Order–disorder Transformation and Enhanced Oxide-Ionic Conductivity of (sm1−xdyx)2zr2o7 Ceramics

Xiao-Liang Xia,Zhan-Guo Liu,Jia-Hu Ouyang

DOI: https://doi.org/10.1016/j.jpowsour.2010.09.056

IF: 9.2

2011-01-01

Journal of Power Sources

Abstract:(Sm1−xDyx)2Zr2O7 (0≤x≤1) ceramics are prepared by a solid state reaction process at 1973K for 10h in air. (Sm1−xDyx)2Zr2O7 (0≤x≤0.3) ceramics exhibit a single phase of pyrochlore-type structure, while (Sm1−xDyx)2Zr2O7 (0.5≤x≤1.0) possess a defective fluorite-type structure. The full width at half-maxima in the Raman spectra increases with increasing Dy content, which indicates that the degree of structural disorder increases as the Dy content increases. The ionic conductivity of (Sm1−xDyx)2Zr2O7 ceramics is investigated by impedance spectroscopy over a frequency range of 0.2Hz to 8MHz in the temperature range of 873–1173K in air and hydrogen atmospheres, respectively. The ionic conductivity has a maximum near the phase boundary between the pyrochlore- and the defective fluorite-type phases under identical temperature levels. The ionic conductivity is determined by the degree of structural disorder or unit cell free volume, which is depending on the Dy content. As the ionic conductivity in the hydrogen atmosphere is almost the same as that obtained in air, the conduction of (Sm1−xDyx)2Zr2O7 is purely ionic with negligible electronic conduction.