sot-gel process and their luminescence properties were investigated. The energy transfer efficiencies between Ce3+ ions and Tb3+ ions resulted in strong emission of Tb3+ ions by 360 nm light as excitation source. The CaYAl3O7:0.03Ce(3+),0.19Tb(3+) phosphors which were sintered for at 900 degrees C 6 h in reducing atmosphere can emit stronger blue-green light.
-
Persistent Luminescence in Rare Earth Ion-Doped Gadolinium Oxysulfide Phosphors
Bingfu Lei,Yingliang Liu,Junwen Zhang,Jianxin Meng,Shiqing Man,Shaozao Tan
DOI: https://doi.org/10.1016/j.jallcom.2010.01.141
IF: 6.2
2010-01-01
Journal of Alloys and Compounds
Abstract:A series of rare-earth ion-doped gadolinium oxysulfide phosphors Gd2O2S:RE3+, Ti, Mg (RE=Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Tm, Yb) were synthesized by solid-state reaction. The excitation and photoluminescence spectra, afterglow spectra, afterglow decay curves and thermoluminescence spectra of the phosphors were examined. According to the afterglow spectra, gadolinium oxysulfide doped with rare-earth ions were classified into three groups. When rare earth ions such as Eu3+, Sm3+, Dy3+, Ho3+, Er3+ and Tm3+ were introduced into the Gd2O2S host, their characteristic emission as well as that from Gd2O2S:Ti, Mg were observed. In case of Yb3+ and Nd3+, only the broadband luminescence of Gd2O2S:Ti, Mg was obtained. Gadolinium oxysulfide doped with Pr3+, Tb3+ and Ce3+ did not show afterglow emission. The calculated trap energy levels of the samples were compared. The role of Ti and Mg ions and a potential mechanism for persistent luminescence in the samples were discussed.
-
Photoluminescence and structural properties of Ce3+ and Eu3+ Co-doped Gd2SiO5 phosphor powders
Wissam Barka,Mohammed Salah Eddine Hamroun,Lahcene Mechernene,Ahmed Guenanou,Chikh Melkaoui,Fouzia Touahra,Lakhdar Guerbous,Redouane Chebout,Khaldoun Bachari,Hamroun, Mohammed Salah Eddine
DOI: https://doi.org/10.1007/s12034-023-03048-5
IF: 1.878
2023-10-10
Bulletin of Materials Science
Abstract:The main objective of this work is to present the enhancement of photoluminescence (PL) and structural properties of Ce 3+ and Eu 3+ co-doped gadolinium orthosilicate Gd 2 SiO 5 (GSO:Eu, Ce) scintillator elaborated by sol–gel method with different concentration of these rare-earth elements. The samples were characterized by X-ray diffraction, field emission-scanning electron microscopy (FE-SEM) and PL spectroscopy. XRD results confirm the crystallization of samples annealed at 1000°C for 4 h to the monoclinic Gd 2 SiO 5 structure. The crystallographic parameters show that Eu 3+ /Ce 3+ incorporated into Gd 2 SiO 5 changes its structure. FE-SEM micrograph results show rod-shaped particles and EDAX spectra confirm the presence of the main constituent elements of the structure. PL showed that two emission peaks dominate the fluorescence spectra of Eu 3+ in Gd 2 SiO 5 and the emission intensity increases relatively with the doping concentration of Ce 3+ ions.
materials science, multidisciplinary
-
Green-Emitting Gd3Ga5O12: Tb3+ Nanoparticles Phosphor: Synthesis, Structure, and Luminescence
A Luchechko,L Kostyk,S Varvarenko,O Tsvetkova,O Kravets
DOI: https://doi.org/10.1186/s11671-017-2032-x
Nanoscale Res Lett
Abstract:Nano- and microceramics of Gd3Ga5O12 garnet doped with 1 mol % Tb3+ ions were synthesized via co-precipitation and high-temperature solid-state reaction methods. X-ray diffraction measurements confirmed the formation of the garnet structure with Ia3d space group in all investigated samples. Atomic force microscopy surface images and grain-size distribution diagrams of Gd3Ga5O12: 1 mol % Tb3+ nanoceramics with 300 and 400 g/mol of polyethylene glycol (PEG) were obtained. The relationship between the content of polyethylene glycol and the particle size of Gd3Ga5O12: Tb3+ phosphors was revealed. An intense broad band (λ m = 266 nm) related to spin-allowed 4f 8-4f 75d 1 transitions of Tb3+ ions was found in photoluminescence excitation spectra of Gd3Ga5O12: Tb3+ nanocrystalline ceramics with PEG-300 and PEG-400 at 300 K. The broad excitation band caused by spin-forbidden (λ m = 295 nm) 4f-5d transitions in Tb3+ ions was additionally observed in the photoluminescence excitation spectra of Gd3Ga5O12: Tb3+ microceramics. Emission of Tb3+ ions under X-ray and UV excitations is presented by two groups of sharp lines which correspond to 5D3 and 5D4 → 7Fj transitions of Tb3+ ions with the most intense line at 546 nm (5D4 → 7F5). It was established that the increasing of PEG content leads to the decreasing of the X-ray and photoluminescence emission intensities.
-
Concentration Quenching of Tb3 + Emissions in Y2O2S Nanocrystals
李丹,吕少哲,王海宇,陈宝玖,鄂书林,张家骅,黄世华
DOI: https://doi.org/10.3321/j.issn:1000-7032.2001.03.005
2001-01-01
Chinese Journal of Luminescence
Abstract:It has been reported recently that some Eu 3+ doped nanocrystalline silicate and oxide were with higher quenching concentrations in comparison with the corresponding bulk materials. Computer simulation has shown that the size confinement and the existence of high density surface states affected significantly the quenching processes of the rare earth dopants in nanoparticles. To understand the feature of the energy transfer process in rare earth doped nanoparticles is important for further seeking applicable nano phosphors . This paper reported, the preparation of a series of Y 2O 2S∶Tb 3+ nanocrystals with uniform sizes and varied Tb 3+ concentrations. The mean size of all the samples prepared was evaluated, based on the X ray diffraction pattern, to be about 20nm. Emission spectra of Tb 3+ in nanocrystalline Y 2O 2S with different Tb 3+ concentrations were measured under 257nm excitation. With increasing Tb 3+ concentration, the luminescence intensity of both the 5D 4 → 7F J and 5D 3 → 7F J transitions increases at first and then decreases. Emission intensities reach their maximum at the Tb 3+ concentration of 0 6% for the 5D 3 emission and of 6 4% for the 5D 4 emission. The lifetime of the 5D 3 level is 0 31ms in the sample with 0 065% Tb concentration, comparably shorter than 0 78ms in bulk Y 2S 2O∶0 3%Tb. This fact indicates that the surface states do act as the quenching centers for the luminescence , and the increasing of quenching concentration comes probably from the lower quantum efficiency of the nanocrystals. The dependences of the intensity on Tb concentration and the decay curves of both 5D 3 and 5D 4 emissions fit with theory. The quenching of the 5D 3 state is governed by dipole dipole interaction, while that of the 5D 4 state by exchange interaction. Both the intensity and temporal analyses coincide and result in the same conclusion. Similar to bulk material, concentration quenching of the 5D 3 state is due to cross relaxation . The mechanism of the concentration quenching of the 5D 4 state is that the energy migrates among the Tb ions and is trapped finally by quenching centers, most likely, the surface states.
-
Photoluminescence properties, excellent thermal stability and energy transfer in Ce3+ and Tb3+ co-doped Sr3Gd2(BO3)4 phosphors
Xiaoxuan Fan,Xiaoyuan Sun,Chunmiao Liu,Wanlu Tian,Min Li,Yongshi Luo,Chunlei Wu
DOI: https://doi.org/10.1016/j.jlumin.2021.118594
IF: 3.6
2022-02-01
Journal of Luminescence
Abstract:Sr3Gd2(BO3)4: Ce3+, Sr3Gd2(BO3)4: Tb3+ and Sr3Gd2(BO3)4: Ce3+, Tb3+ phosphors were synthesized through conventional high temperature solid state reaction method. Phase purity, crystal structure, photoluminescence properties, and lifetime of the samples were analyzed in detailed. Sr3Gd2(BO3)4: Ce3+ showed a bright blue broad emission band, which was attributed to 4f → 5d transitions of the Ce3+ ions, and it exhibited two broad excitation ranged from 200 nm to 400 nm. For all Sr3Gd2(BO3)4: Tb3+ samples, under ultraviolet excitation bands of 240 nm, four emissions peaked at 490 nm, 544 nm, 585 nm and 623 nm appeared, due to the 5D4 → 7FJ (J = 6, 5, 4, 3) transitions of Tb3+ ions. For the Sr3Gd2(BO3)4: Ce3+, Tb3+ phosphors, the lifetime of the samples were analyzed, which showed the presence of energy transfer between the Ce3+ and Tb3+. The energy transfer efficiency from Ce3+ ions to Tb3+ ions reached 98.37%. When the temperature reached 443 K, the luminescence intensity reached 88% of the initial value. Finally, a white LED was fabricated by using a 365 nm near ultraviolet LED chip combined with BaMgAl10O17: Eu2+ (blue), Sr3Gd0.91(BO3)4: 0.09Ce3+, 1.0 Tb3+ (green), and CaAlSiN3: Eu2+ (red) phosphors. The color coordinates was (0.40, 0.42); correlated color temperature was 3721 K; color rendering index was 91.1. The results showed that the Sr3Gd2(BO3)4: Ce3+, Tb3+ green phosphors were suitable for white LEDs.
optics
-
Energy Transfer in Tb3+,Yb3+ Codoped Lu2O3 Near-Infrared Downconversion Nanophosphors
Li,Wei Xiantao,Chen Yonghu,Guo Changxin,Yin Min
DOI: https://doi.org/10.1016/s1002-0721(12)60022-2
IF: 4.632
2012-01-01
Journal of Rare Earths
Abstract:Tb3+ and Yb3+ codoped Lu2O3 nanophosphors were synthesized by the reverse-strike co-precipitation method. The obtained Lu2O3:Tb3+,Yb3+ nanophosphors were characterized by X-ray diffraction (XRD) and photoluminescence (PL) spectra. The XRD results showed that all the prepared nanophosphors could be readily indexed to pure cubic phase of Lu2O3 and indicated good crystallinity. The Tb3+→Yb3+ energy transfer mechanisms in the UV-blue region in Lu2O3 nanophosphors were investigated. The experimental results showed that the strong visible emission around 543 nm from Tb3+ (5D4→7F5) and near-infrared (NIR) emission around 973 nm from Yb3+ (2F5/2→2F7/2) of Lu2O3:Tb3+,Yb3+ nanophosphors were observed under ultraviolet light excitation, respectively. Tb3+ could be effectively excited up to its 4f75d1 state and relaxed down to the 5D4 level, from which the energy was transferred cooperatively to two neighboring Yb3+. The Yb3+ concentration dependent luminescent properties and lifetimes of both the visible and NIR emissions were also studied. The lifetime of the visible emission decreased with the increase of Yb3+ concentration, verifying the efficient energy transfer from the Tb3+ to the Yb3+. Cooperative energy transfer (CET) from Tb3+ to Yb3+ was discussed as a possible mechanism for the near-infrared emission. When doped concentrations were 1 mol.% Tb3+ and 2 mol.% Yb3+, the intensity of NIR emission was the strongest.
-
Role of Yb3+ ion on the evaluation of energy transfer and cross-relaxation processes in Gd2Ce2O7: Yb3+, Er3+ phosphors
Youfusheng Wu,Fengqin Lai,Tongxiang Liang,Yaochun Qiang,Jianhui Huang,Xinyu Ye,Weixiong You
DOI: https://doi.org/10.1016/j.jlumin.2019.03.021
IF: 3.6
2019-01-01
Journal of Luminescence
Abstract:Energy transfer (ET) and cross-relaxation (CR) processes play significant roles in regulating emitting colors and intensity of upconversion (UC) materials. Calculating the coefficients in ET and CR processes can provide visual descriptions for evaluating the UC luminescence properties. Here, we find that those ET and CR processes are responsible for the color-tunable properties in Gd2Ce2O7: Yb3+, Er3+ phosphors. By solving the rate equation, mathematical expressions are established to calculate the ET and CR coefficients based on the experimental UC spectra and lifetimes. The results are benefit to evaluate the efficiencies of ET and CR processes in quantization in different Yb3+ ion concentrations doped samples. The coefficients of ET process arise from 1.05 to 7.93 × 1017 cm3s−1 while those of CR process increase from 2.69 to 72.01 × 1017 cm3s−1 with increasing the Yb3+ ion concentration, which suggest that the CR and ET processes are efficient in Gd2Ce2O7 host. Furthermore, potential temperature sensing properties are also evaluated according to the fluorescence intensity ratio of 2H11/2 and 4S3/2 levels and the maximal sensitivity (S) is achieved about 0.00337 K−1 at 503 K. This work provides an insight into the evaluation of those UC processes and reveals the capacity in color-tunable and temperature sensing aspects.
-
Luminescence properties of barium--gadolinium-titanate ceramics doped with rare-earth ions (Eu3+ and Tb3+)
S Hemasundara Raju,B Muni Sudhakar,B Sudhakar Reddy,S J Dhoble,K Thyagarajan,C Nageswara Raju
DOI: https://doi.org/10.1002/bio.2633
IF: 2.613
Luminescence
Abstract:Barium-gadolinium-titanate (BaGd2 Ti4 O12) powder ceramics doped with rare-earth ions (Eu(3+) and Tb(3+)) were synthesized by a solid-state reaction method. From the X-ray diffraction spectrum, it was observed that Eu(3+) and Tb(3+):BaGd2 Ti4 O12 powder ceramics are crystallized in the form of an orthorhombic structure. Scanning electron microscopy image shows that the particles are agglomerated and the particle size is about 200 nm. Eu(3+) - and Tb(3+) -doped BaGd2 Ti4 O12 powder ceramics were examined by energy dispersive X-ray analysis, Fourier transform infrared spectroscopy, photoluminescence and thermoluminescence (TL) spectra. Emission spectra of Eu(3+)-doped BaGd2 Ti4 O12 powder ceramics showed bright red emission at 613 nm ((5)D0 →(7)F2) with an excitation wavelength λ(exci) = 408 nm ((7)F0 → (5)D3) and Tb(3+):BaGd2 Ti4 O12 ceramic powder has shown green emission at 534 nm ((5)D4 → (7)F5) with an excitation wavelength λ(exci) = 331 nm (((7)F6 → (5)D1). TL spectra show that Eu(3+) and Tb(3+) ions affect TL sensitivity.
-
The Effects of Ga3+ Substitution on Local Structure and Photoluminescence of Tb3Al5O12:Ce Garnet Phosphor
Jun Bi,Xuejiao Wang,Maxim S. Molokeev,Qi Zhu,Xiaodong Li,Jialin Chen,Xudong Sun,Byung-Nam Kim,Ji-Guang Li
DOI: https://doi.org/10.1016/j.ceramint.2018.02.104
IF: 5.532
2018-01-01
Ceramics International
Abstract:(Tb0.985Ce0.015)(3)(Al1-xGax)(5)O-12 garnet phosphors (x = 0, 0.1, 0.2, 0.3, and 1.0) were prepared by calcining their coprecipitated precursors in air at 1500 degrees C, followed by reduction in hydrogen at 1200 degrees C. Rietveld refinement of the XRD results suggested that the Ga dopant predominantly resides at the octahedral Al site of the garnet lattice. Ga doping led to linearly expanded lattice constant, cell volume and theoretical density of the garnet compound and successively lower intensity and longer average fluorescence lifetime of the similar to 570 nm emission of Ce3+. Blue shifted emission and 4f(F-2(5/2)) -> 5d(1)(E-2g) excitation and red shifted 4f(F-2(5/2))-> 5d(2)(E-2g) excitation were also observed for the Ce3+ activator at a higher Ga content. The phenomena were interpreted by considering the band structure of the host, distortion of the CeO8 polyhedron, and centroid shift and field splitting of the Ce3+ 5d energy levels.
-
Photoluminescence and Ce3+→Tb3+→Eu3+ Energy Transfer Processes of the Ce3+/Tb3+/Eu3+-doped β-NaYF4 Phosphors with Broadened Excitation Spectrum
Jianhua Huang,Nan Chen,Xiaojing Wang,Guoping Du,Aisheng Zhang
DOI: https://doi.org/10.1007/s11595-021-2375-0
2021-01-24
Abstract:Ce3+/Tb3+ co-doped and Ce3+/Tb3+/Eu3+ tri-doped β-NaYF4 photoluminescent microcrystals using oleic acid as surfactant were synthesized using the solvothermal method. Their microstructural characteristics and photoluminescence properties were investigated in detail. They have the shape of hexagonal prism bipyramids with uniform particle size, which decreases with the concentrations of Tb3+ and Eu3+. The energy transfer processes of both the Ce3+→Tb3+ and the Ce3+→Tb3+→Eu3+ were systematically studied. Compared with Eu3+ or Tb3+ single-doped β-NaYF4 microcrystals, the sensitization by Ce3+ for the photoluminescence of Tb3+ and Eu3+ leads to a broad excitation spectral bandwidth in the ultraviolet (UV) range. Meanwhile, the corresponding optical absorption efficiency is greatly enhanced. High energy transfer efficiencies have been observed from Ce3+ to Tb3+ and from Tb3+ to Eu3+.
materials science, multidisciplinary
-
Optical and Scintillation Properties of Tb-Doped Gadolinium Pyrosilicate Single Crystals
Prom Kantuptim,Takumi Kato,Daisuke Nakauchi,Nakarin Pattanaboonmee,Noriaki Kawaguchi,Kenichi Watanabe,Weerapong Chewpraditkul,Takayuki Yanagida
DOI: https://doi.org/10.3390/photonics11070673
IF: 2.536
2024-07-19
Photonics
Abstract:Gadolinium pyrosilicate (GPS, Gd2Si2O7) single crystals with different doping concentrations of Tb (0.1–2.0 mol%) are successfully fabricated using the floating-zone technique. In this work, the dependence of Tb-doping concentration on the photoluminescence (PL) and scintillation properties of Tb-doped GPS (Tb:GPS) has been investigated. The PL emission contour graph shows multiple emissions, with the strongest emissions at 378 nm for 0.1% and 0.5% Tb-doping and 544 nm for 1.0% and 2.0% Tb-doping, corresponding to Tb3+ 4f-4f transitions. The PL lifetimes of the specimens range from 4.89 to 5.22 ms. The scintillation spectra exhibit comparable wavelength and intensity trends to the PL emission. The scintillation lifetimes of the specimens range from 2.41 to 3.88 ms. The Tb:GPS specimens demonstrate a relatively excessive afterglow level, with Af20 values ranging from 1640 to 7250 ppm and Af40 values ranging from 136 to 362 ppm. Using recently developed pulse height measurement for millisecond decay scintillators, under excitation at 662 keV γ-rays, the 1.0% Tb:GPS specimen exhibits the highest scintillation light yield among all other specimens at 95,600 ph/MeV, making Tb:GPS one of the highest light yield oxide scintillators.
optics
-
Luminescence properties and efficient energy transfer investigations of inverse garnet-type Mg 3 Y 2− x − y Ge 3 O 12 : x Tb 3+ , y Eu 3+ multicolor phosphor
Jialiang Niu,Ze Zhang,Wei Zhou,Huanhuan Du
DOI: https://doi.org/10.1007/s10854-020-02958-y
2020-01-01
Abstract:Tb 3+ and/or Eu 3+ doped Mg 3 Y 2 Ge 3 O 12 phosphors were synthesized successfully through solid-state reaction. The X-ray diffraction (XRD) patterns, photoluminescence (PL), fluorescence decay curve and energy transfer behavior of the samples were studied in detail. XRD patterns show all samples are attributed to inverse garnet structure. Under UV excitation, the singly doped phosphors with Tb 3+ and Eu 3+ ions showed green and red characteristic emission. The emission color of Mg 3 Y 2 Ge 3 O 12 :Tb 3+ , Eu 3+ can be adjusted by the corresponding Tb 3+ –Eu 3+ energy transfer, which also demonstrated excellent thermal stability at 448 K (78.09%). These results indicate that the Mg 3 Y 2 Ge 3 O 12 :Tb 3+ , Eu 3+ phosphors will have potential use in n-UV pumped LED devices.