Influence of Gd(3+)Doping on Properties of Nay(Moo4)(2):Eu3+ Phosphors

Liu Wei,Li Xilin,Liu Juan,Han Xia,Yan Jinghui,Kang Zhenhui,Lian Hongzhou

2011-01-01

Abstract:Eu3+-doped NaY(MoO4)(2) and Na(Y, Gd)(MoO4)(2) phosphors were prepared via microemulsion-hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM) and fluorescence spectroscopy were used to characterize the samples. The XRD of as-prepared samples were in agreement with the PDF # 82-2369 of NaY(MoO4)(2). SEM images showed that the as-prepared particles had a diameter size ranging from 0.5 to 0.8 mu m. The critical activator molar concentration (Eu3+) in NaY(MoO4)(2) : Eu3+ was 4%, and the luminescent intensity of Na(Y, Gd)(MoO4)(2) : 4%Eu(3+)was maximum when Y : Gd molar ratio at 0.5 : 0.5. Excited by 276, 395 and 465 nm, Na(Y-0.48, Gd-0.48)(MoO4)(2) : 4%Eu(3+)exhibited pale pink, yellow and orange-red respectively. The sample of Na(Y, Gd)(MoO4)(2) : Eu3+ could become a valuable luminescent material for white LED.